Nanoflakes-assembled three-dimensional hollow-porous V2O 5 as lithium storage cathodes with high-rate capacity

Small

Volumn 10, Issue 15, 2014, Pages 3032-3037

  Mai, Liqiang ^a   An, Qinyou ^a   Wei, Qiulong ^a   Fei, Jiayang ^c   Zhang, Pengfei ^a   Xu, Xu ^a   Zhao, Yunlong ^a   Yan, Mengyu ^a   Wen, Wen ^a   Xu, Lin ^a,b  

^a WUHAN UNIVERSITY OF TECHNOLOGY   (China)

^b HARVARD UNIVERSITY   (United States)

^c UNIVERSITY OF PENNSYLVANIA   (United States)

Author keywords

high rate capacity; lithium batteries; nanoflakes; nanostructures; porous structures

Indexed keywords

LITHIUM BATTERIES; NANOSTRUCTURES; VANADIUM COMPOUNDS;

CATH-ODE MATERIALS; HIGH-RATE CAPACITIES; LITHIUM STORAGES; NANO-FLAKES; POROUS STRUCTURES; RATE CAPABILITIES; SOLVOTHERMAL METHOD; VANADIUM PENTOXIDE;

CATHODES;

EID: 84905591817     PISSN: 16136810     EISSN: 16136829     Source Type: Journal    
DOI: 10.1002/smll.201302991     Document Type: Article

References (47)

