Arational model to predict the service life of RC structures in Marine environment

American Concrete Institute, ACI Special Publication

Volumn SP-170, Issue , 1997, Pages 777-799

  Yokozeki, K ^a   Motohashi, K ^b   Okada, K ^a   Tsutsumi, T ^c  

^a KAJIMA TECHNICAL RESEARCH INSTITUTE   (Japan)

^b KAJIMA CORPORATION   (Japan)

^c TOKYO ELECTRIC POWER COMPANY   (Japan)

Author keywords

Chlorides; Corrosion; Cover; Cracking (fracturing); Diffusion; Durability; Mix proportioning

Indexed keywords

CHLORINE COMPOUNDS; CORROSION; DETERIORATION; DURABILITY; FORECASTING; OFFSHORE STRUCTURES; SERVICE LIFE;

ANALYTICAL STUDIES; CHLORIDE PENETRATION; CORROSION OF REINFORCEMENT; DETERIORATION PROCESS; DURABILITY DESIGN; LONGITUDINAL CRACKING; MARINE ENVIRONMENT; SERVICE LIFE PREDICTION;

REINFORCED CONCRETE;

EID: 85111560047     PISSN: 01932527     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (26)

1. The Japan Society of Civil Engineers "Standard Specifications for Concreto"; 1996.
2. The,Japan Society of Civil Engineers "Guidelines for Durability Design of Concrete Structures (Draft)", 1996.
3. The Japan Concrete Institute "Concepts related to Durability Design of Reinforced Concrete Structures"; 1991.
4. A Yamamoto, K. Motohashi, S. Misra and T. Tsutsumi "Propose Durability Design for RC Marine Structures"; Concrete Under Severe Conditions Environment and loading, Volume 1, pp.544-553, CONSEC '95, 1995.
5. T. Tsutsumi, A Yamamoto, S. Misra and K. Motohashi "Reinforcement Corrosion in Concrete Subjected to Early Sea-Water Attack"; Annual Report., Concrete Engineering, pp. 651-656, JCI, 1991. (in Japanese)
6. K. Okada, T. Tsutsumi, K. Yokozeki and K. Motohashi "Experimental Study to Quantify the Penetration Rate of Chloride Ion"; 50th Annual Meeting of the Japan Society of Civil Engineers, pp. 286-287. 1995. (in Japanese)
7. N. S. Berke, D. W. Pfiefer and T. G. Weil "Protection against Chloride Induced Corrosion"; Concrete International, pp.15-55, Dec. 1988.
8. T. Misawa, K Hashimoto and S. Shimodaira "On the Mechanism of Atmospheric Rusting of Iron and Protective Rust Layer on Low Alloy Steels": Boshoku Gijutsu, Vol. 23, No.8, pp. 501-506, 1988. (in Japanese)
9. K. Suda, S. Misra and K. Motohashi "Analytical Investigations on Critical Corrosion Amount at the Onset of Corrosion Cracks"; Annual Report, Concrete Engineering, pp. 751-756, JCI, 1992. (in Japanese)
10. Y. Yoshioka and T. Yonezawa "Fundamental Investigations on Mechanical Properties of Reinforcement Corrosion Products": 37th Annual Meeting of the Japan Society of Civil Engineers, Chapter V, pp.520-521, 1990. (in Japanese)
11. K. Suda, K Motohashi and S. Misra "Effects of Reinforcement Corrosion Products on the Critical Corrosion Amount at the Onset of Corrosion Cracks"; 45th Annual Meeting of the Japan Society of Civil Engineers, pp. 520-521, 1990. (in Japanese)
12. M. Tsunomoto, Y.Kajikawa and M. Kawamura "Elasto-Plastic Analysis of Expansive Behavior due to Corrosion of Reinforcement"; Report of the Japan Society of Civil Engineers, No. 402, V-10, pp.151-159, 1989. (in Japanese)
13. K. Kobayashi and K. Shuttoh "Study of Oxygen Diffusivity of Cementitious Materials (IV)"; Production Research, Vol. 38, No. 6, pp. 269-272, 1986. (in Japanese)
14. H. Seki andY. Kaneko "Life Prediction of Reinforced Concrete Member Based on Corrosion of Reinforcement"; Concrete Engineering, Vol. 29, No. 8, pp. 15-2a,,JCI, 1991. (in Japanese)
15. K. Yokozeki, S. Misra, K. Suda and K. Motohashi "Effect of Cover on the Period for onset Corrosion Induced Cracking"; 47th Annual Meeting of the,Japan Society of Civil Engineers, pp. 396-397, 1992. (in Japanese)
16. Y. Masuda M. Yasuda, H. Hanae andY. Matsubayashi "Experimental Study on the Rate of Corrosion of Reinforcing Bar in Chloride Environment."; Annual Report, Concrete Engineering, pp. 441-446, JCI, 1990. (in Japanese)
17. Y. Masuda, M. Kakegawa and H. Hanae "Experiment on the Influence of Various Factors on the Rate of Corrosion Loss of Reinforcing Bar in Concrete"; Annual Report, Concrete Engineering, pp. 781-786, JCI, 1992. (in Japanese)
18. F. Tomosawa et a! "Influence of Chloride Content on the Rate of Corrosion of Reinforcing Bar in Concrete"; Report of the Building Research Institute, No.118, 1988. (in Japanese)
19. Z.P. Bazant. and B.I-1. Oh "Crack band theory for fracture of concrete"; Materiaux et Constructions, Vol. 16, No. 83, pp.155-177, 1983.
20. H.J. Dagher and S. Kulendran "Finite Element Modeling of Corrosion Damage in Concrete Structures"; ACI Structural Journal, pp.699-708, 1992.
21. 0. Dahlblom and N. S. Ottosen "Smeared Crack Analysis Using Generalized Fictitious Crack Model"; Journal of Engineering Mechanics, ASCE, Vol.116, No.1, pp. 55-76, 1990.
22. R. D. Browne "Mechanisms of Corrosion of Stool in Concrete in relation to Design, Inspection, Repair of Offshore and Coastal Structures"; ACT SP-65, pp.169-204, 1980.
23. K. Takewaka and S. Matsumoto "Behavior of Reinforced Concrete Members Deteriorated by Corrosion of Reinforcement"; Annual Report, Concrete Engineering, pp. 177-180, JCI, 1984. (in Japanese)
24. M. Morikawa, H. Seki and Y. Okumura "Basic Research on Cracking of Concrete due to Expansion by Rebar Corrosion"; Report of the Japan Society of Civil Engineers, No. 378, V-6, pp. 97-105, 1987. (in Japanese)
25. K. Tamori, K. Maruyama, M. Odagawa and T. Hashimoto "Crack Behavior of Reinforced Concrete Members due to Corrosion of Reinforcing Bars"; Annual Report, Concrete Engineering, pp. 505-510, JCI, 1988. (in Japanese)
26. H. Seki and T. Kawahara "Study on Expansion Crack of Concrete by Corrosion of Steel"; Cement Technology Report., Vol. 38, pp. 341-344, 1984. (in Japanese)