Effect of native oxide film on commercial magnesium alloys substrates and carbonate conversion coating growth and corrosion resistance

Materials

Volumn 7, Issue 4, 2014, Pages 2534-2560

  Feliu Jr , Sebastián ^a   Samaniego, Alejandro ^a   Bermudez, Elkin Alejandro ^b   El Hadad, Amir Abdelsami ^c   Llorente, Irene ^a   Galván, Juan Carlos ^a  

^a DEPARTMENT OF PHYSICAL METALLURGY   (Spain)

^b UNIVERSIDAD SIMÓN BOLÍVAR   (Venezuela)

^c Assiut Branch   (Egypt)

Author keywords

Magnesium; Passivity; Segregation; SEM; XPS

Indexed keywords

ALUMINUM COATINGS; CHLORINE COMPOUNDS; COATINGS; CORROSION RESISTANCE; MAGNESIUM; MAGNESIUM ALLOYS; OXIDE FILMS; SCANNING ELECTRON MICROSCOPY; SEGREGATION (METALLOGRAPHY); X RAY PHOTOELECTRON SPECTROSCOPY;

AZ61 MAGNESIUM ALLOY; CARBONATE COMPOUNDS; CHLORIDE ION CONCENTRATION; CONVERSION COATINGS; NATIVE OXIDE FILM; PASSIVITY; PROTECTIVE PROPERTIES; SOLUTION TREATMENTS;

SUBSTRATES;

EID: 84899138326     PISSN: None     EISSN: 19961944     Source Type: Journal    
DOI: 10.3390/ma7042534     Document Type: Article

References (54)

