DCB test: A review of Critical Parameters

NACE - International Corrosion Conference Series

Volumn 1999-April, Issue , 1999, Pages

  Guntz, G C ^a   Linne, C P ^a   Puissochet, F ^a   Orlans Joliet, B J ^a   Poepperling, R K ^b   Fliethmann, J M ^b  

^a Vallourec Research Center   (France)

^b Mannesmann Research Center (MFI)   (Germany)

Author keywords

C90,C95,C100,C110; Carbon steels; Casing; DCB test; Fracture mechanics; High strength; Hydrogen sulphide; Oil country tubular goods; Sour environment; Sulfide stress cracking

Indexed keywords

CANTILEVER BEAMS; CARBON STEEL; CORROSION; CRACKS; FRACTURE; FRACTURE MECHANICS; HYDROGEN SULFIDE; NATURAL GAS WELL COMPLETION; SULFUR COMPOUNDS; TENSILE TESTING;

C90,C95,C100,C110; CASING; DCB TESTS; HIGH STRENGTH; OIL COUNTRY TUBULAR GOODS; SOUR ENVIRONMENT; SULFIDE STRESS CRACKING;

ACCEPTANCE TESTS;

EID: 84991340803     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (13)

1. NACE TM0177-90 Standard (1990)
2. EFC report no 16, "Guidelines on materials requirements for carbon and low alloy steels for H2S-containing environments in oil and gas production", The Institute of Materials (1995)
3. R.B. Heady "Evaluation of sulfide corrosion cracking resistance in low alloy steels", Corrosion NACE Vol. 33, No 3, March 1977, pp 99-107, (1977)
4. H. Asahi, Y. Tsuikano, M. Ueno "Sulfide stress cracking resistance evaluation methods for steels used in oil field environments: features and problems", Corrosion 91, Cincinnati, paper 29, (1991)
5. API 5CT
6. C.R. Morales, T.E. Perez, G.L. Fitzsimons "Sulfide stress cracking: some observations about the DCB test". Corrosion 97, New Orleans, paper 52, (1997)
7. K.E. Szklarz, T.E. Perez, "Observations on the use of the DCB specimen for sulfide stress corrosion test", Corrosion 95, Orlando, paper 48 (1995)
8. D. L. Sponseller "Interlaboratory testing of seven alloys for SSC resistance by the DCB (TM0177-90D) method", Corrosion 91, Cincinnati, paper 3, (1991)
9. T.E. Perez, "A modified K1SSC calculation for DCB specimens", Corrosion 93, Houston, paper 142 (1993)
10. G. Echaniz, C.R. Morales, T.E. Perez "The effect of microstructure on the Klssc low alloy carbon steels", Corrosion 98, San Diego, paper 120, (1998)
11. A.D. Gourlie, G.N. Podolski, J.R. Fleet "A measurement system evaluation of the DCB test and a comparative anlysis of the effect of different coupons on DCB performance", Corrosion 89, New Orleans, paper 10, (1989)
12. C.P. Linne, F. Blanchard, B. Orlans-Joliet, B. Hamilton "Heavy wall casings in C110 grade for sour service", Corrosion 98, San Diego, paper 117, (1998)
13. V.I. Astafjev, P.S. Shmelev, T.V. Tetjueva "Modified DCB test for sulfide stress cracking of tubular steels", Corrosion NACE Vol. 50, No 12, May 1994 pp 947-952, (1994)