Environment Sensitive Fracture

Materials Science and Technology: A Comprehensive Treatment

Volumn 1-2, Issue , 2008, Pages 207-263

  Magnin, Thierry ^a   Combrade, Pierre ^b  

^a CENTRE SMS   (France)

^b AREVA NP   (France)

Author keywords

Corrosion cracking; Deformation interaction; Hydrostatic stress; Macroscopic effects; Material environment

Indexed keywords

CONDENSED MATTER PHYSICS; MATERIALS SCIENCE;

DEFORMATION INTERACTIONS; ENVIRONMENT-SENSITIVE; HYDROSTATIC STRESS; MACROSCOPIC EFFECTS;

STRESS CORROSION CRACKING;

EID: 84954226449     PISSN: None     EISSN: None     Source Type: Book    
DOI: 10.1002/9783527619306.ch5     Document Type: Chapter

References (96)

1. Amzallag, C., Mayonobe, C., Rabbe, P. (1981), ASTM-STP, 69.
2. Amzallag, C., Bernard, J. L., Slama, G. (1984), in: Proc. Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Myrtle Beach, South CA, NACE, p. 727.
3. Andresen, P. L. (1993), in: Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems, Water Reactors, TMS.
4. Atkinson, J., Tice, D., Scott, P. M. (1985), in: Proc. of the 2nd IAEA Specialist's Meeting on Subcritical Crack Growth, Sendaï: Cullen, W. H. (Ed.). NUREG/CP-0067, Vol 1, p. 251.
5. Bamford, W. (1977), Inst. Mech. Eng. Conf. Publ. 4, 51.
6. Bastien, P., Azou, P. (1951), CRAS 232, 1854.
7. Bayerlein, M., Mughrabi, H. (1992), in: Short Fatigue Cracks, ESIS 13: Miller, K. J., de los Rios, E. R. (Eds.). London: MEP, p. 55.
8. Beachem, C. D. (1972), Metall. Trans. 3, 437.
9. Beavers, J. A., Pugh, E. N. (1980), Metall. Trans. A 11A, 809.
10. Birbaum, H. K. (1990), Environment Induced Cracking of Metals, NACE 10: Gangloff, R. P., Ives, M. B. (Eds.). Houston: NACE, p. 21.
11. Birnbaum, H. K., Robertson, I. M., Sofronis, P., Teter, D. in: [2], p. 172.
12. Boursier, J. M., de Bouvier, O., Gras, J.-M., Noel, D., Rios, R., Vaillant, F. (1993), in: Corrosion-Deformation Interactions, CDI'92: Magnin, T., Gras, J. M. (Eds.). Les Ulis, France: Les Editions de Physique, p. 117.
13. Cassagne, T. (1992), in: Corrosion sous Contrainte: Desjardins, D., Oltra, R. (Eds.). Les Ulis, France: Les Editions de Physique, p. 685.
14. Cassagne, T. B., Flanagan, W. F., Lichter, B. D. (1986), Metall. Trans. A 17A, 703.
15. Cassagne, T. B., Flanagan, W. F., Lighter, B. D. (1987), in: Chemistry and Physics of Fracture: Latanision, R. M., Jones, R. H. (Eds.). Dordrecht: Mar-tinus Nijhoff, p. 659.
16. Chambreuil-Paret, A., Chateau, J. P., Magnin, T. (1997), Ser. Mater. 37, 1337.
17. Chateau, J. P., Delafosse, D., Magnin, T. (1999), Acta Mater, to be published.
18. Chen, X., Gerberich, W. W. (1991), Metall. Trans. A 22A, 59.
19. Chêne, J., Brass, A. M. (1990), in: Corrosion sous Contrainte: Desjardins, D., Oltra, R. (Eds.). Les Ulis, France: Les Editions de Physique, p. 159.
20. Combrade, P. (1996), EPRI Report TR-104898, 3-1.
21. Combrade, P., Foucault, M. (1989), in: Proc. 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Jekyll Island, GA, NACE, pp. 8-48
22. Combrade, P., Scott, P. M. (1997), Second International Conference on Corrosion-Deformation Interaction, CDI'96. EFC publication No 21, London: The Institute of Metals, p. 394.
23. Combrade, P., Foucault, M., Slama, G. (1985), in: Proc. of the 2nd IAEA Specialist's Meeting on Sub-critical Crack Growth, Sendaï: Cullen, W. H. (Ed.). NUREG/CP-0067, Vol. 2, p. 201.
24. Congleton, J., Shoji, T., Parkins, R. N. (1985), Corr. Sci. 25, 633.
