Analysis of hydrogen permeation through pipeline steel in near-neutral ph SCC environments

Proceedings of the Biennial International Pipeline Conference, IPC

Volumn 2, Issue , 2000, Pages 1479-1485

  Cheng, Yufeng ^a   Yang, Lin ^a   King, Fraser ^a  

^a NOVA CHEMICALS CORPORATION   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION; CORROSION RATE; HYDROGEN; PIPELINES; STRESS CORROSION CRACKING;

CORROSION RATE MEASUREMENTS; HYDROGEN PERMEATION; HYDROGEN PERMEATION FLUX; MICROBIAL ACTIVITIES; NEAR NEUTRAL PH SCC; NEAR-NEUTRAL PH STRESS CORROSION CRACKINGS; OPEN CIRCUIT POTENTIAL; SULFATE REDUCING BACTERIA;

PERMEATION;

EID: 84994787708     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1115/IPC2000-216     Document Type: Conference Paper

References (23)

1. Jack, T.R., Van Boven, G., Wilmott, M., Sutherby, R.L., and Worthingham, R.G., 1994, "Cathodic Protection Potential Penetration under Disbonded Pipeline Coating, " Materials Performance, Vol. 33, pp. 17-21.
2. Kamimura, T., and Kishikawa, H., 1998, "Mechanism of Cathodic Disbonding of Three-Layer Polyethylene-coated Steel Pipe, " Corrosion, Vol. 54, pp. 979-987.
3. Jack, T., 1999, "Asphalt Coating: Summary of Failure Modes and Effects Analysis, " NRTC Report #01369, NOVA Research & Technology Corporation, Calgary, Canada.
4. Stehmeier, L., 1999, "Survey of High Integrity Coatings Used on Canadian Oil and Gas Pipelines, " NRTC Report #01326, NOVA Research & Technology Corporation, Calgary, Canada.
5. Wilmott, M., Erno, B., Jack, T., and Worthingham, R., 1998, "The Role of Coatings in the Development of Corrosion and Stress Corrosion Cracking on Gas Transmission Pipeline, " Proceedings, International Pipeline Conference, The American Society of Mechanical Engineering, Vol. 1, pp. 399-408.
6. Jack, T.R., Wilmott, M., Sutherby, R.L., and Worthingham, R.G., 1996, "External Corrosion of Line Pipe - A Summary of Research Activities, " Materials Performance, Vol. 35, pp. 18-24.
7. Jack, T.R., Emo, B., Krist, K., and Fessler, R.R., 2000, "Generation of Near-neutral pH and High pH SCC Environments on Buried Pipelines, " Proceedings, Corrosion'2000, NACE, pp. 1262-11262.
8. King, F., Jack, T., Chen, W., Wilmott, M., Fessler, R.R., and Krist, K., 2000, "Mechanistic Studies of Initiation and Early Stage Crack Growth for Near-neutral pH SCC on Pipelines, " Proceedings, Corrosion'2000, NACE, pp. 1361-21361.
9. Wilmott, M., and Chen, W., 1998, "Assessment of the Aggressiveness of Various Types of Solutions Towards Low pH SCC, " NRTC Report #01312, NOVA Research & Technology Corporation, Calgary, Canada.
10. Devanathan, M.A.V., and Stachurski, Z., 1962, "The Adsorption and Diffusion of Electrolytic Hydrogen in Palladium, " Royal Society Proceeding Series A, Vol. 270, pp. 90-102.
11. Stem, M., and Geary, A.L., 1957, J. Electrochem. Soc., Vol. 104, pp. 56.
12. Dafft, E.G., Bohnenkamp, K., and Engell, H.J., 1979, "Investigations of the Hydrogen Evolution Kinetics and Hydrogen Absorption by Iron Electrodes During Cathodic Polarization, " Corrosion Science, Vol. 19, pp. 591-612.
13. Chaudhari, B.S., and Radhakrishnan, T.P., 1990, "Boundaiy Conditions during the Electropermeation of Hydrogen Through Pure Iron, " Corrosion Science, Vol. 30, pp. 1219-1234.
14. 2S Concentration and pH on Hydrogen Permeation in AISI 410 Stainless Steel in 5% NaCI, " Corrosion Science, Vol. 29, pp. 89-104.
15. Zhang, T.Y., Zheng, Y.P., and Wu, Q.Y., 1999, "On the Boundary Conditions of Electrochemical Hydrogen Permeation Through Iron, " J. Electrochem. Soc., Vol. 146, pp. 1741-1750.
16. Zakroczymski, T., and Szklarska-Smialowska, Z., 1985, "Activation of the Iron Surface to Hydrogen Absorption Resulting from a Long Cathodic Treatment in NaOH Solution, " J. Electrochem. Soc., Vol. 132, pp. 2548-2552.
17. Stevens, M.F., and Bernstein, I.M., 1989, "Microstructural Trapping Effects on Hydrogen Induced Cracking of a Microalloyed Steel, " Metall. Trans. A, Vol. 20A, pp. 909-919.
18. Chen, W., Wilmott, M., and Jack, T., 1999, "Hydrogen Permeation and Surface Deterioration of Pipeline Steel Exposed to Neutral pH SCC Environment, " NRTC Report #01311, NOVA Research & Technology Corporation, Calgary, Canada.
19. Zakroczymski, T., Lukomski, N., and Flis, J., 1995, "The Effect of Plasma Nitriding-base Treatments on the Absorption of Hydrogen by Iron, " Corrosion Science, Vol. 37, pp. 811-822.
20. Cheng, Y.F., and Du, Y.L., 1993, 'Design of an Electrochemical Probe for Monitoring Susceptibility of Steel in Pickling to Hydrogen-induced Cracking, " Corrosion, Vol. 49, pp. 776-781.
21. Iyer, R.N., Takeuchi, I., Zamanzadeh, M., and Pickering, H.W., 1990, "Hydrogen Sulfide Effect on Hydrogen Entry into Iron - A Mechanistic Study, " Corrosion, Vol. 46, pp. 460-467.
22. Al-Janabi, Y.T., and Lewis, A.L., 1995, "Electrochemical Hydrogen Permeation Studies of Several Mono-And Diamines, " J. Electrochem. Soc., Vol. 142, pp. 2865-2872.
23. King, F., and Chen, W., 1999, "Surface Characteristics of Pipeline Steel Under Non-disbonded Polyethylene Tape Coatings, " NRTC Report #01359, NOVA Research & Technology Corporation, Calgary, Canada.