Effect of Catalysts and Sodium Hydroxide on Glyoxal-treated Wood

BioResources

Volumn 9, Issue 3, 2014, Pages 4540-4551

  Yan, Yutao ^a   Dong, Youming ^a   Chen, Hui ^a   Zhang, Shifeng ^a   Li, Jianzhang ^a  

^a BEIJING FORESTRY UNIVERSITY   (China)

Author keywords

Ammonium persulfate; Cross linking reaction; Glyoxal; Wood modification

Indexed keywords

ALUMINUM CHLORIDE; ALUMINUM SULFATE; AMMONIUM PERSULFATE; CATALYSTS; CHLORINE COMPOUNDS; EFFICIENCY; MALEIC ANHYDRIDE; SODIUM HYDROXIDE; SULFUR COMPOUNDS; WOOD; ZINC COMPOUNDS;

AMMONIUM DIHYDROGEN PHOSPHATE; ANTI-SWELLING EFFICIENCIES; CATALYST CONCENTRATION; EFFECT OF CATALYST; FORMALDEHYDE CROSS-LINKING; MAGNESIUM CHLORIDES; MODIFICATION EFFICIENCY; OPTIMAL COMBINATION;

MAGNESIUM COMPOUNDS;

ALUMINUM CHLORIDE; ALUMINUM SULFATE; AMMONIUM PERSULFATE; CATALYSTS; CHLORINE COMPOUNDS; EFFICIENCY;

EID: 84925466362     PISSN: None     EISSN: 19302126     Source Type: Journal    
DOI: 10.15376/biores.9.3.4540-4551     Document Type: Article

References (39)

