The influence of residual stresses on the susceptibility to hydrogen embrittlement in hardened steel components subjected to rolling contact conditions

SAE Technical Papers

Volumn , Issue , 2002, Pages

  Walton, Harry W ^a  

^a NONE

Author keywords

[No Author keywords available]

Indexed keywords

FRICTION; HYDROGEN EMBRITTLEMENT;

ATOMIC HYDROGEN; CATASTROPHIC FAILURES; CONTACTING SURFACES; FRACTURE MORPHOLOGY; HARDENED STEEL COMPONENT; RESIDUAL COMPRESSIVE STRESS; ROLLING CONTACTS;

FRACTURE;

EID: 85072457687     PISSN: 01487191     EISSN: 26883627     Source Type: Journal    
DOI: 10.4271/2002-01-1412     Document Type: Conference Paper

References (23)

1. Ohnishi K., Directionality of Hydrogen Embrittlement in Hot Rolled Steel Plate, Trans. JIM 1971, Vol. 12.
2. McEvily A.J., Le May I., Hydrogen- Assisted Cracking, Materials Characterization (Int. Metallographic Soc.). Vol. 26, 4, 1991, 253-268.
3. Fruehan R. J., A Review of Hydrogen Flaking and Its Prevention, Iron and Steel Maker, 1997, 24 (8) 61-69.
4. Propova L.,. Effect of Zirconium on the Properties of Steel 09G2 after Controlled Rolling, Metal Science and Heat Treatment (English Translation) v 32 n 3-4, Sept. 1990, 267-269.
5. Pressouyre G. M.,. Current Solutions to Hydrogen Problems in Steel, Hydrogen Embrittlement and Stress Corrosion Cracking, ASM Publication 1984
6. Romanov O. N., et al., Hairline Cracking Susceptibility of Alloy Engineering Steels Produced by Different Methods, Steel Translations, 22, (5) May 1992, 222-225.
7. Permitin V. E.,. Mechanism of Flake Formation in Steels, Metal Science and Heat Treatment, 33, (7-8), July 1991, 565-568
8. Pressouyre G. M., Hydrogen Traps, Repellers, and Obstacles in Steel; Consequences on Hydrogen Diffusion, Solubility and Embrittlement. Metallurgical Transactions A., 14A, Oct. 1983, 2189-2193.
9. Hollox G. E., Hobbs R. A., Hampshire J. M.,. Lower Bainite Bearings for Adverse Environments, Wear, 68 (1981)k 229-240.
10. Stiner J. E.,. Control of Flaking and Other Hydrogen Problems in Heavy Forgings. Hydrogen Embrittlement and Stress Corrosion Cracking, ASM Publication 1984
11. Sarrak V. I.,. Delayed Fracture, Hydrogen and Impurities in Steel, Metallovendenie I Termicheskaya Obrabotka Metallov, 8, August 1977, 17-21
12. Hyde R.S.,. Contact Fatigue of Hardened Steel. pp 691-703. ASM Handbook Volume 19. Fatigue and Fracture.
13. Grundberg L., Jamieson D. T., Scott D.,. Hydrogen Penetration in Water Accelerated Fatigue of Rolling Surfaces, Philosophical. Magazine. 8 No 91 (1963) 1553-1568
14. Grundberg L., Scott D., The Acceleration of Pitting Failure by Water in the Lubricant. J. Inst. Petrol., 44 (1958) 406-410
15. Ciruna J. A., Szieleit H. J.,. The Effect of Hydrogen on the Rolling Contact Fatigue Life o f AISI 52100 and 440C Steel Balls. Wear, 24 (1973) 107-118.
16. Grunberg L., The formation of hydrogen peroxide on fresh metal surfaces, Proc. Phys. Soc. (Lond), B66 (1953) 153-161.
17. Scott D., Scott H. M., Proc. European Conf. on Electron Microscopy 1961, Delft, Vol 1, 539
18. Tamada K., Tanaka H., Occurrence of brittle flaking on bearings used for automotive electrical instruments and auxiliary devices. Wear 199 (1996) 245-252.
19. Schlicht H., etal,. Effects of Material Properties on Bearing Steel Fatigue Stength. ASTM STP 987, 81-101
20. Rounds F. G., Some Effects of Additives on Rolling Contact Fatigue. ASLE Trans. 10 (1967) 243-254.
21. Walton H.W., Ubiquitous Hydrogen. 19 th. ASM Heat Treating Society Proceedings Including Steel Heat Treating in the New Millennium 1-4 November 1999, Cincinnati, Ohio
22. Fernandes P.J.L., McDuling C.,. Surface Contact Fatigue Failures in Gears. Engineering Failure Analysis. Vol. 4, No. 2, pp 99, 1997. Elsevier Science Ltd.
23. Hengereer F., Brockmuller U., Sorstrom P.O.,. Through-Hardening or Case-Hardening for Tapered Roller Bearings?. Creative Use of Bearing Steels, ASTM STP 1195, Hoo J.J., Ed., ASTM Philidelphia 1993 pp 21-23