Vacancy-creep model for EAC of metallic materials in high temperature water

NACE - International Corrosion Conference Series

Volumn 1996-March, Issue , 1996, Pages

  Aaltonen, P ^a   Saario, T ^a   Karjalainen Roikonen, P ^a   Piippo, J ^a   Tahtinen S ^a   Itaaho M ^b   Hanninen H ^b  

^a VTT TECHNICAL RESEARCH CENTRE OF FINLAND   (Finland)

^b AALTO UNIVERSITY   (Finland)

Author keywords

Creep; Dislocation; EAC; Migration; Vacancy

Indexed keywords

CRACK PROPAGATION; CREEP; DISLOCATIONS (CRYSTALS); HIGH TEMPERATURE CORROSION; HYDROGEN EMBRITTLEMENT; INTERGRANULAR CORROSION; METALS; NICKEL ALLOYS; OXIDE FILMS; RESIDUAL STRESSES; TEXTURES; VACANCIES;

ELECTROCHEMICAL POTENTIAL; ENVIRONMENTALLY ASSISTED CRACKING; HIGH-TEMPERATURE WATER; INTERGRANULAR STRESS CORROSION CRACKING; MECHANISTIC MODELING; MIGRATION; SELECTIVE DISSOLUTION; TRANSGRANULAR STRESS CORROSION CRACKING;

STRESS CORROSION CRACKING;

EID: 84884722956     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (30)

