Corrosion behaviour and crack formation mechanism of basalt fibre in sulphuric acid

Corrosion Science

Volumn 64, Issue , 2012, Pages 1-7

  Nasir, V ^a   Karimipour, H ^a   Taheri Behrooz, F ^a   Shokrieh, M M ^a  

^a IRAN UNIVERSITY OF SCIENCE AND TECHNOLOGY   (Iran)

Author keywords

A. Sulphuric acid; B. SEM; C. Acid corrosion

Indexed keywords

ACID CORROSION; AXIAL CRACKS; CORROSION BEHAVIOUR; CRACK FORMATION MECHANISMS; E-GLASS; EXPOSURE TIME; FIBRE SURFACES; FRACTURE MECHANISMS; STRENGTH DEGRADATION;

BASALT; CORROSIVE EFFECTS; DEGRADATION; GLASS FIBERS; LEACHING; SULFURIC ACID;

FIBERS;

EID: 84865959038     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2012.06.028     Document Type: Article

References (23)

1. Myers T.J., Kytomaa H.K., Smith T.R. Environmental stress-corrosion cracking of fibreglass: lessons learned from failures in the chemical industry. Journal of Hazardous Material 2007, 142:695-704.
2. Farshad M., Necola A. Strain corrosion of glass fibre-reinforced plastics pipes. Polymer Testing 2004, 23:517-521.
3. Hogg P.J., Hull D., Spencer B. Stress and strain corrosion of glass reinforced plastics. Composite 1981, 166-172.
4. Hogg P.J. Factors affecting the stress corrosion of GRP in acid environments. Composite 1983, 14:254-261.
5. Megel M., Kumosa L., Ely T., Armentrout D., Kumosa M. Initiation of stress-corrosion cracking in unidirectional glass/polymer composite materials. Composites Science and Technology 2001, 61:231-246.
6. Ely T., Armentrout D., Kumosa M. Evaluation of stress corrosion properties of pultruded glass fibre/polymer composite materials. Journal of Composite Materials 2001, 35:751-773.
7. Kumosa L., Armentrout D., Kumosa M. An evaluation of the critical conditions for the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites. Composites Science and Technology 2001, 61:615-623.
8. Kumosa L., Kumosa M., Armentrout D. Resistance to stress corrosion cracking of unidirectional ECR-glass/polymer composites for high voltage composite insulator applications. Composites Part A 2003, 34:1-15.
9. Kumosa L., Armentrout D., Kumosa M. The effect of sandblasting on the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites used in high voltage composite (non-ceramic) insulators. Composites Science and Technology 2002, 62:1999-2015.
10. Ely T., Kumosa M. The stress corrosion experiments on an E-Glass/epoxy unidirectional composite. Journal of Composite Materials 2000, 34:841-878.
11. Akdemir A., Tarakcioglu N., Avci A. Stress corrosion crack growth in glass/polyester composites with surface crack. Composite Part B 2001, 32:123-129.
12. Price J.N., Hull D. Effect of matrix toughness on crack propagation during stress corrosion of glass reinforced composites. Composites Science and Technology 1987, 28:193-210.
13. Sapalidis S.N., Hogg P.J., Youd S.J. High temperature acidic stress corrosion of glass fibre composites, Part I effect of fibre type. Journal of Materials Science 1997, 32:309-316.
14. Qiu Q., Kumosa M. Corrosion of E-glass fibres in acidic environments. Composites Science and Technology 1997, 57:497-507.
15. Ehrenstein G.W., Spaude R. A study of the corrosion resistance of glass fibre reinforced polymers. Composite Structures 1984, 2:191-200.
16. Shokrieh M.M., Nasir V., Karimipour H. A micromechanical study on longitudinal strength of fibrous composites exposed to acidic environment. Journal of Material Design 2012, 35:394-403.
17. Wei B., Hailin C., Shenhua S. Tensile behaviour contrast of basalt and glass fibres after chemical treatment. Journal of Material Design 2010, 31:4244-4250.
18. Carmisciano S., Maria De Rosa I., Sarasini F., Tamburrano A., Valente M. Basalt woven fibre reinforced vinylester composites: flexural and electrical properties. Journal of Material Design 2011, 32:337-342.
19. Todic A., Nedeljkovic B., Cikara D., Ristovic I. Particulate basalt-polymer composites characteristics investigation. Journal of Material Design 2011, 32:1677-1683.
20. Liu Q., Shaw M.T., Parnas R.S., McDonnell A.M. Investigation of basalt fibre composite aging behaviour for applications in transportation. Polymer Composites 2006, 27:475-483.
21. Shokrieh M.M., Memar M. Stress corrosion cracking of basalt/epoxy composites under bending loading. Applied Composite Materials 2010, 17:121-135.
22. Wei B., Cao H., Song S. Degradation of basalt fibre and glass fibre/epoxy resin composites in seawater. Corrosion Science 2011, 53:426-431.
23. Metcalfe A.G., Schmitz G.K. Mechanisms of stress corrosion in E-glass filaments. Glass Technology 1972, 13:5-16.