1. 3-] levels on the formation of calcium phosphate conversion coatings on die-cast magnesium alloy AZ91D. Corros. Sci. 2012, 55, 343-348.
2. Chen, X.B.; Birbilis, N.; Abbott, T.B. Review of corrosion-resistant conversion coatings for magnesium and its alloys. Corrosion 2011, 67, 035005:1-035005:16.
3. Chen, X.B.; Zhou, X.; Abbott, T.B.; Easton, M.A.; Birbilis, N. Double-layered manganese phosphate conversion coating on magnesium alloy AZ91D: Insights into coating formation, growth and corrosion resistance. Surf. Coat. Technol. 2013, 217, 147-155.
4. 2- and corresponding protection against corrosion by the coating. Corros. Sci. 2009, 51, 1181-1188.
5. Yu, B.L.; Pan, X.L.; Uan, J.Y. Enhancement of corrosion resistance of Mg-9wt% Al-1 wt% Zn alloy by Calcite (CaCO3) conversion hard coating. Corros. Sci. 2010, 52, 1874-1878.
6. 2- anion-exchangeability of the film on a corrosive environment. Scr. Mater. 2007, 56, 927-930.
7. Zuleta, A.A.; Correa, E.; Villada, C.; Sepulveda, M.; Castaño, J.G.; Echevarria, F. Comparative study of different environmentally friendly (Chromium-free) methods for surface modification of pure magnesium. Surf. Coat. Technol. 2011, 205, 5254-5259.
8. Carboneras, M.; Hernandez-Alvarado, L.A.; Mireles, Y.E.; Hernandez, L.S.; Garcia-Alonso, M.C.; Escudero, M.L. Chemical conversion treatments to protect biodegradable magnesium in applications as temporary implants for bone repair. Rev. Metal. Madrid 2010, 46, 86-92.
9. Wang, J.; Li, D.; Yu, X.; Jing, X.; Zhang, M.; Jiang, Z. Hydrotalcite conversion coating on Mg alloys and its corrosion resistance. J. Alloys Compd. 2010, 494, 271-274.
10. Lin, J.K.; Jeng, K.L.; Uan, J.Y. Crystallization of a chemical conversion layer that forms on AZ91D magnesium alloy in carbonic acid. Corros. Sci. 2011, 53, 3832-3839.
11. Chen, J.; Song, Y.; Shan, D.; Han, E.H. In situ growth of Mg-Al hydrotalcite conversion film on AZ31 magnesium alloy. Corros. Sci. 2011, 53, 3281-3288.
12. Montemor, M.F.; Simões, A.M.; Carmezim, M.J. Characterization of rare-earth conversion films formed on the AZ31 magnesium alloy and its relation with corrosion protection. Appl. Surf. Sci. 2007, 253, 6922-6931.
13. Montemor, M.F.; Simões, A.M.; Ferreira, M.G.S.; Carmezim, M.J. Composition and corrosion resistance of cerium conversion films on the AZ31 magnesium alloy and its relation to the salt anion. Appl. Surf. Sci. 2008, 254, 1806-1814.
14. Lin, C.S.; Fang, S.K. Formation of Cerium conversion Coatings on AZ31 alloy. J. Electrochem. Soc. 2005, 152, B54-B59.
15. Feliu, S., Jr.; Pardo, A.; Merino, M.C.; Coy, A.E.; Viejo, F.; Arrabal, R. Correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys. Appl. Surf. Sci. 2009, 255, 4102-4108.
16. Feliu, S., Jr.; Merino, M.C.; Arrabal, R.; Coy, A.E.; Matykina, E. XPS study of the effect of aluminium on the atmospheric corrosion of the AZ31 magnesium alloys. Surf. Interface Anal. 2009, 41,143-150.
17. Feliu, S., Jr.; Maffiotte, C.; Samaniego, A.; Galvan, J.C.; Barranco, V. Effect of naturally formed oxide films and other variables in the early stages of Mg-alloy corrosion in NaCl solution. Electrochim. Acta 2011, 56, 4454-4565.
18. Feliu, S., Jr.; Maffiotte, C.; Samaniego, A.; Galván, J.C.; Barranco, V. Effect of the chemistry and structure of the native oxide surface film on the corrosion properties of commercial AZ31 and AZ61 alloys. Appl. Surf. Sci. 2011, 257, 8558-8568.
19. Feliu, S., Jr; Samaniego, A.; El-Hadad, A.A.; Llorente, I. The effect of NaHCO3 treatment time on the corrosion resistance of commercial magnesium alloys AZ31 and AZ61 in 0.6 M NaCl solution. Corros. Sci. 2013, 67, 204-216.
20. Yao, H.B.; Li, Y.; Wee, A.T.S. An XPS investigation of the oxidation/corrosion of melt-spun Mg. Appl. Surf. Sci. 2000, 158, 112-119.
21. Pourbaix, M. Atlas of Electrochemical Equilibria in Aqueous Solutions; Pergamon Press: Oxford, UK, 1966.
22. Ardelean, H.; Frateur, I.; Marcus, P. Corrosion protection of magnesium alloys by cerium, zirconium and niobium-bases coatings, Corros. Sci. 2008, 40, 1907-1918.
23. Wang, L.; Shinohara, T.; Zhang, B.P.; Iwa, H. Characterization of surface products on AZ31 magnesium alloy in dilute NaCl solution J. Alloys Compd. 2009, 485, 747-752.
24. Lindström, R.; Svensson, J.E.; Johansson, L.G. The influence of carbon dioxide on the atmospheric corrosion of some magnesium alloys in the presence of NaCl. J. Electrochem. Soc. 2002, 149, B103-B107.
25. Lide, D.R. CRC Handbook of Chemistry and Physics, 86th ed.; CRC Press: Boca Raton, FL, USA, 2005; pp. 8-118.
26. Yamamoto, A.; Hiromoto, S. Effect of inorganic salts, amino acids and proteins on the degradation of pure magnesium in vitro. Mater. Sci. Eng. C 2009, 29, 1559-1568.