25. Cottrell, A. H., Jawson, M. A. (1949), Proc. Roy. Soc. A199, 104.
26. Cragnolino, G., Lin, L. F., Szklarska-Smialowska, Z. (1981), Corrosion 37, 312.
27. Dabosi, E, Béranger, G., Baroux, B. (1994), in: Corrosion Localisée, Les Ulis, France: Les Editions de Physique.
28. Delafosse, D., Chateau, J. P., Chambreuil, A., Magnin, T. (1997), Mater. Sci. Eng. A234-236, 889.
29. Desestret, A., Oltra, R. (1980), Corr. Sci. 20, 799.
30. Edeleanu, C., Forty, A. J. (1960), Phil. Mag. A 59, 713.
31. Flanagan, W. F., Bastias, P., Lichter, B. D. (1991), Acta Metall. Mater. 39 (4), 695.
32. Ford, F. P. (1982a), in: Corrosion Processes: Parkins, R. N. (Ed.). London: Applied Science, p. 271.
33. Ford, F. P. (1982b), EPRI Report NP-2589, Palo Alto.
34. Ford, F. P. (1990), in: Corrosion sous Contrainte: Desjardins, D., Oltra, R. (Eds.). Les Ulis, France: Les Editions de Physique, p. 307.
35. Ford, F. P., Taylor, D. F., Andresen, P. L., Ballinger, R. G. (1987), EPRI Report NP-5064S, Palo Alto.
36. Frégonese, M. (1997), Ph.D. Thesis, Ecole des Mines de Saint Etienne.
37. Gangloff, R. M., Duquette, D. J. (1987), in: Chemistry and Physics of Fracture: Latanision, et al. (Ed.). Martinus, p. 612.
38. Gerberich, W. W., Marsh, P. G., Huang, H. (1991), Parkins Symp. on Fundamental Aspects of Stress Corrosion Cracking: Bruemmer, S. M. (Ed.) Warrendale, PA: Miner. Met. Mater. Soc., p. 191.
39. Gerberich, W. W., Marsh, P., Hoehn, J., Venkatara-man, S., Huang, H. (1993), in: Corrosion-Deformation Interactions, CDI'92: Magnin, T., Gras, J. M. (Eds.). Les Ulis, France; Les Editions de Physique, p. 325.
40. Gerland, M., Mendez, J., Violan, P., Ait Saadi, A. (1988), Mater. Sci. Eng. A118, 83.
41. Hehemann R. F. (1985), Metall. Trans. A 16A, 1909.
42. Hirth, J. P., Lothe, J. (1992), Theory of Dislocations, 2nd ed. New York: Wiley.
43. Kelly, R. G., Young, A. J., Newman, R. C. (1993), ASTM STP-1188, 94.
44. Lacombe, P., Parkins, R. N. (1977), Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys. Houston: NACE 5, p. 521.
45. Lardon, J. M. (1986), Houston: Ph.D. Thesis, Saint-Etienne.
46. Lichter, B. D., Bhatkal, R. M., Flanagan, W. F. (1992), Parkins Symp. on Fundamental Aspects Stress Corrosion Cracking, 1991: Bruemmer, S. M. (Ed.). Warrendale, PA: Miner. Met. Mater. Soc., p. 279.
47. Lidbury, D. P. G. (1984), in: Embrittlement by the Localized Crack Environments: Gangloff, R. P. (Ed.). AIME, p. 149.
48. Lin, J. H., Thomson, R. (1986), Acta, Mater. 34, 187.
49. Lynch, S. P. (1981), Acta. Metall. 29, 325.
50. Lynch, S. P. (1982), Corr. Sci. 22, 925.
51. Lynch, S. P. (1984), Corr. Sci. 24 375.
52. Lynch, S. P. (1984b), Acta. Metall. 32, 79.
53. Lynch, S. P. (1988), Acta. Metall. 36, 2639.
54. Lynch, S. P. (1989), Metallography 23, 147.
55. Magnin, T. (1993), Fatigue 93: Bailon, J. B., Dickson, D. J. (Eds.). EMAS, p. 733.
56. Magnin, T. (1996), in: Advances in Corrosion-Deformation Intractions, Material Science Forum, Vol. 202: Trans. Tech. Publ., p. 89.
57. Magnin, T., Coudreuse, L. (1987), Acta Metall. 35, 2105.
58. Magnin, T., Rieux, P. (1987), Metall. 21, 907.
59. Magnin, T., Driver, T., Lepinoux, J., Kubin, L. P. (1984a), Rev. Phys. Appl. 19, 467.
60. Magnin, T., Coudreuse, L., Fourdeux, A. (1984b), Mater. Sci. Eng. L5, 63.
61. Magnin, T., Lardon, J. M., Coudreuse, L. (1985), ASTM-STP 645, 39.
62. Magnin, T., Chieragatti, R., Oltra, R. (1990), Acta. Metall. 38, 1313.
