Undoped Layered Perovskite Oxynitride Li2LaTa2O6N for Photocatalytic CO2 Reduction with Visible Light

Angewandte Chemie - International Edition

Volumn 57, Issue 27, 2018, Pages 8154-8158

  Oshima, Takayoshi ^a,b   Ichibha, Tom ^c   Qin, Ken Sinkou ^c   Muraoka, Kanemichi ^a,b   Vequizo, Junie Jhon M ^d   Hibino, Keisuke ^a   Kuriki, Ryo ^a,b   Yamashita, Shunsuke ^e   Hongo, Kenta ^c,e,f,g   Uchiyama, Tomoki ^h   Fujii, Kotaro ^a   Lu, Daling ^a   Maezono, Ryo ^c,g   Yamakata, Akira ^d   Kato, Hideki ⁱ   Kimoto, Koji ^e   Yashima, Masatomo ^a   Uchimoto, Yoshiharu ^h   Kakihana, Masato ⁱ   Ishitani, Osamu ^a   Kageyama, Hiroshi ^h   Maeda, Kazuhiko ^a   more..

^a TOKYO INSTITUTE OF TECHNOLOGY   (Japan)

^b JAPAN SOCIETY FOR THE PROMOTION OF SCIENCE   (Japan)

^c JAPAN ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY   (Japan)

^d TOYOTA TECHNOLOGICAL INSTITUTE   (Japan)

^e NATIONAL INSTITUTE FOR MATERIALS SCIENCE   (Japan)

^f JAPAN SCIENCE AND TECHNOLOGY AGENCY   (Japan)

^g RIKEN   (Japan)

^h KYOTO UNIVERSITY   (Japan)

ⁱ TOHOKU UNIVERSITY   (Japan)

Author keywords

CO2 reduction; oxynitride; perovskites; photocatalysis; visible light

Indexed keywords

ABSORPTION SPECTROSCOPY; CARBON DIOXIDE; LANTHANUM COMPOUNDS; LIGHT; LIGHT ABSORPTION; NITRIDES; PEROVSKITE; PHOTOCATALYSIS; RUTHENIUM COMPOUNDS; TANTALUM COMPOUNDS;

CO2 REDUCTION; LAYERED PEROVSKITE STRUCTURE; OXYNITRIDES; PHOTOCATALYTIC PERFORMANCE; THREE DIMENSIONAL (3D) STRUCTURES; TRANSIENT ABSORPTION SPECTROSCOPIES; VISIBLE LIGHT; VISIBLE-LIGHT RESPONSIVE PHOTOCATALYSTS;

LITHIUM COMPOUNDS;

EID: 85047743434     PISSN: 14337851     EISSN: 15213773     Source Type: Journal    
DOI: 10.1002/anie.201803931     Document Type: Article

References (32)

