A predictive fatigue life model for anodized 7050 aluminium alloy

International Journal of Fatigue

Volumn 48, Issue , 2013, Pages 205-213

  Chaussumier, Michel ^a   Mabru, Catherine ^a   Shahzad, Majid ^a   Chieragatti, Rémy ^a   Rezai Aria, Farhad ^a  

^a UNIVERSITÉ DE TOULOUSE   (France)

Author keywords

Anodizing; Crack growth; Life prediction; Pickling; Short crack

Indexed keywords

ALUMINUM; ALUMINUM ALLOYS; ANODIC OXIDATION; CONCENTRATION (PROCESS); CRACK PROPAGATION; FATIGUE OF MATERIALS; FATIGUE TESTING; FORECASTING; PICKLING; PLASTIC DEFORMATION; STRESS CONCENTRATION; SURFACE DEFECTS;

7050 ALUMINIUM ALLOY; FATIGUE LIFE PREDICTIVE MODELS; FRACTOGRAPHIC OBSERVATIONS; LIFE PREDICTIONS; PREDICTIVE MODELING; SHORT CRACKS; STRESS CONCENTRATORS; TOPOGRAPHY MEASUREMENT;

CRACKS;

EID: 84883655175     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2012.11.002     Document Type: Article

References (34)

1. ASM Handbook. Corrosion, vol. 13. USA: ASM International; 1992.
2. Cree AM, Weidmann GW. Effect of anodized coatings on fatigue cracks rates of aluminium alloy. Surf Eng 1997;13(1):51-5. (Pubitemid 127663726)
3. Kermanidis AL, Th, Petroyiannis PV, Pantelakis Sp. G. Fatigue damage tolerance behaviour of coroded 2024 T351 aircraft aluminium alloy. Theorical and Applied Fracture Mechanics 2005;43:121-32.
4. Lonyuk B, Apachitei I, Duszczyk J. The effect of oxide coatings on fatigue properties of 7475-T6 aluminium alloy. Surf Coat Technol 2007;201(21):8688-94. (Pubitemid 47194254)
5. Sadeler R. Effect of a commercial hard anodizing on the property of a 2024-T6 aluminium alloy. J Mater Sci 2006;41:5803-9. (Pubitemid 44386624)
6. Camargo A. Voorwald, Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy. Fatigue Fract Eng Mater Struct 2007;30:993-1007. (Pubitemid 47578047)
7. Cyrik E, Genel K. Effect of anodic oxidation on the fatigue performance of 7075-T6 alloy. Surf Coat Technol 2008;202:5190-201.
8. Shahzad M, Chaussumier M, Chieragatti R, Mabru C, Rezaî-aria F. Effect of sealed anodic film on fatigue performance od 2214-T6 aluminium alloy. Surf Coat Technol 2012;206:2733-9.
9. Rokhlin SI, Kim JY, Nagy H, Zoofan B. Effect of pitting on fatigue crack initiation and fatigue life. Eng Fract Mech 1998;62:425-44.
10. Pao PS, Gill SJ, Feng CR. On fatigue crack initiation from corrosion pits in 7075-T7351 aluminium alloy. Scripta Mater 1998;43(5):391-6.
11. Dolley EJ, Wei RP. The effect of pitting corrosion on fatigue life. Fatigue Fract Eng Mater Struct 2000;23:555-60. (Pubitemid 32874946)
12. Rateick RG, Griffith RJ, Hall DA, Thompson KA. Relationship of microstructure to fatigue strength loss in anodized aluminium-copper alloys. Mater Sci Technol 2005;21:1227-35. (Pubitemid 41541873)
13. Thompson GE, Zhang L, C. Smith JE, Skeldon P. Boric/sulfuric acid anodizing of aluminum alloys 2024 and 7075: film growth and corrosion resistance. Corros Sci 1999;55:1052-60.
14. Snogan F, Blanc C, Mankowski G, Pébère N. Characterisation of sealed anodic films on 7050 T74 and 2214 T6 aluminium alloys. Surf Coat Technol 2002;154:94-103. (Pubitemid 34557465)
15. Liu JH, Li M, Li SM, Huang M. Effect of the microstructure of Al 7050-T7451 on anodic oxide formation in sulfuric acid. Int J Mineral, Metal Mater 2009;16:432-8.
