Degradation monitoring of impact damaged carbon fibre reinforced polymers under fatigue loading with pulse phase thermography

Composites Part B: Engineering

Volumn 59, Issue , 2014, Pages 221-229

  Schmutzler, Henrik ^a   Alder, Marko ^a   Kosmann, Nils ^a   Wittich, Hans ^a   Schulte, Karl ^a,b  

^a HAMBURG UNIVERSITY OF TECHNOLOGY   (Germany)

^b KING ABDULAZIZ UNIVERSITY   (Saudi Arabia)

Author keywords

A. Carbon fibre; B. Fatigue; B. Impact behaviour; D. Non destructive testing

Indexed keywords

CARBON FIBRE REINFORCED POLYMER; FATIGUE LOADINGS; GEOMETRICAL DIMENSIONS; IMPACT BEHAVIOUR; NON DESTRUCTIVE TESTING; PHASE ANGLE DIFFERENCES; PULSE PHASE THERMOGRAPHY; TENSION-COMPRESSION;

CARBON FIBERS; FIBER REINFORCED PLASTICS; NONDESTRUCTIVE EXAMINATION;

CRACKS;

EID: 84891755592     PISSN: 13598368     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesb.2013.12.010     Document Type: Article

References (30)

1. G. Busse Nondestructive evaluation of polymer materials: special issue: characterization of materials NDT & E Int 27 5 1994 253 262
2. C. Garnier, M. Pastor, F. Eyma, and B. Lorrain The detection of aeronautical defects in situ on composite structures using nondestructive testing Compos Struct 93 5 2011 1328 1336
3. Y. Hung, Y. Chen, S. Ng, L. Liu, Y. Huang, and B. Luk et al. Review and comparison of shearography and active thermography for nondestructive evaluation Mater Sci Eng R 2009 64 2009 73 112
4. T. Sujidkul, and Z. Xia Coupled thermal-mechanical modeling of carbon fibers reinforced polymer composites for damage detection Compos B Eng 43 3 2012 1631 1636
5. D. Wu, and G. Busse Lock-in thermography for non-destructive evaluation of materials Revue Générale de Thermique 37 1998 103 117
6. Sakagami T, Kubo S, Teshima Y, Dinwiddie RB, LeMieux DH. In: Proceedings of AeroSense 2000, Orlando, FL; Monday 24 April 2000.
7. X. Maldague, and S. Marinetti Pulse phase infrared thermography J Appl Phys 79 5 1996 2694
8. X. Maldague, F. Galmiche, and A. Ziadi Advances in pulsed phase thermography Infrared Phys Technol 43 3-5 2002 175 181
9. R. Usamentiaga, P. Venegas, J. Guerediaga, L. Vega, and I. López Automatic detection of impact damage in carbon fiber composites using active thermography Infrared Phys Technol 58 2013 36 46
10. Usamentiaga R, Venegas P, Guerediaga J, Vega L, López I. Feature extraction and analysis for automatic characterization of impact damage in carbon fiber composites using active thermography. NDT & E Int (0) 2013.
11. T.K. O'Brien, and K.L. Reifsnider Fatigue damage: stiffness/strength comparisons for composite materials J Test Eval 5 5 1977 384
12. Highsmith AL, Reifsnider KL. Stiffness-Reduction Mechanisms in Composite Laminates. In: Reifsnider KL, editor. Damage in Composite Materials: Basic Mechanisms, Accumulation, Tolerance and Characterization. Baltimore: ASTM, 1982, p.103-117.
13. M. Rheinfurth, N. Kosmann, D. Sauer, G. Busse, and K. Schulte Lamb waves for non-contact fatigue state evaluation of composites under various mechanical loading conditions Compos A Appl Sci Manuf 43 8 2012 1203 1211
14. R.D. Jamison, K. Schulte, K.L. Reifsnider, and W.W. Stinchcomb Characterization and analysis of damage mechanisms in tension-tension fatigue of graphite/epoxy laminates Eff Defects Compos Mater 1984 21 55
15. E.K. Gamstedt, and B.A. Sjögren Micromechanisms in tension-compression fatigue of composite laminates containing transverse plies Compos Sci Technol 59 2 1999 167 178
16. N. Uda, K. Ono, and K. Kazuo Compression fatigue failure of CFRP laminates with impact damage Compos Sci Technol 69 2009 2308 2314
17. M.H. Beheshty, B. Harris, and T. Adam An empirical fatigue-life model for high-performance fibre composites with and without impact damage Compos A 30 1999 971 987
18. N.H. Tai, C.C.M. Ma, J.M. Lin, and G.Y. Wu Effects of thickness on the fatigue-behavior of quasi-isotropic carbon/epoxy composites before and after low energy impacts Compos Sci Technol 59 11 1999 1753 1762
19. D.D. Symons, and G. Davis Fatigue testing of impact-damaged T300/914 carbon-fibre-reinforced plastic Compos Sci Technol 60 2000 379 389
20. A. Chen, D. Almond, and B. Harris In situ monitoring in real time of fatigue-induced damage growth in composite materials by acoustography Compos Sci Technol 2001 61 2001 2437 2443
21. A. Chen, D. Almond, and B. Harris Impact damage growth in composites under fatigue conditions monitored by acoustography Int J Fatigue 2002 24 2002 257 261
22. Toscano C, Riccio A, Camerlingo F, Meola C. Lockin thermography to monitor propagation of delamination in CFRP composites during compression tests. In: Proceedings of 11th QIRT conference. Naples, Italy; June, 2012.
23. A. Mian, X. Han, S. Islam, and G. Newaz Fatigue damage detection in graphite/epoxy composites using sonic infrared imaging technique Compos Sci Technol 64 5 2004 657 666
24. A. Mian, G. Newaz, X. Han, T. Mahmood, and C. Saha Response of sub-surface fatigue damage under sonic load - a computational study Compos Sci Technol 64 9 2004 1115 1122
25. V. Trappe, and K. Harbich Intralaminar fatigue behaviour of carbon fibre reinforced plastics Int J Fatigue 28 10 2006 1187 1196
26. L. Toubal, M. Karama, and B. Lorrain Damage evolution and infrared thermography in woven composite laminates under fatigue loading Int J Fatigue 28 12 2006 1867 1872
27. F. Libonati, and L. Vergani Damage assessment of composite materials by means of thermographic analyses Compos B Eng 50 2013 82 90
28. A. Gagel, D. Lange, and K. Schulte On the relation between crack densities, stiffness degradation, and surface temperature distribution of tensile fatigue loaded glass-fibre non-crimp-fabric reinforced epoxy Compos A Appl Sci Manuf 37 2 2006 222 228
29. C. Garnier, M. Pastor, B. Lorrain, and O. Pantalé Fatigue behavior of impacted composite structures Compos Struct 100 2013 443 450
30. T.H. Matondang, and D. Schütz The influence of anti-buckling guides on the compression fatigue behaviour of carbon fibre-reinforced plastic laminates Composites 15 3 1984 217 221