Diameter-Controlled Synthesis and Capacitive Performance of Mesoporous Dual-Layer MnO2 Nanotubes

ChemNanoMat

Volumn 1, Issue 3, 2015, Pages 159-166

  Huang, Yunpeng ^a   Liang, Zhengyong ^b   Miao, Yue E ^a   Liu, Tianxi ^a  

^a FUDAN UNIVERSITY   (China)

^b ZHENGZHOU UNIVERSITY   (China)

Author keywords

carbon; electrospinning; MnO2 nanotubes; nanofibers; supercapacitors

Indexed keywords

CAPACITANCE; CARBON; CARBON NANOFIBERS; CARBONIZATION; ELECTRODES; ELECTROSPINNING; MESOPOROUS MATERIALS; NANOFIBERS; NANOSHEETS; NANOTUBES; POTASH; REDOX REACTIONS; SUPERCAPACITOR;

CAPACITIVE PERFORMANCE; CONTROLLED SYNTHESIS; ELECTRODE MATERIAL; NANOFIBROUS MEMBRANES; NANOTUBE ELECTRODES; REACTION TEMPERATURE; SACRIFICIAL TEMPLATE METHODS; SPECIFIC CAPACITANCE;

MANGANESE OXIDE;

EID: 85013181089     PISSN: None     EISSN: 2199692X     Source Type: Journal    
DOI: 10.1002/cnma.201500016     Document Type: Article

References (46)

