A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements

Journal of the American Ceramic Society

Volumn 64, Issue 9, 1981, Pages 533-538

  ANSTIS, G R ^a   CHANTIKUL, P ^a   LAWN, B R ^a   MARSHALL, D B ^a  

^a UNIVERSITY OF NEW SOUTH WALES   (Australia)

Author keywords

[No Author keywords available]

Indexed keywords

EID: 84987335986     PISSN: 00027820     EISSN: 15512916     Source Type: Journal    
DOI: 10.1111/j.1151-2916.1981.tb10320.x     Document Type: Article

References (35)

1. Indentation Fracture: Principles and Applications
2. Microfracture Beneath Point Indentations in Brittle Solids
3. Equilibrium Penny‐Like Cracks in Indentation Fracture
4. Indentation Plasticity and the Ensuing Fracture of Glass
5. Quasi‐Static Solid Particle Damage in Brittle Materials
6. A Model for Crack Initiation in Elastic/Plastic Indentation Fields
7. Hardness, Toughness and Brittleness: An Indentation Analysis
8. Residual Stress Effects in Sharp‐Contact Cracking: I
9. Residual Stress Effects in Sharp‐Contact Cracking: II
10. Elastic/Plastic Indentation Damage in Ceramics: The Median/Radial Crack System
11. Fracture Mechanics Applied to Brittle Materials
12. Occurrence of Crack Formation During Vickers Indentation as a Measure of the Toughness of Hard Metals
13. On the Theory of Hertzian Fracture
14. A Comparative Study of the Fracture of Various Silica Modifications Using the Hertzian Test
15. Hertzian Fracture of Glass Ceramics
16. Prediction of Fracture Surface Energy from Microhardness Indentation in Structural Ceramics
17. Fracture Toughness Determinations by Indentation
18. Effects of Residual Stresses on Fracture from Controlled Surface Flaws
19. A Note on the Residual Stress About a Pointed Indentation Impression in a Brittle Solid
20. Indentation Deformation/Fracture of Normal and Anomalous Glasses
21. Fracture Surface Energy of Glass
22. Critical Analysis of the Theory of the Double Cantilever Method
23. On Techniques for Emplacing Small Cracks of Controlled Size in Brittle Solids
24. 4
25. 4
26. Controlled Surface Flaws in Hot‐Pressed SiC
27. Stress Corrosion Cracking of a 6% Cobalt/Tungsten Carbide Hard Metal
28. On the Indentation Fracture of Cemented Carbide: I
29. An Indentation Technique for Measuring Stresses in Tempered Glass Surfaces