Applications of overload data to fatigue analysis and testing

ASTM Special Technical Publication

Volumn , Issue 1411, 2002, Pages 165-180

  DuQuesnay, David L ^a  

^a ROYAL MILITARY COLLEGE OF CANADA   (Canada)

Author keywords

Aluminum; Cycle editing; Damage; Elastic modulus; Fatigue (materials); Fatigue limit; Life prediction; Non damaging cycles; Steel; Variable amplitude loading

Indexed keywords

ELASTIC MODULI; FATIGUE OF MATERIALS; LOADS (FORCES); SOFTWARE PROTOTYPING; STRAIN; STRESS ANALYSIS;

CYCLE EDITING; FATIGUE LIMIT; LIFE PREDICTION; VARIABLE AMPLITUDE LOADING;

FATIGUE TESTING;

EID: 8844285986     PISSN: 00660558     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp10610s     Document Type: Conference Paper

References (17)

1. British Standards Institution, BS 5400, "Steel Concrete and Composite Bridges," Part 10, Code of Practice for Fatigue, 1980.
2. Kikukawa, M., Jono, M. and Murata, Y., "Effect of Mean Stress and Cumulative Damage Under Service Loadings Including Stresses Below the Fatigue Limit," Materials, Experimentation and Design in Fatigue, Proceedings of Fatigue '81, Westbury House, IPC Business Press Ltd., 1981, pp. 308-317.
3. Van, X., Cordes, T.S., Vogel, J.H. and Dindinger, P.M., "A Property Fitting Approach for Improved Estimates of Small Cycle Fatigue Damage," SAE Paper # 920665, Society of Automotive Engineers, Philadelphia, PA 1992.
4. Conle, A. and T.H. Topper, "Overstrain Effects During Variable Amplitude Service History Testing," International Journal of Fatigue, Vol.2, No.3, 1980, pp. 130-136.
5. Plumtree, A. and Shen, G., "Cyclic Deformation and Life Prediction Using Damage Mechanics," Constitutive Laws of Plastic Deformation and Fracture, A.S. Krause et al., Eds, Kluwer Academic Publishers, The Netherlands, 1990, pp. 77-85.
6. Golos, K. and Ellyin, F., "Generalization of Cumulative Damage Criterion to Multilevel Cyclic Loading," Theoretical and Applied Fracture Mechanics, Vol.7, 1987, pp.169-176.
7. DuQuesnay, D.L., Topper, T.H., and Jurcevic, R., "A New Fatigue Life Prediction Model for Variable Amplitude Loading," Localized Damage II, M.H. Aliabadi et al., Eds., Computational Mechanics Publications, Southampton, U.K., Vol.1, Fatigue and Fracture Mechanics, pp. 103-120.
8. DuQuesnay, D.L., Pompetzki, M.A. and Topper, T.H., "Fatigue Life Predictions for Variable Amplitude Strain Histories," SAE Transactions, Vol. 102, No. 5, 1993, pp.455-465.
9. DuQuesnay, D.L., MacDougall, C., Dabayeh, A. and Topper, T.H., "Notch Fatigue Behaviour as Influenced by Periodic Overloads," International Journal of Fatigue, Vol. 17, No.2, 1995, pp.91-99.
10. McClung, R.C. and Sehitoglu, H., "Closure Behaviour of Small Fatigue Cracks Under High Strain Fatigue Histories," ASTM STP 982, Newman, J. and Elber, W. Eds., American Society for Testing and Materials, West Conshohocken, PA, 1988, pp.279-299.
11. Vormwald, M. and Seeger, T., "The Consequences of Short Crack Closure on Fatigue Crack Growth Under Variable Amplitude Loading," Fatigue and Fracture of Engineering Materials and Structures, Vol.14, No.2/3, 1991, pp.205-225.
12. Dabayeh, A., and Topper, T.H., "Changes in Crack-Opening Stress after Underloads and Overloads in 2024-T351 Aluminum Alloy," International Journal of Fatigue, Vol.17, No.4, 1995, pp.261-269.
13. Kahlil, M., DuQuesnay, D.L. and Topper, T.H., "Prediction of Crack-Opening Stress Levels for Service Loading Spectra," Application of Automation Technology in Fatigue and Fracture Testing and Analysis: Fourth Volume, ASTM STP 1411, A. A. Braun, P. C. McKeighan, A. M. Nicolson, and R. D. Lohr, Eds., American Society for Testing and Materials, West Conshohocken, PA, 2002.
14. DuQuesnay, D.L., "Fatigue Damage Accumulation in Metals Subjected to High Mean Stress and Overload Cycles," Ph.D. Thesis, Dept. of Civil Engineering, University of Waterloo, Waterloo, Ontario, 1991.
15. DuQuesnay, D.L., Heffernan, P.J. and Howard, A.B., "Cyclic and Fatigue Behaviour of a Micro-Alloyed Reinforcing Steel," Proceedings of the 15th Canadian Congress of Applied Mechanics, B. Tabarrok and S. Dost, Eds., Vol.1, 1995, pp. 194-195.
16. Lynn, A. and DuQuesnay, D.L., "Computer Simulation of Variable Amplitude Fatigue Crack Initiation Behaviour Using a New Strain Based Cumulative Damage Model," submitted to International Journal of Fatigue, 2001.
17. Petit, J., de Fouquet, J. and Henaff, G., "Influence of Ambient Atmosphere on Fatigue Crack Growth Behaviour of Metals," Laboratoire de mécanique et de physique des matériaux, URA 863 CNRS ENSMA, Site du futuroscope, B.P.109, Chasseneuil du Poitou, 86960 Futuroscope Cedex.