The enhanced tribological properties of NiAl intermetallics: Combined lubrication of multilayer graphene and WS2

Tribology Letters

Volumn 56, Issue 3, 2014, Pages 573-582

  Yao, Jie ^a   Shi, Xiaoliang ^a   Zhai, Wenzheng ^a   Ibrahim, Ahmed Mohamed Mahmoud ^a   Xu, Zengshi ^a   Chen, Long ^a   Zhu, Qingshuai ^a   Xiao, Yecheng ^a   Zhang, Qiaoxin ^a   Wang, Zhihai ^a  

^a WUHAN UNIVERSITY OF TECHNOLOGY   (China)

Author keywords

Self lubrication friction; Self lubricating composites; Solid lubricants; Solid lubrication mechanisms; Solid lubrication wear

Indexed keywords

BINARY ALLOYS; FRICTION; GRAPHENE; INTERMETALLICS; MULTILAYERS; SELF LUBRICATING COMPOSITES; SOLID LUBRICANTS; TUNGSTEN COMPOUNDS; WEAR OF MATERIALS;

FRICTION COEFFICIENTS; MULTILAYER GRAPHENE; NI-AL INTERMETALLICS; REINFORCEMENT PARTICLES; SELF LUBRICATION; SELF-LUBRICATING MATERIAL; SOLID LUBRICATION; TRIBOLOGICAL PROPERTIES;

TRIBOLOGY;

EID: 84918811746     PISSN: 10238883     EISSN: 15732711     Source Type: Journal    
DOI: 10.1007/s11249-014-0439-4     Document Type: Article

References (31)

1. Tyagi, R., Xiong, D.S., Li, J.L., Dai, J.H.: Elevated temperature tribological behavior of NiAl based composites containing nano-silver and hBN. Wear 269, 884-890 (2010)
2. 2 self-lubricating composite. Wear 205, 64-70 (1997)
3. Evans, D.C., Senior, G.S.: Self-lubricating materials for plain bearings. Tribol. Int. 15, 243-248 (1982)
4. 2 at high temperature. Wear 251, 1094-1099 (2001)
5. 4. Tribol. Lett. 43, 55-63 (2011)
6. 2. Wear 274-275, 188-195 (2012)
7. Shi, X.L., Xu, Z.S., Wang, M., Zhai, W.Z., Yao, J., Song, S.Y., Abid, Q.D., Zhang, Q.X.: Tribological behavior of TiAl matrix self-lubricating composites containing silver from 25 to 800°C. Wear 303, 486-494 (2013)
8. Darolia, R.: NiAl alloys for high-temperature structural applications. JOM 43, 44-49 (1991)
9. 2 compound NiAl. Int. Mater. Rev. 38, 193-232 (1993)
10. Johnson, B.J., Kennedy, F.E., Baker, I.: Dry sliding wear of NiAl. Wear 192, 241-247 (1996)
11. Ozdemir, O., Zeytin, S., Bindal, C.: Tribological properties of NiAl produced by pressure-assisted combustion synthesis. Wear 265, 979-985 (2008)
12. Zhu, S.Y., Bi, Q.L., Niu, M.Y., Yang, J., Liu, W.M.: Tribological behavior of NiAl matrix composites with addition of oxides at high temperatures. Wear 274-275, 423-434 (2012)
13. 2 phase. Wear 259, 626-633 (2005)
14. 3SiC2 on tribological properties of NiAl matrix self-lubricating composites over a wide temperature range. Mater. Des. 55, 93-103 (2014)
15. Lee, C., Wei, X.D., Kysar, J.W., Hone, J.: Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 321, 385-388 (2008)
16. Lin, L.Y., Kin, D.E., Kim, W.K., Jun, S.C.: Friction and wear characteristics of multi-layer graphene film investigated by atomic force microscopy. Surf. Coat. Technol. 205, 4864-4869 (2011)
17. 4 composites. Scr. Mater. 66, 7793-7796 (2012)
18. Xu, Z.S., Shi, X.L., Zhai, W.Z., Yao, J., Song, S.Y., Zhang, Q.X.: Preparation and tribological properties of TiAl matrix composites reinforced by multilayer graphene. Carbon 67, 168-177 (2014)
19. 2 additions when sliding against hardened steel. Int. J. Refract Met. Hard Mater. 25, 189-197 (2007)
20. Kandanur, S.S., Rfiee, M.A., Yavari, F., Schrameyer, M., Yu, Z.Z., Blanchet, T.A., Koratkar, N.: Suppression of wear in graphene polymer composites. Carbon 50, 3178-3183 (2012)
21. 2 nanoparticles with ultra-low friction and wear. Nature 407, 164-167 (2000)
22. 2 high temperature self-lubricating wear-resistant composite coating. Appl. Surf. Sci. 258, 3757-3762 (2012)
23. 3Al matrix composites with 1.5 wt% graphene nanoplatelets. Tribol. Lett. 55, 343-352 (2014)
24. 2, Ag and hBN tested from room temperature to 800°C. Mater. Des. 55, 75-84 (2014)
25. American Society for Testing and Materials, Standard test method for Knoop and Vickers hardness of metallic materials, ASTM E384-11e1 (2012)
26. American Society for Testing and Materials. Standard test methods for density of compacted or sintered powder metallurgy (PM) products using Archimedes' principle, ASTM B962-13 (2013)
27. American Society for Testing and Materials, Standard test method for wear testing with a pin-on-disk apparatus, ASTM G99-05 (2005)
28. 4 and WC/Co. Wear 261, 693-701 (2006)
29. Pauschitz, A., Roy, M., Franek, F.: Mechanisms of sliding wear of metals and alloys at elevated temperatures. Tribol. Int. 41, 584-602 (2008)
30. Kolubaev, A., Tarasov, S., Sizova, O., Kolubaev, E.: Scale-dependent subsurface deformation of metallic materials in sliding. Tribol. Int. 43, 695-699 (2010)
31. Berman, D., Erdemir, A., Sumant, A.V.: Few layer graphene to reduce wear and friction on sliding steel surfaces. Carbon 54, 454-459 (2013)