Finite element simulation of the failure process of single fiber composites considering interface properties

Author keywords

A. Polymer matrix composites; B. Fracture; B. Interface; C. Finite element analysis

Indexed keywords

COHESIVE ELEMENT; DAMAGE INITIATION; DEGRADATION FACTOR; FAILURE MODEL; FAILURE PROCESS; FINITE ELEMENT SIMULATIONS; INTERFACE PROPERTY; MATRIX CRACKING; SINGLE FIBER COMPOSITE; UNIAXIAL TENSILE;

EID: 84869501138     PISSN: 13598368     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesb.2012.07.051     Document Type: Article
Times cited : (43)

References (31)
  • 1
    • 0025958106 scopus 로고
    • Exact theory of fiber fragmentation in a single-filament composite
    • W.A. Curtin Exact theory of fiber fragmentation in a single-filament composite J Mater Sci 26 1991 5239 5253
    • (1991) J Mater Sci , vol.26 , pp. 5239-5253
    • Curtin, W.A.1
  • 2
    • 48249085345 scopus 로고    scopus 로고
    • Micromechanics of the fragmentation process in single-fiber composites
    • M. Nishikawa, T. Okabe, N. Takeda, and W.A. Curtin Micromechanics of the fragmentation process in single-fiber composites Model Simul Mater Sci Eng 16 2008 055009
    • (2008) Model Simul Mater Sci Eng , vol.16 , pp. 055009
    • Nishikawa, M.1    Okabe, T.2    Takeda, N.3    Curtin, W.A.4
  • 3
    • 77956667859 scopus 로고    scopus 로고
    • Stochastic damage evolution and failure in fiber-reinforced composites
    • W.A. Curtin Stochastic damage evolution and failure in fiber-reinforced composites Adv Appl Mech 36 1999 163 253
    • (1999) Adv Appl Mech , vol.36 , pp. 163-253
    • Curtin, W.A.1
  • 4
    • 33745613745 scopus 로고
    • Tensile properties of fiber-reinforced metals copper/tungsten and copper/molybdenum
    • A. Kelly, and W.R. Tyson Tensile properties of fiber-reinforced metals copper/tungsten and copper/molybdenum J Mech Phys Solids 13 1965 329 350
    • (1965) J Mech Phys Solids , vol.13 , pp. 329-350
    • Kelly, A.1    Tyson, W.R.2
  • 5
    • 0020782535 scopus 로고
    • Adhesion of graphite fibers to epoxy matrics: I. The role of fiber surface treatment
    • L.T. Drzal, M.J. Rich, and P.F. Loyd Adhesion of graphite fibers to epoxy matrics: I. The role of fiber surface treatment J Adhesion 16 1983 1 30
    • (1983) J Adhesion , vol.16 , pp. 1-30
    • Drzal, L.T.1    Rich, M.J.2    Loyd, P.F.3
  • 6
    • 0020832067 scopus 로고
    • Evaluation of surface treatments for fibers in composite materials
    • W.A. Frazer, F.H. Ancker, A.T. Dibenedetto, and B. Elbirli Evaluation of surface treatments for fibers in composite materials Polym Compos 4 1983 238 248
    • (1983) Polym Compos , vol.4 , pp. 238-248
    • Frazer, W.A.1    Ancker, F.H.2    Dibenedetto, A.T.3    Elbirli, B.4
  • 7
    • 0000085933 scopus 로고
    • Stress transfer in single fiber/resin tensile test
    • W.D. Bascom, and R.M. Jensen Stress transfer in single fiber/resin tensile test J Adhesion 19 1986 219 239
    • (1986) J Adhesion , vol.19 , pp. 219-239
    • Bascom, W.D.1    Jensen, R.M.2
  • 9
    • 0033742067 scopus 로고    scopus 로고
    • Finite element analysis of the effect of fibre shape on stresses in an elastic fibre surrounded by a plastic matrix
    • K.L. Goh, R.M. Aspden, K.J. Mathias, and D.W.L. Hukins Finite element analysis of the effect of fibre shape on stresses in an elastic fibre surrounded by a plastic matrix J Mater Sci 35 2000 2493 2497
    • (2000) J Mater Sci , vol.35 , pp. 2493-2497
    • Goh, K.L.1    Aspden, R.M.2    Mathias, K.J.3    Hukins, D.W.L.4
  • 10
    • 2342447654 scopus 로고    scopus 로고
    • The effect of matrix plasticity on the stress fields in a single filament composite and the value of interfacial shear strength obtained from the fragmentation test
    • D. Tripathi, F.P. Chen, and F.R. Jones The effect of matrix plasticity on the stress fields in a single filament composite and the value of interfacial shear strength obtained from the fragmentation test Proc Roy Soc Lond A 452 1996 621 653
    • (1996) Proc Roy Soc Lond A , vol.452 , pp. 621-653
    • Tripathi, D.1    Chen, F.P.2    Jones, F.R.3
  • 11
    • 0033684651 scopus 로고    scopus 로고
