A template-free method for preparation of cobalt nanoparticles embedded in N-doped carbon nanofibers with a hierarchical pore structure for oxygen reduction

Chemistry - A European Journal

Volumn 21, Issue 5, 2015, Pages 2165-2172

  Wang, Shuguang ^a   Cui, Zhentao ^a   Cao, Minhua ^a  

^a BEIJING INSTITUTE OF TECHNOLOGY   (China)

Author keywords

Carbon nanofibers; Cobalt; Electrospinning; Hierarchical pore structure; Oxygen reduction reaction

Indexed keywords

CARBON; CARBON NANOFIBERS; COBALT; DOPING (ADDITIVES); ELECTROCATALYSTS; ELECTROLYTIC REDUCTION; ELECTROSPINNING; NANOFIBERS; NANOPARTICLES; OXYGEN; PORE STRUCTURE; POROUS MATERIALS; SPINNING (FIBERS);

ELECTRICAL CONDUCTIVITY; ELECTROCATALYTIC PERFORMANCE; ELECTROCHEMICAL PERFORMANCE; HIERARCHICAL PORE STRUCTURES; HIERARCHICALLY POROUS; MASS-TRANSPORT RESISTANCE; OXYGEN REDUCTION REACTION; TEMPLATE FREE METHOD;

REDUCTION;

EID: 84921334175     PISSN: 09476539     EISSN: 15213765     Source Type: Journal    
DOI: 10.1002/chem.201404884     Document Type: Article

References (47)