1. A. Kudo, Y. Miseki, Chem. Soc. Rev. 2009, 38, 253–278.
2. K. Iizuka, T. Wato, Y. Miseki, K. Saito, A. Kudo, J. Am. Chem. Soc. 2011, 133, 20863–20868;
3. K. Teramura, Z. Wang, S. Hosokawa, Y. Sakata, T. Tanaka, Chem. Eur. J. 2014, 20, 9906–9909.
4. T. Tanaka, K. Shinohara, A. Tanaka, M. Hara, J. N. Kondo, K. Domen, J. Photochem. Photobiol. A 1997, 106, 45–49.
5. K. Shimizu, S. Itoh, T. Hatamachi, T. Kodama, M. Sato, K. Toda, Chem. Mater. 2005, 17, 5161–5166.
6. D. E. Scaife, Solar Energy 1980, 25, 41–54.
7. G. Hitoki, T. Takata, J. N. Kondo, M. Hara, H. Kobayashi, K. Domen, Chem. Commun. 2002, 1698–1699;
8. K. Maeda, K. Teramura, D. Lu, T. Takata, N. Saito, Y. Inoue, K. Domen, Nature 2006, 440, 295;
9. C. Pan, T. Takata, M. Nakabayashi, T. Matsumoto, N. Shibata, Y. Ikuhara, K. Domen, Angew. Chem. Int. Ed. 2015, 54, 2955–2959;
10. Angew. Chem. 2015, 127, 2998–3002;
11. H. Kageyama, K. Hayashi, K. Maeda, J. P. Attfield, Z. Hiroi, J. Rondinelli, K. R. Poeppelmeier, Nat. Commun. 2018, 9, 772.
12. H. Kato, K. Ueda, M. Kobayashi, M. Kakihana, J. Mater. Chem. A 2015, 3, 11824–11829.
13. G. Liu, L. Wang, C. Sun, X. Yan, X. Wang, Z. Chen, S. C. Smith, H. M. Cheng, G. Q. Lu, Chem. Mater. 2009, 21, 1266–1274;
14. A. Mukherji, B. Seger, G. Q. Lu, L. Wang, ACS Nano 2011, 5, 3483–3492.
15. A. Nakada, S. Nishioka, J. J. M. Vequizo, K. Muraoka, T. Kanazawa, A. Yamakata, S. Nozawa, H. Kumagai, S. Adachi, O. Ishitani, K. Maeda, J. Mater. Chem. A 2017, 5, 11710–11719.
16. F. Yoshitomi, K. Sekizawa, K. Maeda, O. Ishitani, ACS Appl. Mater. Interfaces 2015, 7, 13092–13097.
17. K. Sekizawa, K. Maeda, K. Domen, K. Koike, O. Ishitani, J. Am. Chem. Soc. 2013, 135, 4596–4599.
18. S. J. Clarke, K. A. Hardstone, C. W. Michie, M. J. Rosseinsky, Chem. Mater. 2002, 14, 2664–2669;
19. J. A. Schottenfeld, A. J. Benesi, P. W. Stephens, G. Chen, P. C. Eklund, T. E. Mallouk, J. Solid State Chem. 2005, 178, 2313–2321;
20. A. da Silva Maia, F. Cheviré, V. Demange, V. Bouquet, M. Pasturel, S. Députier, R. Lebullenger, M. Guilloux-Viry, F. Tessier, Solid State Sci. 2016, 54, 17–21.
21. M. Kaga, H. Kurachi, T. Asaka, B. Yue, J. Ye, K. Fukuda, Powder Diffr. 2012, 26, 4–8.
22. M. Kakihana, J. Sol-Gel Sci. Technol. 1996, 6, 7–55.
23. Neutron powder diffraction data of Li2LaTa2O6N was also measured at ANSTO in Australia (Proposal No. PP5198). However, the background probably due to the incoherent scattering of Li atom was too high to refine the precise crystal parameters.
24. We tried to quantify the concentration of Li in the synthesized Li2LaTa2O6N by means of inductivity coupled plasma optical emission spectroscopy. However, the Li2LaTa2O6N sample was not completely soluble in any of acid media we examined. Hence we could not determine the Li concentration at the present stage.
25. S. J. Pennycook, D. E. Jesson, Ultramicroscopy 1991, 37, 14–38.
26. R. Abe, M. Higashi, K. Domen, J. Am. Chem. Soc. 2010, 132, 11828–11829.
27. Y. Matsumoto, J. Solid State Chem. 1996, 126, 227–234.
28. S. Balaz, S. H. Porter, P. M. Woodward, L. J. Brillson, Chem. Mater. 2013, 25, 3337–3343.
29. F. Amparo, Inorg. Chem. 2006, 45, 9640–9642.
30. T. Yui, A. Kan, C. Saitoh, K. Koike, T. Ibusuki, O. Ishitani, ACS Appl. Mater. Interfaces 2011, 3, 2594–2600.
31. Figure SXRD and DRS measurements revealed that CaTaO2N and LaTaON2 were successfully synthesized without impurities via polymerized complex route (Supporting Information, 14), and the band gaps were 2.5 and 2.0 eV, respectively, which are consistent with those reported in Refs. [7, 10].
32. A. Yamakata, M. Kawaguchi, N. Nishimura, T. Minegishi, J. Kubota, K. Domen, J. Phys. Chem. C 2014, 118, 23897–23906.