    • The progressional approach to interfacial failure in carbon reinforced composites: Elasto-plastic finite element modeling of interface cracks
    • R.B. Nath, D.N. Fenner, and C. Galiotis The progressional approach to interfacial failure in carbon reinforced composites: elasto-plastic finite element modeling of interface cracks Composites: Part A 31 2000 929 943
    • (2000) Composites: Part A , vol.31 , pp. 929-943
    • Nath, R.B.1    Fenner, D.N.2    Galiotis, C.3
  • 12
    • 0034326017 scopus 로고    scopus 로고
    • Matrix crack propagation criteria for model short-carbon fibre/epoxy composites
    • S. Sirivedin, D.N. Fenner, R.B. Nath, and C. Galiotis Matrix crack propagation criteria for model short-carbon fibre/epoxy composites Compos Sci Technol 60 2000 2835 2847
    • (2000) Compos Sci Technol , vol.60 , pp. 2835-2847
    • Sirivedin, S.1    Fenner, D.N.2    Nath, R.B.3    Galiotis, C.4
  • 13
    • 0035281708 scopus 로고    scopus 로고
    • Fibre/matrix stress transfer through a discrete interphase. Part1: Single-fibre model composites
    • S.A. Hayes, R. Lane, and F.R. Jones Fibre/matrix stress transfer through a discrete interphase. Part1: single-fibre model composites Composites: Part A 32 2001 379 389
    • (2001) Composites: Part A , vol.32 , pp. 379-389
    • Hayes, S.A.1    Lane, R.2    Jones, F.R.3
  • 14
    • 0037067221 scopus 로고    scopus 로고
    • Micromechanical analysis of internal stress development during single-fibre fragmentation testing of Ti/SiCf
    • G. Rauchs, M. Preuss, and P.J. Withers Micromechanical analysis of internal stress development during single-fibre fragmentation testing of Ti/SiCf Acta Mater 50 2002 2477 2490
    • (2002) Acta Mater , vol.50 , pp. 2477-2490
    • Rauchs, G.1    Preuss, M.2    Withers, P.J.3
  • 15
    • 2342442924 scopus 로고    scopus 로고
    • Review: Finite element analysis of stress transfer in short-fiber composite materials
    • K.L. Goh, R.M. Aspden, and D.W.L. Hukins Review: finite element analysis of stress transfer in short-fiber composite materials Compos Sci Technol 64 2004 1091 1100
    • (2004) Compos Sci Technol , vol.64 , pp. 1091-1100
    • Goh, K.L.1    Aspden, R.M.2    Hukins, D.W.L.3
  • 16
    • 32344449584 scopus 로고    scopus 로고
    • Phase-stepping photoelasticity for the measurement of interfacial shear stress in single fibre composites
    • F.M. Zhao, S.A. Hayes, E.A. Patterson, and F.R. Jones Phase-stepping photoelasticity for the measurement of interfacial shear stress in single fibre composites Composites: Part A 37 2006 216 221
    • (2006) Composites: Part A , vol.37 , pp. 216-221
    • Zhao, F.M.1    Hayes, S.A.2    Patterson, E.A.3    Jones, F.R.4
  • 17
    • 33746333564 scopus 로고    scopus 로고
    • Influence of a matrix crack on stress transfer to an alumina fiber in epoxy resin using FEA and photoelasticity
    • A.C. Johnson, F.M. Zhao, S.A. Hayes, and F.R. Jones Influence of a matrix crack on stress transfer to an alumina fiber in epoxy resin using FEA and photoelasticity Compos Sci Technol 66 2006 2023 2029
    • (2006) Compos Sci Technol , vol.66 , pp. 2023-2029
    • Johnson, A.C.1    Zhao, F.M.2    Hayes, S.A.3    Jones, F.R.4
  • 18
    • 77958459720 scopus 로고    scopus 로고
    • Automatic generation of random distribution of fibers in long-fiber-reinforced composites and mesomechanical simulation
    • Zhenqing Wang, Xiaoqiang Wang, Jifeng Zhang, Wenyan Liang, and Limin Zhou Automatic generation of random distribution of fibers in long-fiber-reinforced composites and mesomechanical simulation Mater Design 32 2011 885 891
    • (2011) Mater Design , vol.32 , pp. 885-891
    • Wang, Z.1    Wang, X.2    Zhang, J.3    Liang, W.4    Zhou, L.5
  • 20
    • 0030291888 scopus 로고    scopus 로고
    • A criterion for crack initiation in glassy polymers subjected to a composite like stress state
    • L.E. Asp, L.A. Berglund, and R. Talreja A criterion for crack initiation in glassy polymers subjected to a composite like stress state Compos Sci Technol 56 1996 1089 1301
    • (1996) Compos Sci Technol , vol.56 , pp. 1089-1301
    • Asp, L.E.1    Berglund, L.A.2    Talreja, R.3
  • 21
    • 0035438039 scopus 로고    scopus 로고
