An exploratory examination of the effect of sohic damage on the fracture resistance of carbon steels

NACE - International Corrosion Conference Series

Volumn 1997-March, Issue , 1997, Pages

  Cayard, M S ^a   Kane, R D ^a   Cooke, D L ^b  

^a CLI International Inc   (United States)

^b Chevron Research and Technology Co   (United States)

Author keywords

Carbon steel; Crack tip opening displacement; CTOD; Fitness for service; Fracture toughness; H2S; HIC; Hydrogen induced cracking; Hydrogen sulfide; KIc; SOHIC; Sour service; SSC; Stress oriented hydrogen induced cracking; Sulfide stress cracking

Indexed keywords

CARBON STEEL; CRACKS; FRACTURE TESTING; HEAT AFFECTED ZONE; HEAT RESISTANCE; HYDROGEN EMBRITTLEMENT; HYDROGEN SULFIDE; STEEL TESTING; SULFUR COMPOUNDS; SURFACE MORPHOLOGY;

CRACK TIP OPENING DISPLACEMENT; CTOD; FITNESS FOR SERVICE; HYDROGEN INDUCED CRACKING; SOHIC; SOUR SERVICES; SULFIDE STRESS CRACKING;

FRACTURE TOUGHNESS;

EID: 84903099920     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (8)

1. H.I. McHenry, DT. Read and TR. Shives, "Failure Analysis of an Amine-Absorber Pressure Vessel," Materials Performance, August 1987.
2. 2S Environments," Proceedings of the Second International Conference on the Interaction of Steels with Hydrogen in Petroleum Industry Pressure Vessel and Pipeline Service. The Materials Properties Council, Inc., New York, NY, Vol. 1, 1994.
3. 2S Environments," CORROSION/89, Paper No. 269, NACE International, Houston, TX, (1989).
4. M. lino, "Influence of Sulfur Content on the Hydrogen Induced Fracture in Linepipe Steels," Metallurgical Transactions, Vol. 10A, November 1979.
5. 2S Environments," CORROSION/94, Paper No. 519, NACE International, Houston, TX, (1994).
6. 2S Service," CORROSION/95, Paper No. 329, NACE International, Houston, TX, (1995).
7. 2S Environments", NACE International, Houston, TX, (1990).
8. ASTM E1290-93, "Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement," Vol. 3.01, ASTM, Philadelphia, PA, 1995.