1. Ballerini, A., Despres, A., and Pizzi, A. (2005). “Non-toxic, zero emission tannin-glyoxal adhesives for wood panels,” Holz als Roh- und Werkstoff 63(6), 477–478.
2. Bokias, G., Durand, A., and Hourdet, D. (1998). “Molar mass control of poly (N - isopropylacrylamide) and poly (acrylic acid) in aqueous polymerizations initiated by redox initiators based on persulfates,” Macromolecular Chemistry and Physics 199(7), 1387–1392.
3. Choi, H.-M., and Kim, Y. M. (2001). “Performance improvement of nonformaldehyde wrinkle resistant finished cotton fabrics treated with dialdehydes,” Fibers and Polymers 2(4), 190–195.
4. Choi, H.-M., Park, M., and Oh, K. W. (1998). “Non-formaldehyde crease-resistant finishing of silk with glyoxal,” Textile Chemist and Colorist 30(12).
5. Dieste, A., Krause, A., Bollmus, S., and Militz, H. (2008). “Physical and mechanical properties of plywood produced with 1.3-dimethylol-4.5-dihydroxyethyleneurea (DMDHEU)-modified veneers of Betula sp. and Fagus sylvatica,” Holz als Roh und Werkstoff 66(4), 281–287.
6. Ebdon, J., Huckerby, T., and Hunter, T. (1994). “Free-radical aqueous slurry polymerizations of acrylonitrile: 1. End-groups and other minor structures in polyacrylonitriles initiated by ammonium persulfate/sodium metabisulfite,” Polymer, 35(2), 250–256.
7. Frick, J., and Harper, R. J. (1982). “Crosslinking cotton cellulose with aldehydes,” Journal of Applied Polymer Science 27(3), 983–988.
8. Furuzono, T., Ishihara, K., Nakabayashi, N., and Tamada, Y. (1999). “Chemical modification of silk fibroin with 2 - methacryloyloxyethyl phosphorylcholine. I. Graft-polymerization onto fabric using ammonium persulfate and interaction between fabric and platelets,” Journal of Applied Polymer Science 73(12), 2541–2544.
9. Kumar, S. (1994). “Chemical modification of wood,” Wood and Fiber Science 26(2), 270–280.
10. Lee, E. S., and Kim, S. I. (2004). “Effect of glycols and catalysts on cotton fabrics treated with glyoxal,” Fibers and Polymers 5(3), 230–233.
11. Lee, E. S., and Kim, S. I. (2005). “Effect of additives on durable-press cotton fabrics treated with a glyoxal/glycol mixture,” Journal of Applied Polymer Science 96(4), 975–978.
12. Lei, H., Pizzi, A., and Du, G. (2008). “Environmentally friendly mixed tannin/lignin wood resins,” Journal of Applied Polymer Science 107(1), 203–209.
13. Li, J.-Z., Furuno, T., Zhou, W.-R., Ren, Q., Han, X.-Z., and Zhao, J.-P. (2009). “Properties of acetylated wood prepared at low temperature in the presence of catalysts,” Journal of Wood Chemistry and Technology 29(3), 241–250.
14. Liggio, J., Li, S.-M., and McLaren, R. (2005). “Heterogeneous reactions of glyoxal on particulate matter: Identification of acetals and sulfate esters,” Environmental Science & Technology 39(6), 1532–1541.
15. Mansouri, N.-e., Pizzi, A., and Salvadó, J. (2006). “Lignin-based wood panel adhesives without formaldehyde,” Holz als Roh- und Werkstoff 65(1), 65–70.
16. Masere, J., Chekanov, Y., Warren, J. R., Stewart, F. D., Al-Kaysi, R., Rasmussen, J. K., and Pojman, J. A. (2000). “Gas-free initiators for high-temperature free-radical polymerization,” Journal of Polymer Science Part A: Polymer Chemistry 38(21), 3984–3990.
17. Meyer, U., Müller, K., and Zollinger, H. (1976). “The mechanism of catalysis in the crosslinking of cotton with formaldehyde. 2,” Textile Research Journal 46(10), 756–762.
18. Minato, K., and Yano, H. (1990). “Improvement of dimensional stability and acoustic properties of wood for musical instruments by sulfur dioxide catalysed formalization,” Mokuzai Gakkaishi - Journal of the Japan Wood Research Society 36(5), 362–367.
19. Moubarik, A., Allal, A., Pizzi, A., Charrier, F., and Charrier, B. (2009). “Characterization of a formaldehyde-free cornstarch-tannin wood adhesive for interior plywood,” European Journal of Wood and Wood Products 68(4), 427–433.
20. Nakano, T. (1993). “Reaction of glyoxal and glyoxal/glycol with wood,” Wood Science and Technology 28(1), 23–33.
21. Navarrete, P., Pizzi, A., Rode, K., Vignali, M., and Pasch, H. (2013). “MALDI-TOF study of oligomers distribution in spray-dried glyoxalated lignin for wood adhesives,” Journal of Adhesion Science and Technology 27(5–6), 586–597.
22. Navarrete, P., Pizzi, A., Tapin-Lingua, S., Benjelloun-Mlayah, B., Pasch, H., Rode, K., Delmotte, L., and Rigolet, S. (2012). “Low formaldehyde emitting biobased wood adhesives manufactured from mixtures of tannin and glyoxylated lignin,” Journal of Adhesion Science and Technology 26(10–11), 1667–1684.
23. Nozière, B., Dziedzic, P., and Córdova, A. (2010). “Inorganic ammonium salts and carbonate salts are efficient catalysts for aldol condensation in atmospheric aerosols,” Physical Chemistry Chemical Physics 12(15), 3864–3872.
24. Noziere, B., and Cordova, A. (2008). “A kinetic and mechanistic study of the amino acid catalyzed aldol condensation of acetaldehyde in aqueous and salt solutions,” The Journal of Physical Chemistry A 112(13), 2827–2837.
25. +),” The Journal of Physical Chemistry A 113(1), 231–237.
26. Rowell, R. M. (2005). “14. Chemical modification of wood,” in: Handbook of Wood Chemistry and Wood Composites 381.
27. Weaver, J., Nielson, J., and Goldstein, I. (1960). “Dimensional stabilization of wood with aldehydes and related compounds,” Forest Products Journal 10(6), 306–10.
28. Welch, C. (1984). “Glyoxal-glycol mild cure process. Formaldehyde-free durable press fnishing of cotton,” Textile Chem. Color 16(12), 265–270.
29. Welch, C. M. (1983). “Glyoxal as a formaldehyde-free durable press reagent for mild curing applications,” Textile Research Journal 53(3), 181–186.
30. Welch, C. M., and Danna, G. F. (1982). “Glyoxal as a non-nitrogenous formaldehydefree durable-press reagent for cotton,” Textile Research Journal 52(2), 149–157.
31. Xiao, Z., Xie, Y., Adamopoulos, S., and Mai, C. (2012). “Effects of chemical modification with glutaraldehyde on the weathering performance of Scots pine sapwood,” Wood Science and Technology 46(4), 749–767.
32. Xiao, Z., Xie, Y., Militz, H., and Mai, C. (2010). “Effect of glutaraldehyde on water related properties of solid wood,” Holzforschung 64(4), 483–488.
33. Xie, Y., Krause, A., Militz, H., and Mai, C. (2008). “Weathering of uncoated and coated wood treated with methylated 1, 3-dimethylol-4, 5-dihydroxyethyleneurea (mDMDHEU),” Holz als Roh und Werkstoff 66(6), 455–464.
34. Xu, G. G., Yang, C. Q., and Deng, Y. (2002). “Applications of bifunctional aldehydes to improve paper wet strength,” Journal of Applied Polymer Science 83(12), 2539–2547.
35. Yang, X. F., and Chen, S. L. (2000). “Glyoxal—a non formaldehyde durable press finishing agent,” Dyeing and Finishing 9, 41–43.
36. Yasuda, R., Minato, K., and Norimoto, M. (1994). “Chemical modification of wood by non-formaldehyde cross-linking reagents,” Wood Science and Technology 28(3), 209–218.
37. nd Annual Meeting of Japan Wood Research Society, p. 292.
38. Yuan, Z., and Hu, H. (2012). “Preparation and characterization of crosslinked glyoxalated polyacrylamide paper-strengthening agent,” Journal of Applied Polymer Science 126(S1), E459–E469.
39. Yusuf, S. (1996). “Properties enhancement of wood by cross-lingking formation and its application to the reconstituted wood products,” Wood research: Bulletin of the Wood Research Institute Kyoto University, 83, 140–210.