Evaluation of the role of hydrogen in SCC in hot water

NACE - International Corrosion Conference Series

Volumn 1997-March, Issue , 1997, Pages

  Andresen, Peter L ^a   Angeliu, Thomas M ^a  

^a GE GLOBAL RESEARCH   (United States)

Author keywords

High temperature water; Hydrogen effects; Nickel alloys; Stainless steel; Stress corrosion cracking

Indexed keywords

HIGH TEMPERATURE CORROSION; HYDROGEN BONDS; IRON ALLOYS; NICKEL ALLOYS; SINGLE CRYSTALS; STAINLESS STEEL; STEEL CORROSION; WATER;

COHESIVE STRENGTH; CRACK ADVANCE; DISLOCATION MOBILITY; ENVIRONMENTAL CRACKING; HIGH-TEMPERATURE WATER; HYDROGEN EFFECT; METAL BONDS; NICKEL BASE ALLOYS;

STRESS CORROSION CRACKING;

EID: 84884723639     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (34)

1. Parkins Symposium on Fundamental Asepcts of Stress Corrosion Cracking, Ed. S.M. Bruemmer et al., TMS-AIME, Warrendale, September 1991.
2. Corrosion-Deformation Interactions, Eds. T. Magnin & J.M. Gras, Fontainebleu, Les Editions de Physique Les Ulis, 1993.
3. Hydrogen Effects in Metals, Eds. L.M. Bernstein and A.W. Thompson, TMS-AIME, 1981.
4. Hydrogen Degradation of Ferrous Alloys, Eds. R.A. Oriani, J.P. Hirth & M. Smialowski, Noyes Publ-, 1985.
5. P.L. Andresen and F.P. Ford, "Fundamental Quantification of Crack Advance for Life Prediction in Energy Systems", Proc., Corrosion/96 Research Symposium on Life Prediction of Structures Subject of Environmental Degradation, NACE, 1996.
6. F. Peter Ford and Peter L. Andresen, "Corrosion in Nuclear Systems: Environmentally Assisted Cracking in Light Water Reactors", in Corrosion Mechanisms, Ed. P. Marcus and J. Ouder, Marcel Dekker, p.501-546, 1994.
7. F.P. Ford, D.F. Taylor, P.L. Andresen and R.G. Ballinger, "Corrosion Assisted Cracking of Stainless and Low Alloy Steels in LWR Environments", EPRI Contract RP2006-6, Report NP5064M, February 1987.
8. C.L. Briant, "Theoretical Considerations for Decohesion in Low Alloy and Turbine Steels", in Hydrogen Degradation of Ferrous Alloys, Eds. R.A. Oriani, J.P. Hirth & M. Smialowski, Noyes Publ., 1985.
9. C.L. Briant, "Hydrogen Assisted Cracking of Type 304 Stainless Steel", Met Trans A, 10A, p. 181, 1979.
10. P.L. Andresen, "Effects of Temperature on Crack Growth Rates of Stainless Steel & Alloy 600", Corrosion 49, p.714, 1993.
11. Y. Shen and P.G. Shewmon, Met. Trans. A, 22A, p. 1857-1864, 1991.
12. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, p.829, 1995.
13. T.A. Angeliu and P.L. Andresen, "Effect of Exposure to High Temperature Water on the Hydrogen Degradation of High Strength Materials", unpublished research, GE CRD, 1995.
14. C.A. Grove and L.D. Petzold, "Mechanism of SCC of Alloy X750 in High Purity Water", J. of Materials for Energy Systems, Vol. 7, No. 2, p.147-162, Sept 1985.
15. L.D. Petzold and C.A. Grove, "Mechanism of SCC of Alloy X750 in High Purity Water", proceedings of Corrosion of Nickel Alloys, Ed. R.C. Scarberry, ASM, 1985, p. 165.
16. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, ANS, 1992, p. 294.
17. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, ANS, 1992, p.209-218.
18. P.L. Andresen, "Irradiation Assisted Stress Corrosion Cracking", in Book on Stress Corrosion Cracking: Materials Performance and Evaluation, Ed. R.H. Jones, ASM, Materials Park, 1992, p.181-210.
19. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, p. 361, 1993.
20. T.M. Angeliu, P.L. Andresen, and M.L. Pollick, "Repassivation and Crack Propagation of Alloy 600 in 288°C Water", Paper 96086, Corrosion/96, NACE, 1996.
21. G. Economy, R.J. Jacko, and F.W. Pement, Corrosion 43, p.727-734, 1987.
22. N. Totsuka & Z. Szklarska-Smialowska, "Effect of Electrode Potential on the Hydrogen-Induced IGSCC of Alloy 600 in an Aqueous Solution at 350°C", Corrosion 43, p.734, 1987.
23. R. Rios, T. Magnin, D. Noel, and O. deBouvier, "Critical Analysis of Alloy 600 SCC Mechanisms in Primary Water", Met Trans A, 26A, p.925, 1995.
24. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, NACE, p.563-578, 1995.
25. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, p.735-746, 1995.
26. B.W. Bussert, I. Goldberg, R.F. Keefer, and N. Lewis, "An Integrated Approach to Investigating SCC", Workshop on PWSCC of Alloy 600 in PWRs, EPRI, April 1993.
27. P.L. Andresen, "Conceptual Similarities and Common Predictive Approaches for SCC in High Temperature Water Systems", Paper 96258, Corrosion/96, NACE, 1996.
28. T.M. Angeliu and G.S. Was, "Creep and Intergranular Cracking of Ni-Cr-Fe-C Alloys in Argon at 360°C", Met. Trans, 25A, p.1169-1184, 1994.
29. T.M. Angeliu, D.J. Pavarenti, and G.S. Was, "Creep and Intergranular Cracking Behavior of Ni-Cr-Fe-C Alloys in 360°C Water", Corrosion, 51, p.837-848, 1995.
30. th Int Symp on Env. Degradation of Mat'ls in Nuclear Power Systems - Water Reactors, NACE, p.8-28, 1990.
31. A.J. Jacobs, "Hydrogen Buildup in Irradiated Type 304 Stainless Steel", 13th Symp. Radiation Induced Changes in Microstructure, Eds. F.A. Garner, N.H. Packan & A.S. Kumar, STP 956, Vol. II, ASTM, Philadelphia, 1985, p. 239.
32. G.R. Caskey, Jr, "Hydrogen Effects in Stainless Steels", in Hydrogen Degradation of Ferrous Alloys, Eds. R.A. Oriani, J.P. Hirth & M. Smialowski, Noyes Publ, p.822, 1985.
33. th Int Symp on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, p.867-880, 1995.
34. D.M. Carey, D.J. Perry, T.R. Miller and C.D. Thompson, "Alloy 600 SCC Growth Measurements in Primary Coolant", Workshop on PWSCC of Alloy 600 in PWRs, EPRI, November 1994.