Factors affecting the shape parameter in the weibull distribution with respect to predicting earliest failures by scc

NACE - International Corrosion Conference Series

Volumn 2002-April, Issue , 2002, Pages

  Staehle, Roger W ^a   Fang, Zhi ^b  

^a UNIVERSITY OF MINNESOTA   (United States)

^b Medtronic Corporation   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION; FORECASTING;

CONSERVATIVE VALUE; CONVENTIONAL APPROACH; ENGINEERING JUDGMENTS; FAILURE PROBABILITY; PHYSICAL QUANTITIES; PRINCIPAL VARIABLES; STATISTICAL FRAMEWORK; STATISTICAL PARAMETERS;

WEIBULL DISTRIBUTION;

EID: 85046748802     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (52)

1. R.W. Staehle, "Bases for Predicting the Earliest Failures Due to Stress Corrosion Cracking." Chemistry and Electrochemistry of Corrosion and Stress Corrosion Cracking: A Symposium Honoring the Contributions of R. W. Staehle, Ed. Russell Jones. TMS (The Minerals, Metals and Materials Society,) Warrendale, Pennsylvania, 2001, p. K1.
2. R.W. Staehle, J.A. Gorman, K.D. Stavropoulos, and C.S. Welty, Jr., "Application of Statistical Distributions to Characterizing and Predicting Corrosion of Tubing in Steam Generators of Pressurized Water Reactors," Life Prediction of Corrodible Structures. R.N. Parkins, ed., NACE International, Houston, 1994, p. 1374.
3. T. Shibata, "1996 W.R. Whitney Award Lecture: Statistical and Stochastic Approaches to Localized Corrosion," Corrosion 37, 1996, p. 813.
4. T. Shibata, "Corrosion Probability and Statistical Evaluation of Corrosion Data," Uhlig's Corrosion Handbook: 2nd Edition. W.R. Revie, ed., John Wiley and Sons, New York, 2000, p. 367.
5. D.G. Harlow and R.P. Wei, "A Mechanistically Based Approach to Probability Modeling for Corrosion Fatigue Crack Growth," Engineering Fracture Mechanics 45, 1993, p. 79.
6. R.P. Wei and D.G. Harlow, "A Mechanistically Based Probability Approach for Life Prediction," International Symposium on Plant Aging and Life Predictions of Corrodible Structures. T. Shibata and T. Shoji, eds., NACE International, Houston, 1995, p. 47.
7. N.R. Cawley, D.G. Harlow, and R.P. Wei, "Probability and Statistics Modeling of Constituent Particles and Corrosion Pits as a Basis for Multiple-Site Damage Analysis," FAA-NASA Symposium on the Continued Airworthiness of Aircraft Structures: A97-4010111-05. Office of Aviation Research, Washington, 1997, p. 531.
8. R.P. Wei, "Life Prediction: A Case for Multidisciplinary Research," Fatigue and Fracture Mechanics: Volume 27. STP 1296. R.S. Piascik, J.C. Newman, and N.E. Dowling, eds., American Society for Testing and Materials, Philadelphia, 1997, p. 3.
9. R.P. Wei, "Material Aging and Reliability of Engineered Systems," Environmentally Assisted Cracking: Predictive Methods for Risk Assessment and Evaluation of Materials. Equipment, and Structures: STP 1401. R. Kane, ed., American Society for Testing and Materials, Philadelphia, 2000, p. 3.
10. R.W. Staehle, "Lifetime Prediction of Materials in Environments," Uhlig's Corrosion Handbook: 2nd Edition. R.W. Revie, ed., John Wiley and Sons, New York, 2000, p. 27.
11. R.W. Staehle, "Development and Application of Corrosion Mode Diagrams," Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking. S.M. Bruemmer, E.I. Meletis, R.H. Jones, W.W. Gerberich, F.P. Ford and R.W. Staehle, eds., TMS (The Minerals, Metals & Materials Society), 1992, p. 457.
12. R.W. Staehle, "Combining Design and Corrosion for Predicting Life," Life Prediction of Corrodible Structures. R.N. Parkins, ed., NACE, Houston, 1994, p. 138.