27. Samaniego, A.; Llorente, I.; Feliu, S., Jr. Combined effect of composition and surface condition on corrosion behaviour of magnesium alloys AZ31 and AZ61. Corros. Sci. 2013, 68, 66-71.
28. Liao, J.S.; Hotta, M.; Motoda, S.; Shinohara, T. Atmospheric corrosion of two field-exposed AZ31B magnesium alloys with different grain size. Corros. Sci. 2013, 71, 53-61.
29. Hosking, N.C.; Ström, M.A.; Shipway, P.H.; Rudd, C.D. Corrosion resistance of zinc-magnesium coated steel. Corros. Sci. 2007, 49, 3669-3695.
30. Liu, M.; Schmutz, P.; Zanna, S.; Seyeux, A.; Ardelean, H.; Song, G.; Atrens, A.; Marcus, P. Electrochemical reactivity, surface composition and corrosion mechanisms of the complex metallic alloy Al3Mg2. Corros. Sci. 2010, 52, 562-578.
31. Lunder, O.; Walmsley, J.C.; Mack, P.; Nisancioglu, K. Formation and characterization of a chromate conversion coating on AA6060 aluminium. Corros. Sci. 2005, 47, 1604-1624.
32. Pebere, N.; Riera, C.; Dabosi, F. Investigation of magnesium corrosion in aerated sodium-sulfate solution by electrochemical impedance spectroscopy. Electrochim. Acta 1990, 35, 555-561.
33. Mathieu, S.; Rapin, C.; Hazan, J.; Steinmetz, P. Corrosion behaviour of high pressure die-cast and semi-solid cast AZ91D alloys. Corros. Sci. 2002, 44, 2737-2756.
34. Baril, G.; Pebere, N. The corrosion of pure magnesium in aerated and deareated sodium sulfate solutions. Corros. Sci. 2001, 43, 471-484.
35. Makar, L.; Kruger, J. Corrosion studies of rapidly solidified magnesium alloys. J. Electrochem. Soc. 1990, 137, 414-421.
36. Stern, M.; Geary, A.L. Electrochemical polarization 1. A theoretical analysis of the shape of polarization curves. J. Electrochem. Soc. 1957, 104, 56-63.
37. ZView Software, Version 3.1c; Scribner Associates Inc.: Southern Pines, NC, USA, 2007.
38. Pinto, R.; Ferreira, M.G.S.; Carmezim, M.J.; Montemor, M.F. The corrosion behaviour of rare-earth containing magnesium alloys in borate buffer solution. Electrochim. Acta 2011, 56, 1535-1545.
39. Cordoba-Torres, P.; Keddam, M.; Nogueira, R.P. On the intrinsic electrochemical nature of the inductance in EIS, a monte Carlo simulation of the two consequitive-step mechanism: The flat surface 2 D case. Electrochim. Acta 2008, 54, 518-523.
40. Baril, G.; Galicia, G.; Deslouis, C.; Pébere, N.; Tribollet, B.; Vivier, V. An impedance investigation of the mechanism of pure magnesium corrosion in sodium sulfate solutions. J. Electrochem. Soc. 2007, 154, C108-C113.
41. 4/KOH buffered K2SO4 solutions. Corros. Sci. 2007, 49, 1878-1894.
42. Mansfeld, F.; Fernandes, J.C.S. Impedance spectra for aluminium 7075 during the early stages of immersion in sodium chloride. Corros. Sci. 1993, 34, 2105-2108.
43. 2 in the initial stage of atmospheric corrosion of AZ91 magnesium alloy in the presence of NaCl. Rare Met. 2006, 25, 190-196.
44. Liu, W.; Cao, F.; Chen, A.; Chang, L.; Zhang, J.; Cao, C. Effect of chloride ion concentration on electrochemical behavior and corrosion product of AM60 magnesium alloy in aqueous solutions. Corrosion 2012, 68, 045001:1-045001:14.
45. Song, G.L.; Atrens, A. Corrosion mechanisms of magnesium alloys. Adv. Eng. Mater. 1999, 1, 11-33.
46. Liu, M.; Uggowitzer, P.J.; Nagasekhar, A.V.; Schmutz, P.; Easton, M.; Song, G.L.; Atrens, A. Calculated phase diagrams and the corrosion of die-cast Mg-Al alloys. Corros. Sci. 2009, 51, 602-619.
47. Nordlien, J.H.; Nisancioglu, K.; Ono, S.; Masuko, N. Morphology and structure of oxide films formed on MgAl alloys by exposure to air and water. J. Electrochem. Soc. 1996, 143, 2564-2572.
48. Pardo, A.; Merino, M.C.; Coy, A.E.; Arrabal, R.; Viejo, F.; Matykina, E. Corrosion behaviour of magnesium/aluminium alloys in 3.5 wt% NaCl. Corros. Sci. 2008, 50, 823-834.
49. Jönsson, M.; Persson, D.; Gubner, R. The initial steps of atmospheric corrosion on magnesium alloy AZ91D. J. Electrochem. Soc. 2007, 154, C684-C691.
50. Hara, N.; Kobayashi, Y.; Kagaya, D.; Akao, N. Formation and breakdown of surface films on magnesium and its alloys in aqueous solutions. Corros. Sci. 2007, 49, 166-175.
51. Nordlien, J.H.; Ono, S.; Masuko, N.; Nisancioglu, K. A TEM investigation of naturally formed oxide films on pure magnesium. Corros. Sci. 1997, 39, 1397-1414.
52. 3 and corrosion behaviour in Hank's solution for new biomaterial applications. Mater. Trans. 2001, 42, 1777-1780.
53. Wagner, C.D.; Davis, L.E.; Zeller, M.V.; Taylor, J.A.; Raymond R.H.; Gale. L.H. Empirical atomic sensitivity factor for quantitative analysis by electron spectroscopy for chemical analysis. Surf. Interface Anal. 1981, 3, 211-225.
54. Kirkland, N.T.; Birbilis, N.; Staiger, M.P. Assessing the corrosion of biodegradable magnesium implants: A critical review of current methodologies and their limitations. Acta Biomater. 2012, 8, 925-936.