Photoluminescent siloxenes in nanoporous aluminum oxide

Advanced Materials

Volumn 10, Issue 5, 1998, Pages 398-401

  Heilmann, Andreas ^a   Jutzi, Peter ^b   Klipp, Andreas ^b   Kreibig, Uwe ^c   Neuendorf, Rolf ^c   Sawitowski, Thomas ^a   Schmid, Günter ^a  

^a UNIVERSITY OF DUISBURG ESSEN   (Germany)

^b BIELEFELD UNIVERSITY   (Germany)

^c RWTH AACHEN UNIVERSITY   (Germany)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINUM COMPOUNDS; DECOMPOSITION; MEMBRANES; NANOSTRUCTURED MATERIALS; PHOTOLUMINESCENCE; POROUS MATERIALS; SEMICONDUCTING SILICON COMPOUNDS; SILANES;

SILOXENES;

LUMINESCENT DEVICES;

EID: 0032026217     PISSN: 09359648     EISSN: None     Source Type: Journal    
DOI: 10.1002/(SICI)1521-4095(199803)10:5<398::AID-ADMA398>3.0.CO;2-6     Document Type: Article

References (24)

1. L. T. Canham, Appl. Phys. Lett. 1990, 10, 1046.
2. V. Lehmann, U. Gösele, Appl. Phys. Lett. 1991, 58, 856.
3. R. A. Bley, S. M. Kauzlarich, J. E. Davis, H. W. H. Lee, Chem. Mater. 1996, 8, 1881.
4. G. A. Ozin, Chem. Vap. Deposition 1996, 2, 8.
5. V. Lehmann, U. Gösele, Adv. Mater. 1992, 4, 114.
6. J. L. Heinrich, C. L. Curtis, G. M. Credo, K. L. Kavanagh, M. J. Sailor, Science 1992, 225, 66.
7. P. McCord, S. Yau, A. J. Bard, Science 1992, 257, 68.
8. Y. Kanemitsu, Phys. Rep. 1995, 263, 1.
9. D. Routkevich, A. A. Tager, J. Haruyama, D. Almawlawi, M. Moskovits, J. M. Xu, IEEE Trans. Electron Devices 1996, 10, 1646.
10. C. R. Martin, Science 1994, 266, 1961.
11. G. L. Hornyak, M. Kröll, R. Pugin, T. Sawitowski, G. Schmid, J.-O. Bovin, G. Karsson, H. Hofmeister, S. Hopfe, Chem. Eur. J. 1997, 3, 1951.
12. J. W. Diggle, T. C. Downie, C. W. Goulding, Chem Rev. 1969, 69, 365.
13. G.E. Thomson, G. C. Wood, Treatise Mater. Sci. Technol. 1983, 20, 205.
14. J. P. O'Sullivan, G. C. Wood, Proc. R. Soc. London 1970, 317, 511.
15. P. Jutzi, D. Kanne, M. Hurthouse, A. J. Howes, Chem. Ber. 1988, 121, 1299.
16. J. Dahlhaus, P. Jutzi, H. J. Schrenk, W. Kulisch, Adv. Mater. 1993, 5, 377.
17. The calculation is based on the following parameters and assumptions: the inner surface and volume of a single pore, the amount of silane (silicon) in a completely filled pore, and the calculated packing density of Si atoms, which correlate with the projection of corrugated six-membered rings on the pore wall (see Fig. 1).
18. S. Tajima, Electrochim. Acta 1971, 22, 995.
19. M. S Brand, T. Puchert, M. Stutzmann, Solid State Commun. 1997, 102, 365.
20. I. Hirabayashi, K. Morigaki, S. Yamanaka, J. Non-Cryst. Solids 1983, 59/60, 645.
21. M. Stutzmann, M. S. Brandt, M. Rosenbauer, J. Weber, H. D. Fuchs, Phys. Rev. B 1993, 47, 4806.
22. Y. Kanemitsu, K. Suzuki, S. Kyushin, H. Matsumoto, Phys. Rev. B 1995, 51, 13 103.
23. D. J. Lockwood, Z. H. Lu, J. M. Baribeau, Phys. Rev. Lett. 1996, 76, 539.
24. G. Fritz, D. Kummer, Z. Anorg. Allg. Chem. 1960, 304, 322.