Advances in techniques for determination of susceptibility of welds to stress corrosion cracking (KISCC)

Weld Cracking in Ferrous Alloys

Volumn , Issue , 2008, Pages 521-533

  Singh, R K ^a  

^a MONASH UNIVERSITY   (Australia)

Author keywords

[No Author keywords available]

Indexed keywords

CRACKS; FRACTURE MECHANICS; FRACTURE TESTING; HEAT AFFECTED ZONE; RESIDUAL STRESSES; TENSILE TESTING; WELD DECAY; WELDED STEEL STRUCTURES; WELDING;

CIRCUMFERENTIAL NOTCH TENSILE TECHNIQUES (CNT); CONVENTIONAL TECHNIQUES; CORROSIVE ENVIRONMENT; STRESS INTENSITY; THRESHOLD STRESS INTENSITY FACTOR; WELDED COMPONENTS;

STRESS CORROSION CRACKING;

EID: 84903411039     PISSN: None     EISSN: None     Source Type: Book    
DOI: 10.1533/9781845695453.3.521     Document Type: Chapter

References (13)

1. Turnbull A. British Corrosion Journal 1992, 27:271.
2. 1982, ASTM Committee G-1, ASTM Special Technical Publication 821. S.W. Dean, E.N. Pugh, G.M. Ugiansky (Eds.).
3. Ibrahim R.N., Stark H.L. International Journal of Fracture 1990, 44:179.
4. Ibrahim R.N., Stark H.L. Engineering Fracture Mechanics 1986, 25:395.
5. Ibrahim R.N., Stark H.L. Engineering Fracture Mechanics 1987, 28:455.
6. Irwin G.R. Fracture Testing of High-strength Sheet Materials Under Conditions Appropriate for Stress Analysis 1960, July, Report 5486, Naval Research Laboratory.
7. Irwin G.R. Plastic zone near a crack and fracture toughness 1961.
8. Hertzberg R.W. Deformation and Fracture of Engineering Materials 1976, 274-277. Wiley, New York.
9. McClintock F.A., Irwin G.R. ASTM STP 1965, 381:84.
10. Bayles R.K., Singh R., Knight S., Wang J.-A., Hinton B.R.W., Muddle B.C. Environment-Induced Cracking of Materials: Predictions, Industrial Developments and Evaluation 2008, 459. Elsevier, UK. S.A. Shipilov, R.A. Jones, J.-M. Olive, R.B. Rebak (Eds.).
11. Singh R.K., Rihan R., Ibrahim R.N. Metallurgical and Materials Transactions A 2006, 37A:2963.
12. Rihan R., Singh R.K., Ibrahim R.N. Materials Science and Engineering A 2006, 425:272.
13. Singh R.K., Rihan R., Ibrahim R.N. Corrosion Science 2007, 49:4386.