Influence of the laminate lay-up on the fatigue behaviour of SiC-fibre/BMAS-matrix composites

Composites Part A: Applied Science and Manufacturing

Volumn 30, Issue 5, 1999, Pages 623-635

  Vanwijgenhoven, Eddy ^a   Wevers, Martine ^a   Van Der Biest, Omer ^a  

^a UNIVERSITY OF LEUVEN   (Belgium)

Author keywords

[No Author keywords available]

Indexed keywords

CERAMIC MATRIX COMPOSITES; LAMINATES; SILICON CARBIDE; STRESSES;

LAMINATE LAY UP; MECHANICAL RESPONSE;

FATIGUE OF MATERIALS;

EID: 0032688480     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-835X(98)00177-8     Document Type: Article

References (54)

1. Prewo K. Fatigue and stress rupture of silicon carbide fibre-reinforced glass-ceramics. J Mat Sci. 22:1987;2695.
2. Zawada L., Butkus L., Hartman G. Tensile and fatigue behavior of silicon carbide fiber-reinforced aluminosilicate glass. J Am Ceram Soc. 74:1991;2851.
3. Holmes J., Cho C. Experimental observations of frictional heating in fiber-reinforced ceramics. J Am Ceram Soc. 75:1992;929.
4. Harris B., Habib F., Cooke R. Matrix cracking and the mechanical behaviour of SiC/CAS composites. Proc R Soc Lond A. 437:1992;109.
5. Pryce A., Smith P. Matrix cracking in unidirectional ceramic matrix composites under quasi-static and cyclic loading. Acta Metall Mater. 41:1993;1269.
6. Karandikar P., Chou T. Damage development and moduli reductions in Nicalon-calcium aluminosilicate composites under static fatigue and cyclic fatigue. J Am Ceram Soc. 76:1993;1720.
7. Thomas W., Kopp M., Sanchez J. Stress-strain behavior of Nicalon-fiber-reinforced calcium aluminosilicate composites under tensile fatigue conditions. J Am Ceram Soc. 76:1993;2175.
8. Pryce A., Smith P. Matrix cracking in cross-ply ceramic matrix composites under quasi-static and cyclic loading. Acta Metall Mater. 42:1994;861.
9. Holmes J., Wu X., Sorensen B. Frequency dependence of fatigue life and internal heating of a fiber-reinforced/ceramic-matrix composite. J Am Ceram Soc. 77:1994;3284.
10. Sorensen B., Holmes J. Improvement in the fatigue life of fiber-reinforced ceramics by use of interfacial lubrication. Scripta Metall Mater. 32:1995;1393.
11. Reynaud P. Cyclic fatigue of ceramic-matrix composites at ambient and elevated temperature. Comp Sci Tech. 56:1996;809.
12. Lee S., Stinchcomb W. Damage mechanisms and fracture modes in Nicalon/CAS-II laminates. Key Eng Mat. 121/122:1996;227.
13. Rouby D., Reynaud P. Fatigue behaviour related to interface modification during load cycling in ceramic-matrix fibre composites. Comp Sci Tech. 48:1993;109.
14. Shuler S., Holmes J., Wu X., Roach D. Influence of loading frequency on the room-temperature fatigue of a carbon-fiber/SiC-matrix composite. J Am Ceram Soc. 76:1993;2327.
15. Morris W., Cox B., Marshall D., Inman R., James M. Fatigue mechanisms in grapite/SiC composites at room and high temperature. J Am Ceram Soc. 77:1994;792.
16. Chawla N., Holmes J., Lowden R. The role of interfacial coatings on the high frequency fatigue behavior of Nicalon/C/SiC composites. Scripta Mat. 35:1996;1411.
17. Holmes J. Influence of stress ratio on the elevated temperature fatigue of a silicon carbide fiber-reinforced silicon nitride composite. J Am Ceram Soc. 74:1991;1639.
18. Roebben G., Steen M., Bressers J., van der Biest O. Mechanical fatigue in monolithic non-transforming ceramics. Progr Mat Sci. 40:1996;265.
19. Talreja R. Fatigue of fibre-reinforced ceramics, in Proceedings of 11th Riso International Symposium. Structural Ceramics: Processing, Microstructure, and Properties. Riso National Laboratory, Roskilde, Denmark, 1990:145.
20. Evans A., Zok F. The physics and mechanics of fibre-reinforced brittle matrix composites. J Mat Sci. 29:1994;3857.
21. Evans A., Zok F., McMeeking R. Fatigue of ceramic matrix composites. Acta Metall Mater. 43:1995;859.
22. Sorensen B, Holmes J. Fatigue of continuous fiber-reinforced ceramic matrix composites: review of mechanisms and models. Proceedings of the international symposium on fatigue under thermal and mechanical loading: mechanisms, mechanics, and modelling. Dordrecht: Kluwer Academic, 1996:487.
23. Evans A. Design and life prediction isssues for high-temperature engineering ceramics and their composites. Acta Mater. 45:1997;23.
24. Vanswijgenhoven E, Wevers M, van der Biest O. Fatigue behaviour of SiC fibre toughened barium magnesium aluminosilicate glass-ceramic laminates. Proceedings of the international symposium on fatigue under thermal and mechanical loading: mechanisms, mechanics, and modelling. Dordrecht: Kluwer Academic, 1996:269.
25. Plucknett K., Sutherland S., Daniel A., Cain R., West G., Taplin D., Lewis M. Environmental ageing effects in a silicon carbide fibre-reinforced glass-ceramic matrix composite. J Microscopy. 177:1995;251.
26. Bollet F., Galiotis C., Reece M. Measurement of strain distribution in fibre reinforced ceramic matrix composites. Composites Part A. 27A:1996;729.
