Steady state cracking of PMCS at CYROGENIC temperatures

19th AIAA Applied Aerodynamics Conference

Volumn , Issue , 2001, Pages

  Schoeppner, G A ^a   Kim, R ^b   Donaldson, S L ^a  

^a AIR FORCE RESEARCH LABORATORY   (United States)

^b UNIVERSITY OF DAYTON RESEARCH INSTITUTE   (United States)

Author keywords

Composite laminates; Cryogenic materials; Transverse cracks

Indexed keywords

AERODYNAMICS; CRYOGENICS; FRACTURE; FUEL TANKS; MICROCRACKS; SPACE APPLICATIONS;

COMPOSITE LAMINATE; CRYOGENIC FUEL TANKS; CRYOGENIC MATERIALS; CYROGENIC TEMPERATURE; DAMAGE-TOLERANT DESIGN; STABILITY REQUIREMENTS; TRANSVERSE CRACK; UNIDIRECTIONAL COMPOSITES;

LAMINATED COMPOSITES;

EID: 85067322168     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.2514/6.2001-1216     Document Type: Conference Paper

References (9)

1. Parvizi, A., Garrett, K.W. and Bailey, I.E., Constrained Cracking in Glass Fibre-Reinforced Epoxy Cross-ply Laminates, J. Mater. Sci., 13 (1978) pp. 195-201
2. Garrett, K.W. and Bailey, I.E., Multiple transverse Fracture in 90° Cross-ply Laminates for a Glass Fibrereinforced Polyester, J. Mater. Scl, 12 (1977) pp. 157-168
3. Bailey, I.E., Curtis, P.T. and Parvizi, A., On the Transverse Cracking and Longitudinal Splitting Behaviour of Glass and Carbon Fiber Reinforced Epoxy Cross Ply Laminates and the effect of Poisson and Thermally Generated Strain, Proc. R. Soc. Lond., A 366 (1979) pp. 599-623
4. Pagano, N.J., Schoeppner, G.A., Kim, R. and Abrams, F.L., Steady-State Cracking and Edge Effects in Thermo-Mechanical Transverse Cracking of Cross-Ply Laminates, Composites Science and Technology, 58 (1998) pp. 1811-1825
5. Donaldson, S.L. and Kim, R., Interlaminar Fracture Properties of Composite Materials at Cryogenic Temperatures, Proceedings of the American Society of th Composites 15 Annual Technical Conference, Texas A&M, Sept 24-27, 2000
6. Schoeppner, G.A. and Pagano, N.J., "Stress Fields and Energy Release Rates in Cross-ply Laminates, " International Journal of Solids and Structures, Vol. 35, No. 11, 1998, pp. 1025-1055 (Erratum: Vol. 36, July, 1999, pg. 5327)
7. Schoeppner, G.A. and Pagano, N.J., "3D Thermoelastic Moduli and Saturation Crack Density for Cross-ply Laminates with Transverse Cracks," International Journal of Damage Mechanics, Vol. 8, No. 3, 1999, pp. 273-309
8. Pagano, N.J., "Stress Fields in Composite Laminates, International Journal of Solids and Structures", 1978, 14, 385-400
9. Sandhu, R.S., Sendeckyj, G.P., Schoeppner, G.A. and Pappas, J.E., "Initiation and Prevention of Edge Delamination with and without Residual Stresses," Proceedings of the 74th meeting of the Structures and Materials Panel AGARD, AGARD-CP-530, Patras, Greece, 27-28 May 1992