13. R.W. Staehle, "Status and Future of Predicting and Assuring Corrosion Performance," presented at the Second International Conference on Environment Sensitive Cracking and Corrosion Damage. Hiroshima University, Hiroshima, Japan, October, 2001.
14. R.B. Abernethy, The New Weibull Handbook: Second Edition. R.B. Abernethy Publisher, North Palm Beach, Florida, 1996.
15. E.J. Gumbel, "Statistical Theory of Extreme Values and Some Practical Applications," Applied Mathematics 33. U.S. Dept. of Commerce, National Bureau of Standards, Washington, 1954, p. 1.
16. E.J. Gumbel, Statistics of Extremes. Columbia University Press, New York, 1958.
17. J. Galambos, J. Lechner, and E. Simiu, eds., Extreme Value Theory and Applications: Special Publication 866. National Institute of Standards and Technology, Gaithersburg, MD, 1994.
18. W. Weibull, "A Statistical Distribution Function of Wide Applicability," Journal of Applied Mechanics 10, 1951, p. 293.
19. W. Nelson, "Weibull Prediction of a Future Number of Failures," Quality and Reliability Engineering International 16. 2000, p. 23.
20. K.T. Chang, "Analysis of the Weibull Distribution Function," Journal of Applied Mechanics 49, 1982, p. 450.
21. E.D. Eason and L.M. Shusto, Analysis of Cracking in Small Diameter BWR Piping. EPRINP 4394. Electric Power Research Institute, Palo Alto, 1986.
22. J.A. Gorman, R.W. Staehle, and K.D. Stavropoulos, Statistical Analysis of Steam Generator Tube Degradation: NP-7493. EPRI, Palo Alto, 1991.
23. R.W. Staehle, J.A. Gorman, K.D. Stavropoulos, and CS Welty, Jr., "Application of Statistical Distributions to Characterizing and Predicting Corrosion of Tubing in Steam Generators of Pressurized Water Reactors," Life Prediction of Corrodible Structures. R.N. Parkins, ed., NACE International, Houston, 1994, p. 1374.
24. M. Akashi and G. Nakayama, "A Process Model for the Initiation of Stress Corrosion Crack Growth in BWR Plant Materials," Effects of the Environment on the Initiation of Crack Growth. STP 1298. W.A. Van Der Sluys, R.S. Piascik, and R. Zawierucha, eds., American Society for Testing and Materials, Philadelphia, 1997, p. 150.
25. S. Shimada and M. Nagai, "Variation of Initiation Time for Stress Corrosion Cracking in Zircaloy-2 Cladding Tube," Reliability Engineering 9, 1984, p. 19.
26. Z. Fang and R.W. Staehle, Calculations with KalidaGraph Software, Version 3.0.
27. W.L. Clarke and G.M. Gordon, "Investigation of Stress Corrosion Cracking Susceptibility of Fe-Ni-Cr Alloys in Nuclear Reactor Water Environments," Corrosion 29. 1973, p. 1.
28. M Akashi and A. Ohtomo, "Evaluation of the Factor of Improvement for the Intergranular Stress Corrosion Cracking Life of Sensitized Stainless Alloys in Hgh-Temrjerature, High-Purity Water Environment" Journal of the Society of Materials Science of Japan 36. 1987, p. 59.
29. K. Norring, J. Engstrom, and P. Norberg, "Intergranular Stress Corrosion Cracking in Steam Generator Tubing. Testing of Alloy 690 and Alloy 600 Tubes," Proceedings of the Third International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors. G.J. Theus and J.R. Weeks, eds., The Metallurgical Society, Warrendale, Pennsylvania, 1988, p. 587.
30. T. Shibata and T. Takeyama, "Analysis of Stress Corrosion Cracking Failure Times of Type 316 Stainless Steel by the Weibull Distribution," Boshoku Gijutsu 30, 1, 1981, p. 47.
31. T. Shibata and T. Takeyama, "Probability Distribution of Failure Times of Stress Corrosion Cracking of 17Cr-llNi Stainless Steel," Tetsu-To-Hagane 66, 1980, p. 693.
32. P.M. Scott, "2000 F.N. Speller Award Lecture: Stress Corrosion Cracking in Pressurized Water Reactors - Interpretation, Modeling, and Remedies," Corrosion 56, 2000, p. 771.
