Fatigue strength of driving shafts of automatic transmission gearboxes under operational torques

SAE Technical Papers

Volumn , Issue , 1997, Pages

  Sonsino, Cetin Morris ^a   Kaufmann, Heinz ^a   Foth, Joachim ^b   Jauch, Friedemann ^b  

^a FRAUNHOFER INSTITUTE FOR STRUCTURAL DURABILITY AND SYSTEM RELIABILITY LBF   (Germany)

^b ZF FRIEDRICHSHAFEN AG   (Germany)

Author keywords

constant and variable amplitude tests; damage accumulation; damage parameter; Drive shaft; fatigue life assessment; induction hardened; local strain and stress; operational loading conditions; operational service measurement; steel Ck 35 mod. (SAE 1038)

Indexed keywords

DAMAGE DETECTION; FATIGUE TESTING; HARDENING; SHAFTS (MACHINE COMPONENTS); STRESS ANALYSIS;

DAMAGE ACCUMULATION; DAMAGE PARAMETER; FATIGUE LIFE ASSESSMENT; INDUCTION-HARDENED; LOADING CONDITION; LOCAL STRAINS; OPERATIONAL SERVICE; VARIABLE AMPLITUDES;

FATIGUE DAMAGE;

EID: 85072464908     PISSN: 01487191     EISSN: 26883627     Source Type: Journal    
DOI: 10.4271/970706     Document Type: Conference Paper

References (28)

