The effect of negative stress ratio load history on high cycle fatigue threshold

Journal of ASTM International

Volumn 2, Issue 5, 2005, Pages 79-95

  Golden, Patrick J ^a   Nicholas, Theodore ^b  

^a AIR FORCE RESEARCH LABORATORY   (United States)

^b AIR FORCE INSTITUTE OF TECHNOLOGY   (United States)

Author keywords

Fracture mechanics; High cycle fatigue; Load history; Overload; Small cracks; Threshold; Ti 6Al 4V

Indexed keywords

HIGH CYCLE FATIGUE; LOAD HISTORY; OVERLOAD; SMALL CRACKS; THRESHOLD; TI-6AL-4V;

CRACK PROPAGATION; LOADS (FORCES); MATHEMATICAL MODELS; NUCLEATION; STRESS ANALYSIS;

TITANIUM ALLOYS;

EID: 84871326744     PISSN: None     EISSN: None     Source Type: Journal    
DOI: 10.1520/JAI12042     Document Type: Review

References (18)

1. rd Volume, ASTM STP 1417, W. G. Reuter and R. S. Piascik, Eds., ASTM International, West Conshohocken, PA, 2002, pp. 476-492.
2. Jasper, T. M., "The Value of the Energy Relation in the Testing of Ferrous Metals at Varying Ranges of Stress and at Intermediate and High Temperatures," Philosophical Magazine, Series 6, Vol. 46, Oct. 1923, pp. 609-627.
3. Haigh, B. P., "The Relative Safety of Mild and High-Tensile Alloy Steels Under Alternating and Pulsating Stresses," Proceedings of the Institution of Automotive Engineers, Vol. 24, 1930, pp. 320-347.
4. rd Volume, ASTM STP 1417, W. G. Reuter and R. S. Piascik, Eds., ASTM International, West Conshohocken, PA, 2002, pp. 129-146.
5. El Haddad, M. H., Smith, K. N., and Topper, T. H., "Fatigue Crack Propagation of Short Cracks," Journal of Engineering Materials and Technology, Vol. 101, 1979, pp. 42-46.
6. nd International Conference on Mechanical Behaviour of Materials, 1976, pp. 627-630.
7. Moshier, M. A., Nicholas, T., and Hillberry, B. M., "Load History Effects on Fatigue Crack Growth Threshold for Ti-6Al-4V and Ti-17 Alloys," International Journal of Fatigue, Vol. 23, 2001, pp. S253-S258.
8. Hutson, A. L., Neslen, C., and Nicholas, T., "Characterization of Fretting Fatigue Crack Initiation Processes in Ti-6Al-4V," Tribology International, Vol. 36, 2003, pp. 133-143.
9. Golden, P. J., Bartha, B. B., Grandt, Jr., A. F., and Nicholas, T., "Measurement of the Fatigue Crack Propagation Threshold of Fretting Cracks in Ti-6Al-4V," International Journal of Fatigue, Vol. 26, 2004, pp. 281-288.
10. th Volume, ASTM STP 1321, T. L. Panontin and S. D. Sheppard, Eds., ASTM International, West Conshohocken, PA, 1999, pp. 626-641.
11. st Volume, ASTM STP 1389, G. R. Halford and J. P. Gallagher, Eds., ASTM International, West Conshohocken, PA, 2000, pp. 427-444.
12. Gallagher J. P., et al., AFRL-ML-TR-2001-4159, Improved High-Cycle Fatigue (HCF) Life Prediction, Wright-Patterson Air Force Base, OH, January 2001.
13. Hartman, G. A., "Infrared Damage Detection System (IDDS) for Real-Time, Small-Scale Damage Monitoring," Proceedings of SEM Annual Conference on Experimental Mechanics, Charlotte, NC, 2003, in press.
14. Nicholas, T., "Step Loading, Coaxing and Small Crack Thresholds in Ti-6Al-4V under High Cycle Fatigue," Fatigue - David L Davidson Symposium, K. S. Chan, P. K. Liaw, R. S. Bellows, T. C. Zogas, and W. O. Soboyejo, Eds., Cleveland: TMS (The Minerals, Metals & Materials Society), 2002, pp. 91-106.
15. Schütz, W., "A History of Fatigue," Engineering Fracture Mechanics, Vol. 54, 1996, pp. 263-300.
16. Moshier, M. A., "The Effect of Low Cycle Fatigue Cracks and Loading History on High Cycle Fatigue Threshold," Ph.D. Dissertation, Purdue University, 2000.
17. Golden, P. J., "High Cycle Fatigue of Fretting Induced Cracks, " Ph.D. dissertation, Purdue University, 2001.
18. Russ, S. M., "Effect of Underloads on Fatigue Crack Growth of Ti-17," Ph.D. Dissertation, Georgia Institute of Technology, October 2003.