Study on cracking mechanism of laser clad NiCrBSi coating

Shanghai Jiaotong Daxue Xuebao/Journal of Shanghai Jiaotong University

Volumn 46, Issue 7, 2012, Pages 1043-1048

  Yu, Ting ^a,b   Deng, Qi Lin ^a   Zhang, Wei ^c   Dong, Gang ^d   Yang, Jian Guo ^a  

^a SHANGHAI JIAO TONG UNIVERSITY   (China)

^b NANCHANG UNIVERSITY   (China)

^c Shanghai Institute of Laser Technology   (China)

^d TONGJI UNIVERSITY   (China)

Author keywords

Crack; Hard phase; Laser cladding; Nickel based alloy

Indexed keywords

CHEMICAL COMPOSITIONS; COOLING PROCESS; CRACK BEHAVIOR; CRACK SOURCES; CRACKING MECHANISMS; FRACTURE SECTION; HARD PHASE; HOT CRACKS; METAL MATRICES; NICKEL BASED ALLOY; NICRBSI COATINGS; THERMAL EXPANSION COEFFICIENTS;

BRITTLE FRACTURE; CRACKS; FRACTURE MECHANICS; GRAIN BOUNDARIES; LASER CLADDING; LIQUID FILMS; MICROSTRUCTURE; SLAGS; SOURCE SEPARATION;

COATINGS;

EID: 84866295668     PISSN: 10062467     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (11)

1. 3) [J]. Surface & Coatings Technology, 2009, 203 (16): 2292-2299.
2. Zhang Y K, Chen J F, Lei W N, et al. Effect of laser surface melting on friction and wear behavior of AM50 magnesium alloy [J]. Surface & Coatings Technology, 2008, 202 (14): 3175-3179.
3. 2 laser cladding [J]. Appled Lasers, 1999, 49(5): 193-197+200.
4. CHEN Jing, LIN Xin, WANG Tao, et al. The hot cracking mechanism of 316L stainless steel cladding in rapid laser forming process [J]. Rare Metal Materials and Engineering, 2003, 32(3): 183-186.
5. Zhou S F, Zeng X Y, Hu Q W, et al. Analysis of crack behavior for Ni-based WC composite coatings by laser cladding and crack-free realization [J]. Applied Surface Science, 2008, 255 (5): 1646-1653.
6. Liu S L, Zheng X P, Geng G Q. Dry sliding wear behavior and corrosion resistance of NiCrBSi coating deposited by activated combustion-high velocity air fuel spray process [J]. Materials & Design, 2010, 31 (2): 913-917.
7. Zhao H Y, Zhang H T, Xu C H, et al. Temperature and stress fields of multi-track laser cladding [J]. Transactions of Nonferrous Metals Society of China, 2009, 19: S495-S501.
8. Xu G J, Kutsuna M, Liu Z J, et al. Characteristics of Ni-based coating layer formed by laser and plasma cladding processes [J]. Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2006, 417 (1-2): 63-72.
9. Gonzalez R, Garcia M A, Penuelas I, et al. Microstructural study of NiCrBSi coatings obtained by different processes [C]//16th International Conference on Wear of Materials. Montreal: [s.n.], 2007: 619-624.
10. Hernandez J, Vannes A. Laser surface cladding and residual stress [C]//Proc 3rd Inter Conf on laser in Manufacturing. Paris: [s.n.], 1986: 181-189.
11. Dahotre N B, Kadolkar P B, Watkins T R, et al. State of residual stress in laser-deposited ceramic composite coatings on aluminum alloys [J]. Acta Materialia, 2007, 55 (4): 1203-1214.