Growth of aligned single-crystalline TiO2 nanorod arrays on transparent conducting oxide coated glass

Japanese Journal of Applied Physics

Volumn 52, Issue 6 PART 2, 2013, Pages

  Tsai, Jung Che ^a   Hon, Min Hsiung ^a   Leu, Ing Chi ^b  

^a NATIONAL CHENG KUNG UNIVERSITY   (Taiwan)

^b NATIONAL UNIVERSITY OF TAINAN   (Taiwan)

Author keywords

[No Author keywords available]

Indexed keywords

ARRHENIUS EQUATION; COATED GLASS SUBSTRATES; HYDROTHERMAL METHODS; NANO-ROD ARRAYS; SINGLE-CRYSTALLINE; SYNTHESIS TEMPERATURES; TETRAGONAL RUTILE STRUCTURE; TRANSPARENT CONDUCTING OXIDE;

ACTIVATION ENERGY; COALESCENCE; CRYSTALLINE MATERIALS; GLASS; OXIDE MINERALS; SUBSTRATES; TITANIUM DIOXIDE;

NANORODS;

EID: 84881017076     PISSN: 00214922     EISSN: 13474065     Source Type: Journal    
DOI: 10.7567/JJAP.52.06GG09     Document Type: Conference Paper

References (29)

1. S. Y. Huang, L. Kavan, I. Exnar, and M. Grätzel: J. Electrochem. Soc. 142 (1995) L142.
2. J. Wang, Y. Bai, M. Wu, J. Yin, and W. F. Zhang: J. Power Sources 191 (2009) 614.
3. J. Jitputti, S. Pavasupree, Y. Suzuki, and S. Yoshikawa: Jpn. J. Appl. Phys. 47 (2008) 751.
4. A. Fujishima and K. Honda: Nature 238 (1972) 37.
5. B. O'Regan and M. Grätzel: Nature 353 (1991) 737.
6. V. M. Mohan and K. Murakami: Jpn. J. Appl. Phys. 51 (2012) 02BP11.
7. C. Shimada, K. Kitamura, and S. Shiratori: Jpn. J. Appl. Phys. 51 (2012) 044106.
8. T. Matsuura, T. Kato, K. I. Minato, and T. Ueno: Jpn. J. Appl. Phys. 51 (2012) 06FG07.
9. W. J. Lee and M. H. Hon: Appl. Phys. Lett. 99 (2011) 251102.
10. M. C. Li, C. C. Kuo, S. H. Peng, S. H. Chen, and C. C. Lee: Jpn. J. Appl. Phys. 51 (2012) 025504.
11. L. X. Chen, T. Rajh, Z. Y. Wang, and M. C. Thurnauer: J. Phys. Chem. B 101 (1997) 10688.
12. T. Kasuga, M. Hiramatsu, A. Hoson, A. Sekino, and K. Niihara: Adv. Mater. 11 (1999) 1307.
13. J. H. Yoon, S. R. Jang, R. Vittal, J. Lee, and K. J. Kim: J. Photochem. Photobiol. A 180 (2006) 184.
14. W. J. Lee, M. H. Hon, Y. W. Chung, and J. H. Lee: Jpn. J. Appl. Phys. 50 (2011) 06GH06.
15. K. H. Yu and J. H. Chen: Nanoscale Res. Lett. 4 (2009) 1.
16. P. Hoyer: Langmuir 12 (1996) 1411.
17. C. H. Sun, N. X. Wang, S. Y. Zhou, X. J. Hu, S. Y. Zhou, and P. Chen: Chem. Commun. (2008) 3293.
18. A. M. Nor, M. F. Achoi, M. H. Mamat, M. M. Zabidi, S. Abdullah, and M. R. Mahmood: Jpn. J. Appl. Phys. 51 (2012) 06FG08.
19. X. Feng, K. Shankar, O. K. Varghese, M. Paulose, T. J. Latempa, and C. A. Grimes: Nano Lett. 8 (2008) 3781.
20. J. H. Bang and P. V. Kamat: Adv. Funct. Mater. 20 (2010) 1970.
21. Q. H. Mu, Y. G. Li, Q. H. Zhang, and H. Z. Wang: J. Hazard. Mater. 188 (2011) 363.
22. M. Abd-Lefdil, R. Diaz, H. Bihri, M. Ait Aouaj, and F. Rueda: Eur. Phys. J.: Appl. Phys. 38 (2007) 217.
23. C. J. Howard, T. M. Sabine, and F. Dickson: Acta Crystallogr., Sect. B 47 (1991) 462.
24. H. M. Cheng, J. M. Ma, Z. G. Zhao, and L. M. Qi: Chem. Mater. 7 (1995) 663.
25. B. Liu and E. S. Aydil: J. Am. Chem. Soc. 131 (2009) 3985.
26. M. Adachi, Y. Murata, J. Takao, J. Jiu, M. Sakamoto, and F. Wang: J. Am. Chem. Soc. 126 (2004) 14943.
27. H. G. Yang, C. H. Sun, S. Z. Qiao, J. Zou, G. Liu, S. C. Smith, H. M. Cheng, and G. Q. Lu: Nature 453 (2008) 638.
28. K. Kakiuchi, E. Hosonob, H. Imai, T. Kimuraa, and S. Fujihara: J. Cryst. Growth 293 (2006) 541.
29. K. Lu and Y. Li: Phys. Rev. Lett. 80 (1998) 4474.