1. M. Armand, J. M. Tarascon, Nature 2008, 451, 652.
2. J. B. Goodenough, Y. Kim, Chem. Mater. 2009, 22, 587.
3. B. Kang, G. Ceder, Nature 2009, 458, 190.
4. M. S. Whittingham, Chem. Rev. 2004, 104, 4271.
5. J. M. Tarascon, M. Armand, Nature 2001, 414, 359.
6. H. Wu, G. Chan, J. W. Choi, I. Ryu, Y. Yao, M. T. McDowell, S. W. Lee, A. Jackson, Y. Yang, L. B. Hu, Y. Cui, Nat. Nanotechnol. 2012, 7, 310.
7. S. Q. Wang, S. R. Li, Y. Sun, X. Y. Feng, C. H. Chen, Energy Environ. Sci. 2011, 4, 2854.
8. Q. T. Qu, Y. S. Zhu, X. W. Gao, Y. P. Wu, Adv. Energy Mater. 2012, 2, 950.
9. S. Zhou, X. G. Yang, Y. J. Lin, J. Xie, D. W. Wang, ACS Nano 2012, 6, 919.
10. Y. Wang, G. Z. Cao, Adv. Mater. 2008, 20, 2251.
11. T. Y. Zhai, H. M. Liu, H. Q. Li, X. S. Fang, M. Y. Liao, L. Li, H. S. Zhou, Y. Koide, Y. Bando, D. Golberg, Adv. Mater. 2010, 22, 2547.
12. C. Ban, N. A. Chernova, M. S. Whittingham, Electrochem. Commun. 2009, 11, 522.
13. J. Muster, G. T. Kim, V. Krstic, J. G. Park, Y. W. Park, S. Roth, M. Burghard, Adv. Mater. 2000, 12, 420.
14. T. Watanabe, Y. Ikeda, T. Ono, M. Hibino, M. Hosoda, K. Sakai, T. Kudo, Solid State Ionics 2002, 151, 313.
15. X. Y. Chen, E. Pomerantseva, P. Banerjee, K. Gregorczyk, R. Ghodssi, G. Rubloff, Chem. Mater. 2012, 24, 1255.
16. A. Q. Pan, H. B. Wu, L. Yu, T. Zhu, X. W. Lou, ACS Appl. Mater. Interfaces 2012, 4, 3874.
17. Y. L. Cheah, V. Aravindan, S. Madhavi, ACS Appl. Mater. Interfaces 2013, 5, 3475.
18. S. H. Ng, T. J. Patey, R. Buechel, F. Krumeich, J. Z. Wang, H. K. Liu, S. E. Pratsinis, Phys. Chem. Chem. Phys. 2009, 11, 3748.
19. K. Takahashi, S. J. Lim, Y. Wang, G. Z. Cao, Jpn. J. Appl. Phys., Part 1 2005, 44, 662.
20. L. Q. Mai, L. Xu, C. H. Han, X. Xu, Y. Z. Luo, S. Y. Zhao, Y. L. Zhao, Nano Lett. 2010, 10, 4750.
21. L. Q. Mai, F. Dong, X. Xu, Y. Z. Luo, Q. Y. An, Y. L. Zhao, J. Pan, J. N. Yang, Nano Lett. 2013, 13, 740.
22. L. Q. Mai, X. Xu, L. Xu, C. H. Han, Y. Z. Luo, J. Mater. Res. 2011, 26, 2175.
23. H. M. Liu, W. S. Yang, Energy Environ. Sci. 2011, 4, 4000.
24. Y. Wang, K. Takahashi, H. M. Shang, G. Z. Cao, J. Phys. Chem. B 2005, 109, 3085.
25. H. Wang, K. Huang, C. Huang, S. Liu, Y. Ren, X. Huang, J. Power Sources 2011, 196, 5645.
26. X. H. Rui, Z. Y. Lu, H. Yu, D. Yang, H. H. Hng, T. M. Lim, Q. Y. Yan, Nanoscale 2013, 5, 556.
27. Z. Y. Wang, L. Zhou, X. W. Lou, Adv. Mater. 2012, 24, 1903.
28. J. S. Chen, X. W. Lou, Small 2011, 1, 1877.
29. Y. M. Wu, Z. H. Wen, H. H. Feng, J. H. Li, Small 2012, 8, 858.
30. G. L. Cui, Y. S. Hu, L. J. Zhi, D. Q. Wu, I. Lieberwirth, J. Maier, K. Müllen, Small 2007, 3, 2066.
31. D. Mao, J. X. Yao, X. Y. Lai, M. Yang, J. Du, D. Wang, Small 2011, 7, 578.
32. Y. Yao, M. T. McDowell, I. Ryu, H. Wu, N. Liu, L. Hu, W. D. Nix, Y. Cui, Nano Lett. 2011, 11, 2949.
33. D. Y. Chen, X. Mei, G. Ji, M. H. Lu, J. P. Xie, J. M Lu, J. Y. Lee, Angew. Chem. Int. Ed. 2012, 51, 2409.
34. A. Vu, Y. Q. Qian, A. Stein, Adv. Energy Mater. 2012, 3, 1056.
35. J. Zheng, B. H. Wu, Z. Y. Jiang, Q. Kuang, X. L. Fang, Z. X. Xie, R. B. Huang, L. S. Zheng, Chem. Asian J. 2010, 5, 1439.
36. X. Xu, Y. Z. Luo, L. Q. Mai, Y. L. Zhao, Q. Y. An, L. Xu, F. Hu, L. Zhang, Q. J. Zhang, NPG Asia Mater. 2012, 4, e20.
37. X. F. Zhang, K. X. Wang, X. Wei, J. S. Chen, Chem. Mater. 2011, 23, 5290.
38. C. H. Han, M. Y. Yan, L. Q. Mai, X. C. Tian, L. Xu, X. Xu, Q. Y. An, Y. L. Zhao, X. Y. Ma, J. L. Xie, Nano Energy 2013, doi: 10.1016/j.nanoen.2013.03. 012.
39. C. Q. Feng, S. Y. Wang, R. Zeng, Z. P. Guo, K. Konstantinov, H. K. Liu, J. Power Sources 2008, 184, 485.
40. S. Ng, T. J. Patey, R. Buchel, F. Krumeich, J. Wang, H. K. Liu, S. E. Pratsinis, P. Novak, Phys. Chem. Chem. Phys. 2009, 11, 3748.
41. J. J. Yu, J. Yang, W. B. Nie, Z. H. Li, E. H. Liu, G. T. Lei, Q. Z. Xiao, Electrochim. Acta 2013, 89, 292.
42. Y. Wang, K. Takahashi, H. M. Shang, G. Z. Cao, J. Phys. Chem. B 2005, 109, 3085.
43. X. L. Jia, Z. Chen, A. Suwarnasarn, L. Rice, X. L. Wang, H. Sohn, Q. Zhang, B. M. Wu, F. Wei, Y. F. Lu, Energy Environ. Sci. 2012, 5, 6845.
44. N. Jayaprakash, J. Shen, S. S. Moganty, A. Corona, L. A. Archer, Angew. Chem. Int. Ed. 2011, 50, 5904.
45. A. Q. Pan, T. Zhu, H. B. Wu, X. W. Lou, Chem. Eur J. 2013, 19, 494.
46. S. Q. Wang, Z. D. Lu, D. Wang, C. G. Li, C. H. Chen, Y. D. Yin, J. Mater. Chem. 2011, 21, 6365.
47. X. M. Sun, Y. D. Li, Angew. Chem. Int. Ed. 2004, 43, 597.