1. Foth, J., Jauch, F., Sonsino, C.M., Kaufmann, H.,: Betriebsfestigkeit von torsionsbelasteten Wellen für Automatgetriebe (Fatigue Strength of Drive Shafts of Automatic Transmission Gearboxes under Operational Torques) In: Maschinenelemente und Lebensdauer, Gestaltung und Optimierung; 21th Conf. of the DVM-Arbeitskreis Betriebsfestigkeit, Dresden, 11.-12. 10. 1995;Pupl.: Deutscher Verband für Materialforschung und -prüfung, Berlin (1995), pp. 161-172
2. Buxbaum, O.,: Betriebsfestigkeit-Sichere und wirtschaftliche Bemessung schwingbruchgefährdeter Bauteile (Fatigue Strength under Operational Conditions-Safety and Economic Assessment of Cyclically Loaded Components) Verlag Stahleisen mbH, Düsseldorf (1992), 2nd edition
3. Grubišić V.,: Determination of the Load Spectra for Design and Testing In: 3rd Int. Conf. Innovation and Reliability in Automotive Design and Testing, Florence, April 8-10, 1992
4. Heuler, P., Seeger, T.,: Criterion for Omission of Variable Amplitude Loading Histories International Journal of Fatigue 8 (1986), No. 4, pp. 225-230
5. Oppermann, H.,: Zulässige Verkürzung zufallsartiger Lastfolgen für Betriebsfestigkeitsversuche (Allowable Shortening of Random Sequences for Fatigue Strength Testing) In: Papers to the Fourth LBF Colloquium on 8 and 9 March 1988 in Darmstadt;Publ.:, Buxbaum O., Fraunhofer-Institut für Betriebsfestigkeit LBF, Darmstadt; Report No. TB-180(1988), pp. 31-49
6. Schütz, W.,: Über eine Beziehung zwischen der Lebensdauer bei konstanter und bei veränderlicher Beanspruchungsamplitude und ihre Anwendbarkeit auf die Bemessung von Flugzeugbauteilen (A Relationship between the Fatigue Life under Constant and Variable Amplitude Loading and its Application to the Assessment of Aircraft Components) Zeitschrift für Flugwissenschaften 15 (1967) No. 11, pp. 407-419
7. Sonsino, C.M., Grubišić V.,: Mechanik von Schwingbrüchen an gegossenen und gesinterten Konstruktionswerkstoffen unter mehrachsiger Beanspruchung (Mechanics of Fatigue Cracks in Casted and Sintered Construction Materials under Multi-Axial Stresses) Konstruktion 37 (1985) No. 7, pp. 261-269
8. Siebel, E., Stieler, M.,: Ungleichförmige Spannungsverteilung bei schwingender Beanspruchung (Non-Uniform Stress Distribution under Cyclic Loading) VDI-Z 97 (1955) No. 5, pp. 121-126
9. Haibach, E., Ostermann, H., Köbler, H.G.,: Abdecken des Risikos aus Zufälligkeiten weniger Schwingfestigkeitsversuche (Addressing the Risks of Randomness in a Small Number of Fatigue Tests) Fraunhofer-Institut für Betriebsfestigkeit LBF, Darmstadt; Technical memoranda TM No. 68/73 (1973)
10. Haibach, E.,: Betriebsfestigkeit-Verfahren und Daten zur Bauteilberechnung (Fatigue Strength under Operational Conditions-Procedures and Data in the Fatigue Life Assessment of Components) VDI-Verlag GmbH, Düsseldorf (1989)
11. Grubišić V.,: Verfahren zur optimalen Bemessung von Fahrzeugrädern (Procedures for Optimal Assessment of Vehicle Wheels) Fraunhofer-Institut für Betriebsfestigkeit LBF, Darmstadt; Report No. FB-86 (1970)
12. Palmgren, A.,: Die Lebensdauer von Kugellagern (The Fatigue Life of Roller Bearings) VDI-Z. 68 (1924) No. 14, pp. 339-341
13. Miner, M.A.,: Cumulative Damage in Fatigue Journal of Applied Mechanics 12 (1945) No. 3, pp. A159-A164
14. Liu, J.,: Beitrag zur Verbesserung der Dauerfestigkeitsberechnung bei mehrachsiger Beanspruchung (Contribution to the Improvement of Fatigue Life Assessment under Multi-Axial Stresses) Technische Universität Clausthal, Fakultät für Bergbau, Hüttenwesen und Maschinenwesen, Dissertion (1991)
15. Vormwald, M.,: Anriβlebensdauervorhersage auf der Basis der Schwingbruchmechanik für kurze Risse (Crack Initiation Life Prediction on the Basis of Fracture Mechanics for Short Cracks) Heft 47, Veröffentlichung des Instituts für Stahlbau und Werkstoffmechanik der Technischen Hochschule Darmstadt (1989)
16. Vormwald, M.,: The Consequences of Short Crack Closure on Fatigue Crack Growth under Variable Amplitude Loading Fatigue and Fracture of Engineering Materials and Structures, Vol. 14 (1991) No. 2 / 3, pp. 205-225
17. Lipp, W., Svenson, O.,: Beitrag zur vereinfachten Wiedergabe von Beanspruchungen mit veränderlichen Mittelwerten im Schwingfestigkeitsversuch (Contribution to a Simpler Representation of Stresses with Changing Mean Values in Fatigue Testing) Fraunhofer-Institut für Betriebsfestigkeit LBF, Darmstadt; Report No. FB-74 (1967)
18. Endo, T., Anzi, H.,: Refined Rainflow Algorithm: P/V Difference Method International Journal of Material Science, Vol. 30 (1981) No. 328, pp 89-93
19. Smith, K.N., Watson, P., Topper, T.H.,: A Stress-Strain Function for the Fatigue of Metals Journal of Materials 5 (1970) No. 4, pp. 767-778
20. Sonsino, C.M.,: Zur Bewertung des Schwingfestigkeits-verhaltens von Bauteilen mit Hilfe örtlicher Beanspruchungen (The Evaluation of Fatigue Behavior of Components with the Help of Local Stresses) Konstruktion 45 (1993) No. 1, pp. 25-33
21. Bäumel A. jr., Seeger, T.,: Lebensdauerberechnung für inhomogen beanspruchte Bauteile mit Randschicht und Eigenspannung (Fatigue Life Assessment for Non-Uniformly Stressed Components with Surface Layer and Residual Stresses) In: Kerben und Betriebsfestigkeit, 15th Lecture Convention of the DVM Working Group for the Strength of Structures under Operational Conditions, Ingolstadt, 18-19. 10. 1989, pp. 75-88
22. Zacher, P., Seeger, T.,: FILIPP-PC-Programm zur Lebensdauervorhersage nach dem örtlichen Konzept (FlLIPP-PC Program for Fatigue Life Prediction using the Local Concept) Fachgebiet Werkstoffmechanik, Technische Hochschule Darmstadt, FF-1/ 1992
23. Grubišić V., Sonsino, C.M.,: Einfluβgröβen der Betriebsfestigkeit geschmiedeter Bauteile (Influences on the Fatigue Strength of Forged Components) VDI-Z 134 (1992) No. 11, pp. 105-112
24. Kaufmann, H., Sonsino, C.M., Wetter, E.,: Einfluβ von Härtungsparametern auf die Schwingfestigkeit von Gesenkschmiedeteilen (Influence of Hardening Parameters on the Fatigue Strength of Forged Components) VDI-Z 134 (1992) No. 11, pp. 113-117
25. Savaidis, G., Seeger, T.,: Werkstoffmechanische Beanspruchungs- und Lebensdaueranalyse zweistufig schwing-beanspruchter Biegeproben aus 42 CrMo 4 (Stress-Strain and Fatigue Life Analyses on Specimens of 42 CrMo 4 under Two-Step Bending) Materialwissenschaft und Werkstofftechnik 25 (1994) No. 4, pp. 141-151
26. Dowling, N.E., Iyyer, N.S.,: Fatigue Crack Growth and Closure at High Cyclic Strains Materials Science and Engineering 96 (1987), pp. 99-107
27. Schütz, D., Lowak, H.,: Zur Verwendung von Bemessungsunterlagen aus Versuchen mit betriebsähnlichen Lastfolgen zur Lebensdauerabschätzung (The Use of Assessment Data from Experimental Tests under Similar Operational Load Sequences for Fatigue Life Prediction) Fraunhofer-Institut für Betriebsfestigkeit LBF, Darmstadt; Report No. FB-109 (1976)
28. Sonsino, C.M., Kaufmann, H., Grubišić V.,: Übertragbarkeit von Werkstoffkennwerten am Beispiel eines betriebsfest auszulegenden, geschmiedeten Nutzfahrzeug-Achsschenkels (Transferability of Material Data for the Example of a Randomly Loaded Forged Truck Stub Axle; to be published in English in the Proceedings of the 1997 SAE International Congress) Konstruktion 47 (1995) No. 7 + 8, pp. 222-232