27. Gogotsi Y., Yoshimura M. Low-temperature oxidation, hydrothermal corrosion, and their effects on properties of SiC (Tyrannno) fibers. J Am Ceram Soc. 78:1995;1439.
28. Lambrinou K., van der Biest O., Boccaccini A., Taplin D. Densification and crystallisation behaviour of barium magnesium aluminosilicate glass powder compacts. J Eur Ceram Soc. 16:1996;1237.
29. Lankford J., Couque H., Nicholls A. Effect of dynamic loading on tensile strength and failure mechanisms in a SiC fibre reinforced ceramic matrix composite. J Mat Sci. 27:1992;930.
30. Sorensen B., Holmes J. Effect of loading rate on the monotonic tensile behavior of a continuous-fiber-reinforced glass-ceramic matrix composite. J Am Ceram Soc. 19:1996;313y.
31. Martin-Meizoso A., Puente I., Sanchez J., Gil Sevillano J. High strain-rate and high temperature tensile behaviour of CAS/SiC. Key Eng Mat. 127/131:1997;729.
32. Spearing S., Zok F., Evans A. Stress corrosion cracking in a unidirectional ceramic-matrix composite. J Am Ceram Soc. 77:1994;562.
33. Goettler R., Faber K. Interfacial shear stresses in fiber-reinforced glasses. Comp Sci Tech. 37:1989;129.
34. Surgeon M., Vanswijgenhoven E., Wevers M., van der Biest O. Acoustic emission during tensile testing of SiC-fibre-reinforced BMAS glass-ceramic composites. Composites Part A. 28A:1997;473.
35. Sorensen B. Effect of fibre roughness on the overall stress - transverse strain response of ceramic composites. Scripta Metall Mater. 28:1993;435.
36. Vanswijgenhoven E., van der Biest O. The relation between longitudinal stress and transverse strain during tensile testing of unidirectional fibre toughened ceramic matrix composites. Acta Mat. 45:1997;3349.
37. Kim R., Pagano N. Crack initiation in unidirectional brittle-matrix composites. J Am Ceram Soc. 74:1991;1082.
38. Nardone V., Prewo K. Tensile performance of carbon-fibre-reinforced glass. J Mat Sci. 23:1988;168.
39. Bhatt R., Phillips R. Laminate behavior for SiC fiber-reinforced reaction-bonded silicon nitride matrix composites. J Comp Tech Res. 12:1990;13.
40. Mall S., Kim R. Failure mechanisms in laminates of silicon carbide/calcium-aluminosilicate ceramic composite. Composites. 23:1992;215.
41. Cady C., Heredia F., Evans A. In-plane mechanical properties of several ceramic-matrix composites. J Am Ceram Soc. 78:1995;2065.
42. Vanswijgenhoven E, Wevers M, van der Biest O. The relation between longitudinal stress and transverse strain during cyclic loading of unidirectional fibre toughened ceramic matrix composites. Acta Materialia, submitted.
43. Vagaggini E., Domergue J., Evans A. Relationships between hysteresis measurements and the constituent properties of ceramic matrix composites: I, theory. J Am Ceram Soc. 78:1995;2709.
44. Domergue J., Vagaggini E., Evans A. Relationships between hysteresis measurements and the constituent properties of ceramic matrix composites: II, experimental studies on unidirectional materials. J Am Ceram Soc. 78:1995;2721.
45. Dauskardt R. A frictional-wear mechanism for fatigue-crack growth in grain bridging ceramics. Acta Metall Mater. 41:1993;2765.
46. Guo S., Kagawa Y. Characterization of interface sliding damage in SiC fiber-reinforced Ti-15-3 Matrix composite by cyclic fatigue. Acta Mater. 45:1997;2257.
47. Eckel A., Bradt R. Strength distribution of reinforcing fibers in a Nicalon fiber/chemically vapor infiltrated silicon carbide matrix composite. J Am Ceram Soc. 72:1989;455.
48. Thouless M., Sbaizero O., Sigl L., Evans A. Effect of interface mechanical properties on pull-out in a SiC-fiber-reinforced lithium aluminum silicate glass-ceramic. J Am Ceram Soc. 72:1989;525.
49. Beyerle D., Spearing S., Zok F., Evans A. Damage and failure in unidirectional ceramic-matrix composites. J Am Ceram Soc. 75:1992;2719.
50. Stinchcomb W, Reifsnider K, Yeung P, Masters J. Effect of ply constraint on fatigue damage development in composite material laminates. In: ASTM STP 723. Philadelphia, PA: American Society for Testing and Materials, 1981:64.
51. Talreja R. Fatigue of fiber composites, materials science and technology, Vol. 13, Structure and properties of composites. New York, NY: VCH, 1993:584.
52. Salpekar S, O'Brien T. Combined effect of matrix cracking and free edge on delamination. In: ASTM STP 1110. Philadelphia, PA: American Society for Testing and Materials, 1991:87.
53. Jamison R, Schulte K, Reifsnider K, Stinchcomb W. Characterization and analysis of damage mechanisms in tension-tension fatigue of graphite/epoxy laminates. In: ASTM STP 836. Philadelphia, PA: American Society for Testing and Materials, 1984:21.
54. Highsmith A, Reifsnider K. Internal load distribution effects during fatigue loading of composite laminates. In: ASTM STP 907. Philadelphia, PA: American Society for Testing and Materials, 1986:233.