The correlation between crack chemistry and Crack Growth behavior of 7XXX series aluminum alloys: Ca comparison of field and laboratory tests

NACE - International Corrosion Conference Series

Volumn 1999-April, Issue , 1999, Pages

  Cooper, K R ^a   Kelly, R G ^a   Colvin, E L ^b  

^a University of Virginia   (United States)

^b ALCOA TECHNICAL CENTER   (United States)

Author keywords

7xxx series; Aluminum alloy; Crack chemistry; Environment assisted cracking; Field testing

Indexed keywords

ATMOSPHERIC CHEMISTRY; ATMOSPHERIC CORROSION; CALCIUM; CHLORINE COMPOUNDS; CHROMIUM ALLOYS; COPPER ALLOYS; CRACK PROPAGATION; CRACKING (CHEMICAL); CRACKS; CREVICE CORROSION; GROWTH KINETICS; HIGH STRENGTH ALLOYS; LABORATORIES; MAGNESIUM ALLOYS; SULFUR COMPOUNDS; ZINC ALLOYS;

7XXX SERIES; AL -ZN-MG-CU ALLOYS; ATMOSPHERIC EXPOSURES; CRACK GROWTH BEHAVIOR; ENVIRONMENT-ASSISTED CRACKING; FIELD AND LABORATORY TEST; FIELD TESTING; LABORATORY ENVIRONMENT;

ALUMINUM ALLOYS;

EID: 85046776955     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (23)

1. A. Turnbull, "Chemistry Within Localized Corrosion Cavities," Proceedings of the Second International Conference on Localized Corrosion, (Houston, TX: NACE, 1990).
2. B. F. Brown, et al., Journal of the Electrochemical Society, 116, 2 (1969): p. 218.
3. J. A. Davis, "Use of Microelectrodes for Study of Stress Corrosion of Aluminum Alloys," Localized Corrosion, (Houston, TX: NACE, 1971).
4. T. H. Nguyen, et al, Journal of the Electrochemical Society, 129, 4 (1982): p. 780.
5. R. T. Foley, Corrosion, 42, 5 (1986): p. 277.
6. N. J. H. Holroyd, et al, "Environmental Interaction with the Crack Tip Region During Environment Sensitive Fracture of Aluminum Alloys," Embrittlement by the Localized Crack Environment, (Warrendale, PA: The Metallurgical Society of AIME, 1984).
7. T. H. Nguyen, et al, Corrosion, 38, 6 (1982): p. 319.
8. M. Marek, et al, "Solution Chemistry in Crevices and Stress Corrosion Cracks," 6th International Conference on Metallic Corrosion, (Mt. Waverly, VIC: Australian Corrosion Association, 1975).
9. P. Jandik and G. Bonn, Capillary Electrophoresis of Small Molecules and Ions, (NY: VCH Publishers, Inc., 1993), p. 298.
10. P. Jandik, et al, LC/GC, 9, 9 (1991): p. 634.
11. R. G. Kelly, et al, "Determining the Chemical Composition of Occluded Dissolution Sites," Proceedings of the International Symposium on Pits and Pores: Formation, Properties, and Significance for Advanced Luminescent Materials, (Pennington, NJ: The Electrochemical Society, 1997).
12. K. R. Cooper and R. G. Kelly, "Using Capillary Electrophoresis to Study the Chemical Conditions Within Cracks in Aluminum Alloys," Journal of Chromatography A (submitted for publication).
13. M. O. Speidel and M. V. Hyatt, Stress-Corrosion Cracking of High Strength Aluminum Alloys, (NY, NY: Plenum Press, 1972), p. 115.
14. D. O. Sprowls, et al, "Evaluation of Stress-Corrosion Cracking Susceptibility Using Fracture Mechanics Techniques," Alcoa Laboratories, Contract No. NAS 8-21487, 31 May 1973.
15. S. Maitra and G. C. English, Metallurgical Transactions A, 13A, (1982): p. 161.
16. T. J. Summerson and D. O. Sprowls, "Corrosion Behavior of Aluminum Alloys," Aluminum Alloys - Their Physical and Mechanical Properties, (Engineering Materials Advisory Services Ltd., 1986).
17. L. M. Young, et al, "The Effects of Electrode Potential and Temper on Environment Assisted Cracking in AA 7050," Light Weight Alloys for Aerospace Applications IV, (Warrendale, PA: The Minerals, Metals & Materials Society, 1997).
18. T. L. Anderson, Chapter 3 - Elastic-Plastic Fracture Mechanics, (Boston: CRS Press, Inc., 1991), p. 131.
19. C. J. Baes and R. E. Mesmer, The Hydrolysis of Cations, (Malabar, FL: Robert E. Krieger Publishing Company, 1976), p. 489.
20. N. J. H. Holroyd, "Environment-Induced Cracking of High-Strength Aluminum Alloys," Environment-Induced Cracking of Metals, (Houston, TX: NACE, 1990).
21. T. D. Burleigh, Corrosion, 47, 2 (1991): p. 89.
22. F. P. Ford, "A Quantitative Examination of the Slip-Dissolution and Hydrogen Embrittlement Theories of Cracking in Aluminum Alloys," Mechanisms of Environment Sensitive Cracking of Materials, (Warrendale, PA: The Metals Society, 1977).
23. F. P. Ford, et al, Journal of the Electrochemical Society, 127, 6 (1980): p. 1325.