1. S. S. Lee, H. W. Bai, Z. Y. Liu, D. D. Sun, Appl. Catal. B 2013, 140–141, 68–81.
2. X. Wang, H. Q. Fan, P. R. Ren, Catal. Commun. 2013, 31, 37–41.
3. Z. L. Wang, D. Xu, J. J. Xu, X. B. Zhang, Chem. Soc. Rev. 2014, 43, 7746–7786.
4. Y. P. Huang, Y. E. Miao, S. S. Ji, W. W. Tjiu, T. X. Liu, ACS Appl. Mater. Interfaces 2014, 6, 12449–12456.
5. T. Maiyalagan, J. Sundaramurthy, P. S. Kumar, P. Kannan, M. Opallo, S. Ramakrishna, Analyst 2013, 138, 1779–1786.
6. C. Peng, G. G. Li, D. L. Geng, M. M. Shang, Z. Y. Hou, J. Lin, Mater. Res. Bull. 2012, 47, 3592–3599.
7. A. Ghosh, E. J. Ra, M. H. Jin, H. Jeong, T. H. Kim, C. Biswas, Y. H. Lee, Adv. Funct. Mater. 2011, 21, 2541–2547.
8. J. Yan, E. Khoo, A. Sumboja, P. S. Lee, ACS Nano 2010, 4, 4247–4255.
9. X. L. Huang, J. Chai, T. Jiang, Y. J. Wei, G. Chen, W. Q. Liu, D. X. Han, L. Niu, L. M. Wang, X. B. Zhang, J. Mater. Chem. 2012, 22, 3404–3410.
10. Z. Wu, X. L. Huang, Z. L. Wang, J. J. Xu, H. G. Wang, X. B. Zhang, Sci. Rep. 2014, 4, 3669.
11. G. M. Wang, H. Y. Wang, Y. C. Ling, Y. C. Tang, X. Y. Yang, R. C. Fitzmorris, C. Wang, J. Z. Zhang, Y. Li, Nano Lett. 2011, 11, 3026–3033.
12. L. L. Zhang, X. B. Zhang, Z. L. Wang, J. J. Xu, D. Xu, L. M. Wang, Chem. Commun. 2012, 48, 7598–7600.
13. H. Y. Chen, T. L. Zhang, J. Fan, D. B. Kuang, C. Y. Su, ACS Appl. Mater. Interfaces 2013, 5, 9205–9211.
14. G. R. Yang, W. Yan, J. N. Wang, H. H. Yang, CrystEngComm 2014, 16, 6907–6913.
15. H. Xia, J. K. Feng, H. L. Wang, M. O. Lai, L. Lu, J. Power Sources 2010, 195, 4410–4413.
16. Y. E. Miao, R. Y. Wang, D. Chen, Z. Y. Liu, T. X. Liu, ACS Appl. Mater. Interfaces 2012, 4, 5353–5359.
17. Y. E. Miao, S. X. He, Y. L. Zhong, Z. Yang, W. W. Tjiu, T. X. Liu, Electrochim. Acta 2013, 99, 117–123.
18. M. Y. Wang, J. Ioccozia, L. Sun, C. J. Lin, Z. Q. Lin, Energy Environ. Sci. 2014, 7, 2182–2202.
19. J. G. Yu, G. P. Dai, B. B. Huang, J. Phys. Chem. C 2009, 113, 16394–16401.
20. E. Eustache, P. Tilmant, L. Morgenroth, P. Roussel, G. Patriarche, D. Troadec, N. Rolland, T. Brousse, C. Lethien, Adv. Energy Mater. 2014, 4, 13016128.
21. C. Tang, Q. Zhang, M. Q. Zhao, G. L. Tian, F. Wei, Nano Energy 2014, 7, 161–169.
22. L. Li, Z. Wu, S. Yuan, X. B. Zhang, Energy Environ. Sci. 2014, 7, 2101–2122.
23. Z. Y. Zhang, F. Xiao, L. H. Qian, J. W. Xiao, S. Wang, Y. Q. Liu, Adv. Energy Mater. 2014, 4, 1400064.
24. J. Zhu, Z. Xu, B. N. Lu, Nano Energy 2014, 7, 114–123.
25. Z. J. Fan, J. Yan, L. J. Zhi, Q. Zhang, T. Wei, J. Feng, M. L. Zhang, W. Z. Qian, F. Wei, Adv. Mater. 2010, 22, 3723–3728.
26. M. Kaempgen, C. K. Chan, J. Ma, Y. Cui, G. Gruner, Nano Lett. 2009, 9, 1872–1876.
27. M. Remskar, A. Mrzel, Z. Skraba, A. Jesih, M. Ceh, J. Demšar, P. Stadelmann, F. Lévy, D. Mihailovic, Science 2001, 292, 479–481.
28. W. Xiao, H. Xia, J. Y. H. Fuh, L. Lu, J. Power Sources 2009, 193, 935–938.
29. D. D. Han, X. Y. Jing, P. C. Xu, Y. S. Ding, J. Y. Liu, J. Solid State Chem. 2014, 218, 178–183.
30. Y. P. Huang, Y. E. Miao, W. W. Tjiu, T. X. Liu, RSC Adv. 2015, 5, 18952–18959.
31. Y. F. Shen, R. P. Zerger, R. N. DeGuzman, S. L. Suib, L. McCurdy, D. I. Potter, C. L. OYoung, Science 1993, 260, 511–515.
32. Y. S. Ding, X. F. Shen, S. Sithambaram, S. Gomez, R. Kumar, V. M. B. Crisostomo, S. L. Suib, M. Aindow, Chem. Mater. 2005, 17, 5382–5389.
33. J. Y. Tao, N. S. Liu, W. Z. Ma, L. W. Ding, L. Y. Li, J. Su, Y. H. Gao, Sci. Rep. 2013, 3, 2286.
34. J. P. Liu, J. Jiang, C. W. Cheng, H. X. Li, J. X. Zhang, H. Gong, H. J. Fan, Adv. Mater. 2011, 23, 2076–2081.
35. J. F. Wang, G. Zhu, L. J. Deng, L. P. Kang, Z. P. Hao, Z. H. Liu, CrystEngComm 2012, 14, 8253–8260.
36. W. B. Yan, T. Ayvazian, J. Y. Kim, Y. Liu, K. C. Donavan, W. D. Xing, Y. G. Yang, J. C. Hemminger, R. M. Penner, ACS Nano 2011, 5, 8275–8287.
37. L. Y. Yuan, X. H. Lu, X. Xiao, T. Zhai, J. J. Dai, F. C. Zhang, B. Hu, X. Wang, L. Gong, J. Chen, C. G. Hu, Y. X. Tong, J. Zhou, Z. L. Wang, ACS Nano 2012, 6, 656–661.
38. X. Zhang, X. Z. Sun, H. T. Zhang, C. Li, Y. W. Ma, Electrochim. Acta 2014, 132, 315–322.
39. P. Yu, X. Zhang, D. L. Wang, L. Wang, Y. W. Ma, Cryst. Growth Des. 2009, 9, 528–533.
40. Y. Dzenis, Science 2004, 304, 1917–1919.
41. A. Greiner, J. H. Wendorff, Angew. Chem. Int. Ed. 2007, 46, 5670–5703;
42. Angew. Chem. 2007, 119, 5770–5805.
43. M. Inagaki, Y. Yang, F. Kang, Adv. Mater. 2012, 24, 2547–2566.
44. Y. P. Huang, Y. E. Miao, L. S. Zhang, W. W. Tjiu, J. S. Pan, T. X. Liu, Nanoscale 2014, 6, 10673–10679.
45. H. O. Pierson, Handbook of Carbon, Graphite, Diamond, and Fullerenes: Properties, Processing, and Applications, Noyes Publications, 1993.
46. W. Xiao, D. L. Wang, X. W. Lou, J. Phys. Chem. C 2010, 114, 1694–1700.