    • A new static failure criterion for isotropic polymers
    • H. Altenbach, and K. Tushtev A new static failure criterion for isotropic polymers Mech Compos Mater 37 2001 5 6
    • (2001) Mech Compos Mater , vol.37 , pp. 5-6
    • Altenbach, H.1    Tushtev, K.2
  • 22
    • 0027611074 scopus 로고
    • Modelling damage in a plain weave fabric reinforced composite materials
    • D. Blackketter, D.E. Walrath, and A.C. Hansen Modelling damage in a plain weave fabric reinforced composite materials J Compos Technol Res 15 1993 136 142
    • (1993) J Compos Technol Res , vol.15 , pp. 136-142
    • Blackketter, D.1    Walrath, D.E.2    Hansen, A.C.3
  • 23
    • 0037237627 scopus 로고    scopus 로고
    • Strength simulation of woven fabric composite materials with material non-linearity using micromechanics based model
    • A. Tabiei, G. Song, and Y. Jiang Strength simulation of woven fabric composite materials with material non-linearity using micromechanics based model J Thermoplast Compos 16 2003 5 20
    • (2003) J Thermoplast Compos , vol.16 , pp. 5-20
    • Tabiei, A.1    Song, G.2    Jiang, Y.3
  • 24
    • 79951682874 scopus 로고    scopus 로고
    • Silberschmidt. Interaction of matrix cracking and delamination in cross-ply laminates: Simulations with stochastic cohesive zone elements
    • Zahid R. Khokhar, Ian A. Ashcroft, and V. Vadim Silberschmidt. Interaction of matrix cracking and delamination in cross-ply laminates: simulations with stochastic cohesive zone elements Appl Compos Mater 18 2011 3 16
    • (2011) Appl Compos Mater , vol.18 , pp. 3-16
    • Khokhar, Z.R.1    Ashcroft, I.A.2    Vadim, V.3
  • 25
    • 28344433037 scopus 로고    scopus 로고
    • Delamination modelling in a double cantilever beam
    • M. Meo, and M.J. Thieulot Delamination modelling in a double cantilever beam Compos Struct 71 2005 429 434
    • (2005) Compos Struct , vol.71 , pp. 429-434
    • Meo, M.1    Thieulot, M.J.2
  • 26
    • 76549104214 scopus 로고    scopus 로고
    • Numerical simulation of the fiber fragmentation process in single-fiber composites
    • Xiaohong Wang, Boming Zhang, Shanyi Du, Yufen Wu, and Xinyang Sun Numerical simulation of the fiber fragmentation process in single-fiber composites Mater Design 31 2010 2464 2470
    • (2010) Mater Design , vol.31 , pp. 2464-2470
    • Wang, X.1    Zhang, B.2    Du, S.3    Wu, Y.4    Sun, X.5
  • 27
    • 70450222915 scopus 로고    scopus 로고
    • Effects of interphase material properties in unidirectional fibre reinforced composites
    • A.R. Maligno, N.A. Warrior, and A.C. Long Effects of interphase material properties in unidirectional fibre reinforced composites Compos Sci Technol 70 2010 36 44
    • (2010) Compos Sci Technol , vol.70 , pp. 36-44
    • Maligno, A.R.1    Warrior, N.A.2    Long, A.C.3
  • 28
    • 0032468084 scopus 로고    scopus 로고
    • A novel axisymmetric variational analysis of stress transfer into fibres through a partially debonded interface
    • W. Wu, I. Verpoest, and J. Varna A novel axisymmetric variational analysis of stress transfer into fibres through a partially debonded interface Compos Sci Technol 58 1998 1863 1877
    • (1998) Compos Sci Technol , vol.58 , pp. 1863-1877
    • Wu, W.1    Verpoest, I.2    Varna, J.3
  • 30
    • 41249099986 scopus 로고    scopus 로고
    • Determination of interface properties from experiments on the fragmentation process in single-fiber composites
    • M. Nishikawa, T. Okabe, and N. Takeda Determination of interface properties from experiments on the fragmentation process in single-fiber composites Mater Sci Eng A 2008 549 557
    • (2008) Mater Sci Eng A , pp. 549-557
    • Nishikawa, M.1    Okabe, T.2    Takeda, N.3
  • 31
    • 79953161172 scopus 로고    scopus 로고
    • Effects of interphase properties in unidirectional fiber reinforced composite materials
    • Xiaoqiang Wang, Jifeng Zhang, and Zhenqing. Wang Effects of interphase properties in unidirectional fiber reinforced composite materials Mater Design 32 2011 3486 3492
    • (2011) Mater Design , vol.32 , pp. 3486-3492
    • Wang, X.1    Zhang, J.2    Wang, Z.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.