The relationship between hydrogen permeation and sulfide stress cracking susceptibility of OCTG materials at different temperatures and PH values

NACE - International Corrosion Conference Series

Volumn 1997-March, Issue , 1997, Pages

  Vera, J R ^a   Case, R ^a   Castro, A ^b  

^a PDVSA INTEVEP   (Venezuela)

^b Lagoven   (Venezuela)

Author keywords

Fracture Mechanics; High strength steels; Hydrogen Permeation; Sour Service; Sulfide stress cracking; Testing Criteria

Indexed keywords

CRACKS; FRACTURE MECHANICS; FRACTURE TESTING; HIGH STRENGTH STEEL; PERMEATION; PH; SULFUR COMPOUNDS;

FIELD CONDITIONS; HYDROGEN CONCENTRATION; HYDROGEN PERMEATION; LABORATORY TEST; SATURATED SOLUTIONS; SOUR SERVICES; SULFIDE STRESS CRACKING; TESTING CRITERIA;

HYDROGEN SULFIDE;

EID: 84991434834     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (24)

1. R.S. Treseder, T.M. Swanson. Corrosion, 24, 31 (1968): pp 31-37.
2. A. Ikeda, T. Kudo, Y. Okada, S. Mukai, F. Terasaki. "Corrosion Behaviors of High Alloy Oil Country Tubular Goods for Deep Sour Gas Well". Corrosion/84, paper No 206, (Houston, TX: NACE International 1984).
3. E. Pugh. "A post Conference Evaluation of Our Understanding of the Failure Mechanisms". Stress Corrosion Cracking and hydrogen embrittlement of Iron Base Alloys. (Houston, TX, NACE International, 1977)
4. M. Kermani, D. Harrop, M.L.R. Truchon, J.L. Crolet, "Experimental limits of sour service for tubular steels", Corrosion91, Paper No 21. (Houston, TX, NACE International, 1991).
5. National Association of Corrosion Engineers, Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking in H2S Enviroments. TMO177-90. (1990).
6. M. Bonis, J.L. Crolet, Corr. Sci., Vol. 27 (1987): p. 1059.
7. J. Jelinek, S. D'agata, M. Bonis, M. F. Louge, J. L. Crolet "Selection of a C110 casing grade for midly sour service" Eurocorr 94, Vol 3, (London EFC 1994): pp 24-42.
8. J. Payer, W. Berry, W. Boyd. Evaluation of Slow Strain Rate Stress Corrosion Tests Results, Stress Corrosion Cracking - The Slow Strain Rate Technique, ASTM STP 655, ASTM (1979): pp 61-77.
9. H.L. Ewalds, R.J.H. Wanhill. Fracture Mechanics, Edward Arnold (Ed.). London, Delftse Uitgevers Maatschappij, (1985) pp 193-205.
10. R. Case, J. Vera, A. Viloria, M. Staia, "Effect of the Environment on the Sulfide Stress Cracking in High Strength Steels by Fracture Mechanics" (in Spanish). 1st NACE Latin American Corrosion Conference, 2, paper 94100 (Houston, TX, NACE International, 1994).
11. M. Kermani, D. Harrop, R. MacGuish, J. Vera. "Sulphide Stress Cracking of Dowhole Tubular Steels". Corrosion/91, 1991, Paper No 272. (Houston TX: NACE International 1991).
12. M.B Kernani, D.A. Creamer, J.T. Smith, J.R. Vera. "The effect of Hydrogen Permeation on the SSC Performance of Tubular Steels. Corrosion/93, Paper No 122. (Houston TX: NACE International 1993).
13. R. Kane, J. Greer. J. Pet. Techn. Vol. 7, (1977), pp 558-563.
14. R. Case, C. Sequera, J. R. Vera. "The use of ACPD technique in assessing cracking propagation and KISSCC of high strength OCTG materials in sour media". Submitted to Corrosion/97. Paper No 46 (Houston TX: NACE International 1997).
15. M.A.V. Devanathan, Z. Stachurski. Proc. of the Royal Society. A 270 (1962): pp. 90-102.
16. R. Driver. J. Electrochem. Soc., Vol. 128, 11 (1981): pp.2367-2369.
17. N. Boes, H. Züchner, J. of Less Com. Met., 49 (1976): pp 223-240.
18. M. Wilhelm, J. Vera, N. Hackerman. J. Electrochemical Society: Accelerated Brief Communication, Vol.130, 10 (1983): pp.2129-2132
19. O. Yepez, J.R. Vera, R. Callarotti. "A Comparison between an Electrochemical and a Vacuum Loss Technique as Hydrogen Probes for Corrosion Monitoring". Submitted to Corrosion/97. Paper No 272 (Houston TX: NACE International 1997).
20. A. Turnbull, M. Saenz de Santa Maria, N.D. Thomas, Corr. Sci. Vol. 29 (1989): p 89.
21. M. Kermani, R. MacGuish, J. Smith, R. Case, J. Vera. "The effect of Environmental Variables on Crack Propagation of Carbon Steels in Sour Media". International Corrosion Conference (ICC), Vol.4, p.2639. (Houston TX: NACE International 1993).
22. K. Kiuchi, R.B. McLellan. "The diffusion of hydrogen in well annealed and deformed iron". Department of mechanical engineering and materials science. Rice University. Houston, Texas (1981).
23. P. Manolatos, M. Jerome, C. Duret-Thual, J. Le Coze, Corr. Sci., Vol 37, No 11 (1995):p 1773.
24. A. Turnbull. Standardisation of Hydrogen Permeation Measurement by Electrochemical Technique. National Physical Laboratory. England