Rolling contact fatigue behavior of sintered and hardened steels

Journal of Failure Analysis and Prevention

Volumn 2, Issue 4, 2002, Pages 71-75

  Gnanamoorthy, R ^a   Rajiv, N ^a   Gopinath, K ^a   Miyahsita, Y ^b   Mutoh, Y ^b  

^a INDIAN INSTITUTE OF TECHNOLOGY MADRAS   (India)

^b NAGAOKA UNIVERSITY OF TECHNOLOGY   (Japan)

Author keywords

Density; Failure analysis; Powder metallurgy steels; Rolling contact fatigue; Sintered and hardened

Indexed keywords

DENSITY (SPECIFIC GRAVITY); FAILURE ANALYSIS; FATIGUE TESTING; FRICTION; HARDENING; HARDNESS; POROSITY; POWDER METAL PRODUCTS; POWDER METALLURGY; ROLLERS (MACHINE COMPONENTS); ROLLING; SINTERING; STEEL METALLURGY; STEEL POWDER METALLURGY; STEEL TESTING;

ENDURANCE LIMIT; FATIGUE FAILURES; FATIGUE TEST MACHINE; NUMBER OF CYCLES TO FAILURE; POWDER PROCESSING; ROLLING CONTACT FATIGUE; SINTERED AND HARDENED; SINTERED AND HARDENED STEEL;

FATIGUE OF MATERIALS;

EID: 84889009747     PISSN: 15477029     EISSN: None     Source Type: Journal    
DOI: 10.1007/bf02715457     Document Type: Review

References (15)

1. G.F. Bocchini: "The Influence of Porosity on the Characteristics of Sintered Materials," Int. J. Powder Metall., 1986, 22(3), pp. 185-200.
2. J. Holmes and R.A. Queeney: "Fatigue Crack Initiation in a Porous Steel," Powder Metall., 1985, 28(4), pp. 231-35.
3. P. Beiss and M. Dalgic: "Effects of Pore Structure on Bending Fatigue Strength of Sintered Steel," Metal Powder Report, 1997, 51(1), pp. 38-40.
4. Y.T. Chen: "Fracture Toughness Testing of PM Materials," Metal Powder Report, 1989, 39, pp. 425-28.
5. W. Pompe, G. Leitner, K. Wetzig, G. Zies, and W. Grabner: "Crack Propagation and Processes Near Crack Tip of Metallic Sintered Materials," Powder Metall., 1984, 27, pp. 45-52.
6. R.C. Juvinall and K.M. Marshek: Fundamentals in Machine Design, John Wiley & Sons, New York, 1991, p. 331.
7. S. Way: "Pitting Due to Rolling Contact," ASME, J. Appl. Mech., 1935, 2, pp. A49-58.
8. W. Cheng, H.S. Cheng, L.M. Keet, and X. Li: "Surface Crack Initiation Under Contact Fatigue: Experimental Observation and Contact Analysis," T. ASME J. Tribol., 1993, 115, pp. 658-65.
9. H. Salehinzadeh and N. Saka: "Crack Propagation in Rolling Line Contacts," T. ASME J. Tribol., 1992, 114, pp. 690-95.
10. C.A. Stickels: "Rolling Contact Fatigue Tests of 52100 Bearing Steel Using a Modified NASA Ball Test Rig," Wear, 1984, 98, pp. 199-210.
11. L. Xiaogan, C. Quing, and S. Eryu: "Initiation and Propagation of Case Crushing Cracks in Rolling Contact Fatigue," Wear, 1988, 122, pp. 33-43.
12. P.H. Dawson: "Effect of Metallic Contact on the Pitting of Lubricated Rolling Surfaces," J. Mech. Eng. Sci., 1962, 4(1), pp. 16-20.
13. S. Marcela and A. Salak: "Durability and Failure of Powder Forged Rolling Bearing Rings," Wear, 1999, 236, pp. 47-54.
14. A.W. Julia, P.D. Nurthen, and P.R. Brewin: "Rolling Contact Fatigue Testing of P/M High Speed Steels," Int. J. Powder Metall., 1990, 26, pp. 345-51.
15. K.L. Johnson: Contact Mechanics, Cambridge University Press, Cambridge, 1985.