Homogenization of diffuse delamination in composite laminates

Composite Structures

Volumn 100, Issue , 2013, Pages 113-120

  Jalalvand, Meisam ^a   Hosseini Toudeshky, Hossein ^a   Mohammadi, Bijan ^b  

^a AMIRKABIR UNIVERSITY OF TECHNOLOGY   (Iran)

^b IRAN UNIVERSITY OF SCIENCE AND TECHNOLOGY   (Iran)

Author keywords

Composite laminates; Damage; Diffuse delmination; Homogenization; Interface

Indexed keywords

ANALYTICAL APPROACH; COMPOSITE LAMINATE; CROSS-PLY LAMINATE; DAMAGE; DIFFUSE DELMINATION; DOUBLE CANTILEVER BEAM; HOMOGENIZATION; TRANSVERSE CRACKING;

CRACKS; DELAMINATION; INTERFACES (MATERIALS); LAMINATES; STIFFNESS; TENSILE STRESS;

FAILURE (MECHANICAL);

EID: 84875343177     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2012.12.022     Document Type: Article

References (20)

1. Farrokhabadi A., Hosseini-Toudeshky H., Mohammadi B. A generalized micromechanical approach for the analysis of transverse crack and induced delamination in composite laminates. Compos Struct 2011, 93(2):443-455.
2. Hashin Z. Analysis of cracked laminates: a variational approach. Mech Mater 1985, 4(2):121-136.
3. McCartney L.N. Predicting transverse crack formation in cross-ply laminates. Compos Sci Technol 1998, 58(7):1069-1081.
4. Nairn J.A., Hu S. The initiation and growth of delamination induced by matrix microcracks in laminated composites. Int J Fract 1992, 57:1-24.
5. Takeda N., Ogihara S. Initiation and growth of delamination from the tips of transverse cracks in CFRP cross-ply laminates. Compos Sci Technol 1994, 52(3):309-318.
6. Allix O., Ladevèze P. Interlaminar interface modelling for the prediction of delamination. Compos Struct 1992, 22(4):235-242.
7. Ladeveze P. A damage mechanics for composites materials. Integration of theory and applications in applied mechanics 1990, Kluwer Academic Publishers, Dordrecht. J.F. Dijksman, F.T.M. Nieuwstadt (Eds.).
8. Ladevèze P. A damage computational method for composite structures. Comput Struct 1992, 44(1-2):79-87.
9. Ladevèze P., Lubineau G., Marsal D. Towards a bridge between the micro- and mesomechanics of delamination for laminated composites. Compos Sci Technol 2006, 66(6):698-712.
10. Barbero E.J., De Vivo L. A constitutive model for elastic damage in fiber-reinforced PMC laminae. Int J Damage Mech 2001, 10:73-93.
11. Ladeveze P., LeDantec E. Damage modelling of the elementary ply for laminated composites. Compos Sci Technol 1992, 43(3):257-267.
12. Allix O., Hild F. Continuum damage mechanics of materials and structures: present and future. Continuum damage mechanics of materials and structures 2002, Elsevier. O. Allix, F. Hild (Eds.).
13. Barbero E.J., Cortes D.H. A mechanistic model for transverse damage initiation, evolution, and stiffness reduction in laminated composites. Compos Part B: Eng 2010, 41(2):124-132.
14. Li S., Reid S.R., Soden P.D. A continuum damage model for transverse matrix cracking in laminated fibre-reinforced composites. Philos Trans Roy Soc Lond, Ser A 1998, 356(1746):2379-2412.
15. Farrokhabadi A., Hosseini-Toudeshky H., Mohammadi B. Damage analysis of laminated composites using a new coupled micro-meso approach. Fatigue Fract Eng Mater Struct 2010, 33(7):420-435.
16. Abisset E., Daghia F., Ladevèze P. On the validation of a damage mesomodel for laminated composites by means of open-hole tensile tests on quasi-isotropic laminates. Compos Part A: Appl Sci Manuf 2011, 42(10):1515-1524.
17. Camanho P.P., Davila C.G., de Moura M.F. Numerical simulation of mixed-mode progressive delamination in composite materials. J Compos Mater 2003, 37(16):1415-1438.
18. Davila CG, Camanho PP, de Moura MF. Mixed-mode decohesion elements for analyses of progressive delamination. In: 42nd AIAA/ASME/ASCEIAHS/ASC structures, structural dynamics and materials conference. Seattle, Washington; 2001. Paper AIAA-01-1486.
19. Benzeggagh M.L., Kenane M. Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus. Compos Sci Technol 1996, 56(4):439-449.
20. Balzani C., Wagner W. An interface element for the simulation of delamination in unidirectional fiber-reinforced composite laminates. Eng Fract Mech 2008, 75(9):2597-2615.