1. Z. W. Chen, D. Higgins, A. P. Yu, L. Zhang, J. J. Zhang, Energy Environ. Sci. 2011, 4, 3167-3192.
2. G. Wu, P. Zelenay, Acc. Chem. Res. 2013, 46, 1878-1889.
3. I. E. L. Stephens, A. S. Bondarenko, U. Grønbjerg, J. Rossmeisl, I. Chorkendorff, Energy Environ. Sci. 2012, 5, 6744-6762.
4. J. b. Wu, H. Yang, Acc. Chem. Res. 2013, 46, 1848-1857.
5. C. W. B. Bezerra, L. Zhang, K. Lee, H. Liu, A. L. B. Marques, E. P. Marques, H. J. Wang, J. J. Zhang, Electrochim. Acta 2008, 53, 4937-4951.
6. Y. Jiao, Y. Zheng, M. Jaroniec, S. Z. Qiao, J. Am. Chem. Soc. 2014, 136, 4394-4403.
7. R. F. Zhou, Y. Zheng, D. Hulicova-Jurcakova, S. Z. Qiao, J. Mater. Chem. A 2013, 1, 13179-13185.
8. R. Jasinski, Nature 1964, 201, 1212-1213.
9. G. Wu, K. L. More, C. M. Johnston, P. Zelenay, Science 2011, 332, 443-447.
10. J. S. Lee, G. S. Park, S. T. Kim, M. Liu, J. Cho, Angew. Chem. 2013, 125, 1060-1064.
11. M. Lefèvre, E. Proietti, F. Jaouen, J. P. Dodelet, Science 2009, 324, 71-74.
12. A. L. Bouwkamp-Wijnoltz, W. Visscher, J. A. R. van Veen, S. C. Tang, Electrochim. Acta 1999, 45, 379-386.
13. M. Lefèvre, J. P. Dodelet, J. Phys. Chem. B 2002, 106, 8705-8713.
14. D. Y. Shin, B. Y. Jeong, B. J. S. Mun, H. Jeon, H. J. Shin, J. Y. Baik, J. Y. Lee, J. Phys. Chem. C 2013, 117, 11619-11624.
15. H. W. Liang, W. Wei, Z. S. Wu, X. L. Feng, K. Müllen, J. Am. Chem. Soc. 2013, 135, 16002-16005.
16. H. L. Jiang, Y. H. Su, Y. H. Zhu, J. H. Shen, X. L. Yang, Q. Feng, C. Z. Li, J. Mater. Chem. A 2013, 1, 12074-12081.
17. J. Liang , Y.Jiao, M.Jaroniec, S. Z.Qiao, Angew. Chem. Int. Ed. 2012, 51, 11496- 11500;
18. J. Liang, Y. Jiao, M. Jaroniec, S. Z. Qiao, Angew. Chem. 2012, 124, 11664-11668.
19. G. H. An, H. J. Ahn, Carbon 2013, 65, 87-96.
20. J. K. Dombrovskis, H. Y. Jeong, K. Fossum, O. Terasaki, A. E. C. Palmqvist, Chem. Mater. 2013, 25, 856-861.
21. Y. M. Tan, C. F. Xu, G. X. Chen, X. L. Fang, N. F. Zheng, Q. J. Xie, Adv. Funct. Mater. 2012, 22, 4584-4591.
22. H. P. Cong, P. Wang, M. Gong, S. H. Yu, Nano Energy 2014, 3, 55-63.
23. C. Z. Wei, Y. Y. Liu, X. R. Li, J. H. Zhao, Z. Ren, H. Pang, ChemElectroChem 2014, 1, 799-807.
24. J. J. Duan, S. Chen, S. Dai, S. Z. Qiao, Adv. Funct. Mater. 2014, 24, 2072-2078.
25. T. Y. Ma, Y. Zheng, S. Dai, M. Jaroniec, S. Z. Qiao, J. Mater. Chem. A 2014, 2, 8676-8682.
26. J. Liang, X. Du, C. Gibson, X. W. Du, S. Z. Qiao, Adv. Mater. 2013, 25, 6226-6231.
27. Y. Xiao, C. G. Hu, L. T. Qu, C. W. Hu, M. H. Cao, Chem. Eur. J. 2013, 19, 14271-14278.
28. J. Liang , Y.Zheng, J.Chen, J.Liu, D.Hulicova-Jurcakova, M.Jaroniec, S. Z.Qiao, Angew. Chem. Int. Ed. 2012, 51, 3892 -3896;
29. J. Liang, Y. Zheng, J. Chen, J. Liu, D. Hulicova-Jurcakova, M. Jaroniec, S. Z. Qiao, Angew. Chem. 2012, 124, 3958-3962.
30. L. F. Wu, H. B. Feng, M. J. Liu, K. X. Zhang, J. H. Li, Nanoscale 2013, 5, 10839-10843.
31. J. Tang, T. Wang, X. C. Pan, X. Sun, X. L. Fan, Y. X. Guo, H. R. Xue, J. P. He, J. Phys. Chem. C 2013, 117, 16896-16906.
32. S. Maldonado, K. J. Stevenson, J. Phys. Chem. B 2005, 109, 4707-4716.
33. J. J. Duan, Y. Zheng, S. Chen, Y. H. Tang, M. Jaroniec, S. Z. Qiao, Chem. Commun. 2013, 49, 7705-7707.
34. S. M. Unni, S. Devulapally, N. Karjule, S. Kurungot, J. Mater. Chem. 2012, 22, 23506-23513.
35. R. L. Liu, D. Q. Wu, X. L. Feng, K. Mllen, Angew. Chem. 2010, 122, 2619-2623.
36. Z. X. Yan, M. Cai, P. K. Shen, J. Mater. Chem. 2012, 22, 2133-2139.
37. J. Wu, H. W. Park, A. P. Yu, D. Higgins, Z. W. Chen, J. Phys. Chem. C 2012, 116, 9427-9432.
38. T. F. Hung, S. G. Mohamed, C. C. Shen, Y. Q. Tsai, W. S. Chang, R. S. Liu, Nanoscale 2013, 5, 12115-12119.
39. M. Y. Wang, J. R. Huang, M. Wang, D. G. Zhang, W. M. Zhang, W. H. Li, J. Chen, Electrochem. Commun. 2013, 34, 299-303.
40. G. Wu, C. M. Johnston, N. H. Mack, K. Artyushkova, M. Ferrandon, M. Nelson, J. S. Lezama-Pacheco, S. D. Conradson, K. L. More, D. J. Myers, P. Zelenay, J. Mater. Chem. 2011, 21, 11392-11405.
41. H. Xiao, Z. G. Shao, G. Zhang, Y. Gao, W. T. Lu, B. L. Yi, Carbon 2013, 57, 443-451.
42. I. Y. Jeon, S. Zhang, L. P. Zhang, H. J. Choi, J. M. Seo, Z. H. Xia, L. M. Dai, J. B. Baek, Adv. Mater. 2013, 25, 6138-6145.
43. H. Y. Zhu, S. Zhang, Y. X. Huang, L. H. Wu, S. H. Sun, Nano Lett. 2013, 13, 2947-2951.
44. C. Z. Zhang, N. Mahmood, H. Yin, F. Liu, Y. L. Hou, Adv. Mater. 2013, 25, 4932-4937.
45. H. J. Tang, H. J. Yin, J. Y. Wang, N. L. Yang, D. Wang, Z. Y. Tang, Angew. Chem. 2013, 125, 5695-5699.
46. W. Ding , Z. D.Wei, S. G.Chen, X. Q.Qi, T.Yang, J. S.Hu, D.Wang, L. J.Wan, S. F.Alvi, L.Li, Angew. Chem. Int. Ed. 2013, 52, 11755 -11759;
47. W. Ding, Z. D. Wei, S. G. Chen, X. Q. Qi, T. Yang, J. S. Hu, D. Wang, L. J. Wan, S. F. Alvi, L. Li, Angew. Chem. 2013, 125, 11971-11975.