Stress corrosion cracking of zirconium and zircaloy-4 in iodine containing solutions

NACE - International Corrosion Conference Series

Volumn 2002-April, Issue , 2002, Pages

  Farina, S B ^a   Duffo, G S ^a   Galvele, J R ^a  

^a DEPARTAMENTO DE FÍSICA   (Argentina)

Author keywords

Intergranular attack; Iodine; Stress corrosion cracking; Zircaloy 4; Zirconium

Indexed keywords

CORROSION RATE; CRACK PROPAGATION; CRACKS; INTERGRANULAR CORROSION; IODINE; MOLECULES; RESIDUAL STRESSES; SINGLE CRYSTALS; SOLVENTS; ZIRCONIUM; ZIRCONIUM ALLOYS;

1-PENTANOL; CORROSIVE SPECIES; CRACK PROPAGATION RATE; SOLVENT MOLECULAR; SOLVENT MOLECULES; STERIC EFFECT; SURFACE MOBILITY; ZIRCALOY-4;

STRESS CORROSION CRACKING;

EID: 84907835001     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (15)

1. B. Cox, R. Haddad, J. Nucl. Mater. 137 (1986) 115.
2. G. A. Cragnolino, "Corrosion bajo tensiones del circonio y de sus aleaciones en presencia de cloruros", PhD Thesis. Universidad de Buenos Aires, Argentina (1975).
3. S. B. Farina, "Corrosion bajo tension de circonio y aleaciones en soluciones de halogenuros". Ms. Sci. Thesis. Universidad Nacional de General San Martin, Argentina (2001).
4. B. Cox, J. Nucl. Mat. 170, (1990): p. 1.
5. I. Schuster, C. Lemaignan, J. Nucl. Mat. 166, (1989): p. 348.
6. B. Cox, Corrosion 33, 3, (1977): p. 79.
7. K. Elayaperumal, P. K. De, J. Balachandra, J. Nucl. Mater 45, (1972/73): p. 323.
8. B. Cox, Corrosion 1, 4, (1975): p. 367.
9. K. Mori, A. Takamura, T. Shimose, Corrosion 22, 2, (1966): p. 29.
10. J. R. Galvele, S. M. de De Micheli, I. L. Muller, S. B. de Wexler, I. L. Alanis, Localized Corrosion (eds R. W. Staehle, B. F. Brown, J. Kruger and A. Agrawal), (Houston, TX: NACE, 1974), p. 590.
11. L. J. Andrews, R. M. Keefer, Adv. Inorg. Chem. Radiochem. 3, (1961): p. 91.
12. J. R. Galvele, Corros. Sci. 27, 1, (1987): p. 1.
13. J. R. Galvele, Electrochim. Acta 45, (2000): p. 3537.
14. th Edition, (Cleveland, OH: CRC Press, The Chemical Rubber Co., 1998/99), p. 4.98.
15. rd Ed. (Ithaca, NY: Cornell University Press, 1960), p. 410.