63. Magnin, T., Chambreuil, A. Bayle, B. (1996), Acta Metall. 44(4), 1457.
64. Magnin, T., Chambreuil-Paret, A., Chateau, J. P., Delafosse, D., Bayle, B. (1997), in: Second International Conference on Corrosion-Deformation Interaction, CDI'96: EFC publication No 21, London: The Institute of Metals, p. 12.
65. McEvily, A. J., Wei, R. P. (1972), Corrosion Fatigue. Houston: NACE 2, p. 381.
66. Meletis, E. I., Lian, K., Huang, W. (1993), in: Corrosion-Deformation Interactions, CDI'92, Magnin, T., Gras, J. M. (Eds.). Les Ulis, France: Les Editions de Physique, p. 69.
67. Mendez, J., Villechaise, P., Violan, P., Delafond, F. (1993), in: Corrosion-Deformation Interactions, CDI'92: Magnin, T., Gras, J. M. (Eds.). Les Ulis, France: Les Editions de Physique, p. 741.
68. Mughrabi, H. (1983), in: Proc. 4th Risø Int. Symp. on Metallurgy and Materials Science, September 5-9, 1983: Bilde Sorensen, J., Leffers, T., Hansen, N., Horsewell, A., Liholt, H. (Eds.). Risø, National Laboratory, Risø, p. 65.
69. Newman, R. C., Mehta, A. (1988), Corr. Sci. 28, 1183.
70. Newman, R. C., Shahrabi, T., Sieradzki, K. (1989), Sc. Metall. 23, 71.
71. Oppenheim, I. C., Trevor, D. J., Chidsey, C. E. D., Trevor P. L., Sieradzki, K. (1991), Science 254, 687.
72. Oriani, R. A., Josephic, P. H. (1974), Acta Metall. 22, 1065.
73. Parkins, R. N. (1990), in: Environment-Induced Cracking of Metals, NACE 10: Gangloff, R. P., Ives, M. B. (Eds.). Houston: NACE, p. 1.
74. Pessall, N. (1980), Corr. Sci. 20, 225.
75. Pugh, E. N. (1985), Corrosion 41, 517.
76. Revie, R. H., Uhlig, H. H. (1974), Acta Metall. 22, 619.
77. Roberts, S. G., Hirsh, P. B., Booth, A. S., Ellis, M., Serbena, F. C. (1993), Phys. Sc. T49, 420.
78. Saito, M., Smith, G. S., Newman, R. C. (1993), Corr. Sei 35 (1-4), p. 411.
79. Sieradzki, K., Newman, R. C. (1985), Phil. Mag. A51, 95.
80. Sieradzki, K., Kim, J. S., Cole, A. T., Newman, R. C. (1987), 7. Electrochem. Soc. 134, 1635.
81. Sieradzki, K., Corderman, R. R., Shukla, K., Newman, R. C. (1989), Phil. Mag. A 59, 713.
82. Silcock, J. M., Swann, P. R. (1979), in: Environment-Sensitive Fracture of Engineering Materials: Fou-roulis, Z. A. (Ed.). The Metallurgical Society of AIME, p. 133.
83. Sofronis, P., Birnbaum, H. K. (1995), J. Mech. Phys. Solids. 1, 49.
84. Staehle, R. W. (1987), Theory of SCC in Alloys. NATO, p. 223.
85. Stroh, A. N. (1954), Proc. Roy. Soc. 223, 404.
86. Troiano, A. R. (1962), Trans. Am. Soc. Met. 52, 54.
87. Turnbull, A., Ferris, D. H. (1987), Corr. Sci. 27(12), 1323.
88. Vaillant, F., Amzallag, C., Champredonde, J. (1997), in: Proc. 8th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems, Water Reactors, ANS, Vol. 1, p. 357.
89. Van der Sluys, W. A. (1988), in: Proc. 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Traverse City, MI: TMS, p. 277.
90. Van der Vekken, C. J. (1990), in: Environment-Induced Cracking of Metals, NACE 10: Gangloff, R. P., Ives, M. B. (Eds.). Houston: NACE, p. 197.
91. Van Leeuwen, H. P. (1974), Eng. Fract. Mech 6, 141.
92. Vehoff, H.,Neuman, P. (1983),Acto. Metall. 31, 1781.
93. Vosikoski, O. (1975), Trans. ASME 97(4), 298.
94. Wang, R., Mughrabi, H., MacGovern, S., Rappu, M. (1984), Mater. Sci. Eng. 65, 219.
95. Yan, B., Farrington, G., Laird, C. (1985), Acta Metall. 33, 1533.
96. Young, L. M., Andresen, P. L. (1995), in: Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors: NACE, Vol. 2, p. 1193.