1. A. Turnbull, Modelling of environmental assisted cracking, Corrosion Science 34, (1993): pp. 21-960.
2. R. C. Newman, M. Saito, "Anodic stress-corrosion cracking: slip-dissolution and film-induced cleavage", Proc. Int. Conf. on Corrosion-Deformation Interactions, CDI'92, pp. 3-26. Eds. T. Magnin and J. M. Gras, Les Editions de Physique Les Ulis, 1993.
3. H. Hänninen, "Comparison of proposed stress corrosion cracking mechanisms", Proc. of 10th Scandinavian Corrosion Congress, pp. 405-412. Stockholm, 1986.
4. P. Ford, P. Andresen, H. Solomon, G. Gordon, S. Ranganath, D. Weinstein, and R. Pathania, "Application of water chemistry control, on-line monitoring and crack growth rate models for improved BWR materials performance", Proc. 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors. Ed. D. Cubicciotti, pp. 4-26-4-51. NACE, 1990.
5. P. Ford, D. Taylor, P. Andresen and R. Ballinger, Environmentally controlled cracking of stainless and low alloy steels in light water reactor environments. NP-5064M, Final Report (Palo Alto, CA: EPRI, 1987).
6. K. Sieradzki, R. Newman, Brittle behavior of ductile metals during stress corrosion cracking. Philosophical Magazine 51, (1985): pp. 95-132.
7. D. A., Jones, A unified mechanism of stress corrosion and corrosion fatigue cracking, Metallurgical Transactions, Vol 16A, June (1985): pp. 1133-1141.
8. E. I. Meletis, K. Lian and W. Huang, "Vacancy-dislocation interactions and transgranular stress corrosion cracking, " Proc. Int. Conf. on Corrosion-Deformation Interactions, CDI'92, p. 69-81, Eds. T. Magnin and J. M. Gras, Les Editions de Physique Les Ulis, 1993.
9. T. Saario, P. Aaltonen, P. Karjalainen-Roikonen, J. Piippo, K. Mäkelä, S. Tähtinen and H. Hänninen, "Selective Dissolution-Vacancy-Creep Model for IGSCC of Alloy 600, " presented at Seventh Int. Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Colorado, pp. 841-854. NACE, 1995.
10. A. J. Davenport, M. Sansone, J. A. Bardwell, A.J. Aldykiewicz, Jr., M. Taube and CM. Vitus, In situ multielement XANES study of formation and reduction of the oxide film on stainless steel, J. Electrochem. Soc, 139, 2(1992): pp. 371-373.
11. H. Hänninen, P. Aaltonen, P. Nenonen, R. Jargelius and B. Lehtinen, Characterization of austenitic stainless steel pipe welds after prolonged power plant exposure, Corrosion 48, 2(1992): pp. 114-123.
12. P. L. Andresen, F. P. Ford, S. M. Murphy, J. M. Perks, "State of knowledge of radiation effects on environmental cracking in light water reactor core materials", presented at Fourth Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Jekyll Island, 1989. P. 1-83-1-120.
13. H. W. Pickering, C. Wagner, Electrolytic dissolution of binary alloys containing a noble metal, Electrochemical Science 114, 7 (1967): pp. 698-706.
14. J. Robertson, The mechanism of high temperature aqueous corrosion of stainless steels, Corrosion Science, 32, 4(1991): pp. 443-465.
15. D. D. Macdonald, The point defect model for the passive state, J.I Electrochem. Soc, 139, 12(1992): pp. 3434-3449.
16. M. Itäaho, The effect of environment on the creep and fracture behavior of materials. Helsinki University of Technology, MSc. Thesis, 1995, 96 p.
17. R. W. Revie, H. H. Uhlig, Effect of applied potential and surface dissolution on the creep behavior of copper. Acta Metallurgica, 22, May (1974): pp. 619-627.
18. S. Tähtinen, P. Nenonen and H. Hänninen, Hydrogen-induced phase transformations in an austenitic stainless steel. Scripta Metallurgica 20, 1(1986): pp. 153-157.
19. T. Saario, J. Piippo, Mechanism of electronic conduction in passive film on iron. 7th Int. Symposium on Passivity, Passivation of Metals and Semiconductors. Clausthal, Germany, 21-26 August, 1994. Institut für Metallkunde und Metallphysik der TU Clausthal.
20. T. R. Anthony, Atom currents generated by vacancy winds. In: Diffusion in solids, recent developments. Eds. A. S. Nowick and J. J. Burton. (New York: Academic Press, 1975), pp. 353-379.
21. J. P. Hirth, W. D. Nix, Analysis of cavity nucleation in solids subjected to external and internal stresses. Acta Metallurgica 33, (1985): pp. 359-368.
22. F. A. Garner, D. S. Gelles, Irradiation creep mechanisms: an experimental perspective. Journal of Nuclear Materials 159, (1988): pp. 286-309.
23. N. Totsuka, Z. Szlarska-Smialowska, Effect of electrode potential on the hydrogen-induced IGSCC of Alloy 600 in high temperature aqueous environments. Corrosion 43, (1987): pp. 734-738.
24. H. A. Hänninen, T. C. Lee, I. M. Robertson and H.K. Birnbaum, Direct observations on hydrogen effects on fracture of A533B steel. Proc. Int. Conf. on Corrosion-Deformation Interactions, CDI'92, pp. 377-388. Eds. T. Magnin and J. M. Gras, Les Editions de Physique Les Ulis, 1993.
25. D.V. Beggs, M. T. Hahn and E. N. Pugh, "Recent observations on the propagation of stress corrosion cracks and their relevance to proposed mechanisms of stress corrosion cracking". Hydrogen Embrittlement and Stress Corrosion Cracking, pp.181-205. Eds. R. Gibala and R. F. Hehemann. ASTM, 1984.
26. D. A. Jones, "Evidence for localized surface plasticity during stress corrosion cracking, " Corrosion '95, Paper No. 169. 9 p.
27. R. O. Toivanen, On the mechanism of dezincification of brass. Helsinki University of Technology, Report TKK-V-A14, 1995. 30 p.
28. W. G. Wolfer, Correlation of radiation creep theory with experimental evidence. Journal of Nuclear Materials 90, (1980): pp.175-192.
29. A. J. Jacobs, Hydrogen buildup in irradiated type-304 stainless steel. ASTM STP 956. Eds. F. A. Garner, C. H. Henager, Jr. and N. Igata (Philadelphia: American Society for Testing and Materials, 1987), pp. 239-244.
30. S. Jani, M. Marek, R. F. Hochman and E. I. Meletis, A mechanistic study of transgranular stress corrosion cracking of type 304 stainless steel. Metallurgical Transactions, Vol. 22A, June (1991): pp. 1453-1461.