16. Barter SA. Fatigue crack growth in 7050 aluminium alloy thick section plate with a surface condition simulating some regions of F/A-18 structure, DSTO-TR-1458, 2003.
17. Isida M, Yoshida T, Noguchi H. Tension of a finite-thickness plate with a pair of semi-elliptical surface cracks. Eng Fract Mech 1990;35(6):961-5.
18. Murakami Y, Nemat-Nasser S. Interacting dissimilar semi-elliptical surface flaws under tension and bending. Eng Fract Mech 1982;16(3):373-86. (Pubitemid 12508885)
19. Chieragatti R, Surarachai M, Mabru C, Espinosa C, Vergnes V. Procédés de caractérisation de la tenue en fatigue d'une pièce à partir de son profil de surface. French Patent no 0650793, 2006.
20. Suraratchaï M, Limido J, Mabru C, Chieragatti R. Modelling the influence of machined surface roughness on the fatigue life of aluminium alloy. Int J Fatigue 2008;30(12):2119-26.
21. Shahzad M, Chaussumier M, Chieragatti R, Mabru C, Rezaï-Aria F. Influence of surface treatments on fatigue life of Al 7010 alloy. J Mater Process Technol 2010;210(13):1821-6.
22. Shahzad M, Chaussumier M, Chieragatti R, Mabru C, Rezaï-Aria F. Influence of anodizing process on fatigue life of machined aluminium alloy. Procedia Eng 2010;2(1):1015-24.
23. Chaussumier M, Shahzad M, Mabru C, Chieragatti R, Rezaï-Aria F. A fatigue multi-site cracks model using coalescence, short and long crack growth laws, for anodized aluminum alloys. Procedia Eng 2010;2(1):995-1004.
24. Chieragatti R, Espinosa C, Lacome JH, Limido J, Mabru C, SALAUN M. Influence of roughness on the fatigue of machined surfaces: determination of local stress concentration. 29èmes journées de Printemps, JP 2010 2010. 19-20 May 2010.
25. Shahzad M, Chaussumier M, Chieragatti R, Mabru C, Rézaï-Aria F. Surface characterization and influence of anodizing process on fatigue life of 7050 alloy. Mater Des 2011;32(6):3328-35.
26. Przystupa MA, Bussi RJ, Magnusen PE, Hinkle AJ. Microstructure based fatigue life predictions for thick plate 7050-T7451 airframe alloy. Int J Fatigue 1997;10(1):285-8.
27. Santus C, Taylor D. Physically short crack propagation in metals during high cycle fatigue. Int J Fatigue 2009;31:1356-65.
28. Haddad MH, Topper TH, Smith KN. Prediction of non propagating cracks. Eng Fract Mech 1979;11(3):573-84.
29. Pearson S. Initiation fatigue cracks in commercial aluminium alloys and the subsequent propagation of very short cracks. Eng Fract Mech 1975;7(2):235-47.
30. Lankford J. The influence of microstructure on the growth of small fatigue cracks. Fatigue Fract Eng Mater Struct 1895;8:161-75.
31. Newman JC, Philipps EP, Swain MH. Fatigue life prediction methodology using small-crack theory. Int J Fatigue 1999;21:109-19.
32. Chapetti MD. Fatigue propagation threshold of short cracks under constant amplitude loading. Int J Fatigue 2003;25:1319-26.
33. Newman JC, Raju IS. Stress-intensity factor equations for cracks in three dimensional finite bodies subjected to tension and bending loads. In: ATLURI SN, editor. Computational methods in mechanics of fracture. Elsevier Science Publishers; 1986. p. 312-34.
34. DeBartolo EA, Hillberry BM. A model of initial flaw sizes in aluminium alloys. Int J Fatigue 2001;23:79-86.