Fractographic study of fatigue cracks in a steel car wheel

Engineering Failure Analysis

Volumn 47, Issue PA, 2015, Pages 199-207

  Zheng, Zhanguang ^a,b   Yuan, Shuai ^a,b   Sun, Teng ^a,b   Pan, Shuqin ^a  

^a GUANGXI UNIVERSITY   (China)

^b Guangxi Key Laboratory of Manufacturing System and Advanced Manufacturing Technology   (China)

Author keywords

Fatigue failure; Fractographic; Steel wheel; Transgranular crack

Indexed keywords

CRACK DETECTION; FAILURE (MECHANICAL); FATIGUE CRACK PROPAGATION; FATIGUE DAMAGE; FATIGUE OF MATERIALS; FATIGUE TESTING; SCANNING ELECTRON MICROSCOPY; STRESS CORROSION CRACKING; TEXTURES; WHEELS;

FATIGUE FAILURES; FATIGUE STRIATIONS; FRACTOGRAPHIC; FRACTOGRAPHIC ANALYSIS; FRETTING FATIGUE DAMAGE; STEEL WHEELS; THICKNESS VARIATION; TRANSGRANULAR CRACK;

CRACKS;

EID: 84911192200     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2014.09.010     Document Type: Article

References (9)

1. Kocabicak U., Firat M. Numerical analysis of wheel cornering fatigue tests. Eng Fail Anal 2001, 8:339-354.
2. Wang X., Zhang X. Simulation of dynamic cornering fatigue test of a steel passenger car wheel. Int J Fatigue 2010, 32:434-442.
3. Zheng Z.G., Sun T., Xu X.Y., Pan S.Q., Yuan S. Numerical simulation of steel wheel dynamic cornering fatigue test. Eng Fail Anal 2014, 39:124-134.
4. Carboni M., Beretta S., Fini A. Defects and in-service fatigue life of truck wheels. Eng Fail Anal 2003, 10:45-57.
5. Bhattacharyya S., Adhikary M., Das M.B., Sarkar S. Failure analysis of cracking in wheel rims - material and manufacturing aspects. Eng Fail Anal 2007, 15:547-554.
6. Wu J.H., Guo T.X., Liu H. Mini car wheel disc crack reason. Automobile Technol. Mater. 2005, 7:28-29. (in Chinese).
7. Zhang Shijiang, Shao Yunkai. Performance requirements and test methods of passenger car wheels. Beijing CSAE GB/T 5334-2005; 2005. p. 1-5 (in Chinese).
8. Lee J.M., Choi B.H. Experimental observation and modeling of the retardation of fatigue crack propagation under the combination of mixed-mode single overload and constant amplitude loads. Int J Fatigue 2009, 31:1848-1857.
9. Yanishevsky M., Li G., Shi G.q., Backman D. Fractographic examination of coupons representing aircraft structural joints with and without hole cold expansion. Eng Fail Anal 2013, 30:74-90.