33. R.J. Jacko, Evaluation of Thermally Treated Alloy 600 in Faulted Secondary and Primary Water Environments: NP-3051 (ext.). Electric Power Research Institute, Palo Alto, 1985.
34. G. Nakayama, M. Akashi, and A. Ohtomo, "A Probabilistic Assessment for the Stress Corrosion Cracking Lifetime of Sensitized 304 Stainless Steel in Sodium Chloride Solutions," ISIJ International 31, 1991, p. 223.
35. T. Shibata, J. Nakata, and S. Fujimoto, "Probability Distribution of SCC Failure Time Type 304 Stainless Steel in CaC12 Solution," Lifetime Prediction of Corrodible Structures. R.N. Parkins, ed., NACE International, Houston, 1994, p. 1064.
36. G.L. Webb, Environmental Degradation of Alloy 600 and Welded Filler Metal EN82 in an Elevated Temperature Aqueous Environment: WAPD-T-2989. Bettis Atomic Power Laboratory, Pittsburgh, 1993.
37. R.J. Jacko, Corrosion Evaluation of Thermally Treated Alloy 600 Tubing in Primary and Faulted Secondary Water Environments: NP-6721-SD. Electric Power Research Institute, Palo Alto, 1990.
38. R.W. Cochran and R.W. Staehle, "Effects of Surface Preparation on Stress Corrosion Cracking of Type 310 Stainless Steel in Boiling 42% Magnesium Chloride," Corrosion 24, 1968, p. 369.
39. T. Shibata, K. Furusaki, and J. Nakata, "Probability Distribution of Crack Initiation and Propagation Times for Stress Corrosion Cracking of Type 304 Stainless Steel," Boshoku Gijutsu 33, 1984, p. 223.
40. T. Shibata, A. Asada, and J. Nakata, "Effect of Surface Conditions on the Probability Distribution of Stress Corrosion Cracking Failure Times of Type 304 Stainless Steel," Boshoku Gijutsu 34, 1985, p. 23.
41. T. Shibata, S. Fujimoto, A. Asada, and J. Nakata, "Effect of CaC12 Concentration on the Probability Distribution of Stress Corrosion Cracking Failure Time of Type 304 Stainless Steel," 10th International Congress on Metallic Corrosion. K.I. Vasu, Chair, Trans Tech Publications, Switzerland, 1987, p. 1892.
42. T. Shibata, J. Nakata, and S. Fujimoto, "Probability Distribution of SCC Failure Time Type 304 Stainless Steel in CaC12 Solution," Lifetime Prediction of Corrodible Structures. R.N. Parkins, ed., NACE International, Houston, 1994, p. 1064.
43. S. Zhang, T. Shibata, and T. Haruna, "Initiation and Propagation of IGSCC for Sensitized Type 304 Stainless Steel in Dilute Sulfate Solutions," Corrosion Science 39, 1997, p. 1725.
44. T. Shibata and T. Takeyama, "Stochastic Theory of Pitting Corrosion," Corrosion 33, 1977, p. 248.
45. T. Shibata and T. Takeyama, "Death and Birth Stochastic Process in Pitting Corrosion of 17Cr Ferritic Stainless Steels," Proceedings of the 6th International Congress on Metallic Corrosion. 1981, p. 146.
46. T. Shibata and K. Okamoto, "Estimation of Maximum Pit Depth on the Oil Tank Base Plate by Extreme Value Analysis," Bositoku Gijutsu 30, 1981, p. 404.
47. T. Shibata, "Surface Area Dependence of Pitting Potential," Bositoku Gijutsu 31, 1982, p. 643.
48. T. Shibata, "Stochastic Approach to the Effect of Alloying Elements on the Pitting Resistance of Ferritic Stainless Steels," Transactions ISIJ 23, 1983, p. 785.
49. T. Shibata, "Development of Stochastic Models of Pit Generation," Journal of the Electrochemical Society 134, 1987, p. 418.
50. S. Takasaki and T. Kontani, "Evaluation of Pitting Corrosion of Heat Exchanger Tubes in Cooling Water by Extreme Value Statistical Analysis," Zairyo 36, 1987, p. 72.
51. T. Shibata, "Stochastic Studies of Passivity Breakdown," Corrosion Science 31, 1990, p. 413.
52. E. Sato, H. Abo, and T. Murata, "Lifetime Estimation and Accelerated Stress Corrosion Cracking Test of Stainless Steel in a Neutral Chloride Environment," Corrosion 46, 1990, p. 924.