Deterioration mechanism of cementitious materials under acid rain attack

Engineering Failure Analysis

Volumn 27, Issue , 2013, Pages 272-285

  Chen, Meng Cheng ^a   Wang, Kai ^a   Xie, Li ^a  

^a EAST CHINA JIAOTONG UNIVERSITY   (China)

Author keywords

Acid rain attack; Cementitious material; Deterioration mechanism; Experimental analysis

Indexed keywords

CEMENT HYDRATION; CEMENTITIOUS MATERIALS; DETERIORATION MECHANISM; ENERGY DISPERSIVE X-RAY; ETTRINGITES; EXPERIMENTAL ANALYSIS; FOURIER TRANSFORM INFRARED; MINERALOGICAL COMPOSITIONS; PURE CHEMICALS; SIMULATED ACID RAIN SOLUTIONS; TIME-PERIODS;

ACID RAIN; CALCIUM SILICATE; HYDRATION; MATERIALS; NITRIC ACID; SCANNING ELECTRON MICROSCOPY; X RAY DIFFRACTION;

DETERIORATION;

EID: 84867621876     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2012.08.007     Document Type: Article

References (27)

1. Wang X.Y., Li Z.J. The research progress of life prediction used in concrete. J Build Mater 1999, 2(3):249-256. [in Chinese].
2. Zhang X.Y., An B.G., et al. Present research situation on the corrosion and erosion of materials by acid rain attack. Corros Sci Protect Technol 2002, 14(3):157-160. [in Chinese].
3. Eney A.B., Petzold D.E. The problem of acid rain: an overview. Environment 1987, 7(7):95-103.
4. Mansfeld F., Vijayakumar R. Atmospheric corrosion behavior in Southern California. Corros Sci 1988, 28(9):939-946.
5. Larssen T., Seip H.M., Semb A., Mulder J., et al. Acid deposition and its effects in China: an overview. Environ Sci Policy 1999, 2:9-24.
6. Hill J., et al. An experimental study of combined acid and sulfate attack of concrete. Cem Concr Compos 2003, 25:997-1003.
7. Okochi H., Kameda H., Hasegawa S., Saito N., Kubota K., Igawa M. Deterioration of concrete structures by acid deposition - an assessment of the role of rainwater on deterioration by laboratory and field exposure experiments using mortar specimens. Atmos Environ 2000, 34:2937-2945.
8. Zivica V., Bajza A. Acidic attack of cement based materials - a review part 1. Principle of acidic attack. Constr Build Mater 2001, 15:331-340.
9. Gregerova M., Vsiansky D. Identification of concrete deteriorating minerals by polarizing and scanning electron microscopy. Mater Charact 2009, 60:680-685.
10. Xie S.D., Qi L., Zhou D. Investigation of the effects of acid rain on the deterioration of cement concrete using accelerated tests established in laboratory. Atmos Environ 2004, 38:4457-4466.
11. Xiao J., Zhou S.J. Effect of low-calcium fly ash on cement mortar strength in acid rain condition. J Build Mater 2005, 8(4):840-845. [in Chinese].
12. Hu X. Analysis for simulation test on acid rain attacking concrete. J Chin Ceram Soc 2008, 36(Suppl.):147-152. [in Chinese].
13. Fan Y.F., et al. Deterioration of compressive property of concrete under simulated acid rain environment. Constr Build Mater 2010, 24:1975-1983.
14. Han T.C., Wang H.Q. Application of thermal mechanics into studies on concrete corrosion. J Jiaozuo Inst Technol 1997, 16(4):65-70. [in Chinese].
15. Wei Y.Y., Luo J., et al. Study of acid corrosion of cement mortar I: experiment on still acid solution corrosion. J Ceram Soc 1998, 26(4):417-423. [in Chinese].
16. Chen Q., Zhu B.L. A thermal study of concrete corrosion by underground water attack. China Railway Sci 2003, 24(6):57-60. [in Chinese].
17. Hu X.B., Hou X.Y., et al. Analysis of hardened cement paste compositions by acid rain attack. Railway Sci Eng 2007, 4(4):47-51. [in Chinese].
18. Chen J.X., Wu J.C., Chen H.B. Survey of the durability of building in severe acid rain circumstance. Concrete 2001, 145(11). [in Chinese].
19. Zhao Y.X., Hou Q. The variation characteristics and formation analysis of acid rain in China during 1993-2006. Acta Meteor Sinica 2008, 66:1032-1042.
20. Zhang L. The mechanism and key factors of sulfate attack on concrete. Northeast Roads 1998, 21(4):90-92.
21. Bensted J. Thaumasite-direct, woodfordite and other possible formation routes. Cem Concr Compos 2003, 25:873-877.
22. Ma B.G., Gao X.J., Byars W.A. Thaumasite formation in a tunnel of Bapanxia Dan in Western China. Cem Concr Res 2006, 36(5):716-722. [in Chinese].
23. Yuan R.Z. Cementitious material science 2000, Wuhan University of Technology Press, Wuhan, [in Chinese].
24. Barnes P., et al. The Structures and properties of cement, translated by Wu ZQ 1991, China Building and Industry Press, Beijing.
25. Wang K., Ma B.G., Long S.Z. Acid rain attack on different variety of cement concrete. J Wuhan Univ Technol 2009, 31(2):1-4. [in Chinese].
26. Shi C.J., Stegemann J.A. Acid corrosion resistance of different cementing materials. Cem Concr Res 2000, 25:803-808.
27. Jahani F., Devinny J., et al. Investigations of sulfuric acid corrosion of concrete [J]. Cem Concr Res 1995, 22(3):1125-1136.