Low temperature heat treatment of anodic TiO 2 nanotube array thin film and their photo-electrochemical properties

Nanoscience and Nanotechnology Letters

Volumn 4, Issue 5, 2012, Pages 564-568

  Li, Hongyi ^a   Wang, Jinshu ^a   Wang, Hong ^a   Liu, Man ^a  

^a BEIJING UNIVERSITY OF TECHNOLOGY   (China)

Author keywords

Low Temperature Heat Treatment; Photo Induced Cathodic Protection; TiO 2 Nanotube

Indexed keywords

3.5%NACL; ANODIZATIONS; AQUEOUS ELECTROLYTE; NACL AQUEOUS SOLUTION; NANOTUBE ARRAYS; OPEN CIRCUIT POTENTIAL; PHOTO-INDUCED; PHOTOELECTROCHEMICAL PROPERTIES; REACTION SOLUTIONS; SOLVOTHERMAL PROCESS; SOLVOTHERMAL-ANNEALING; TIO;

CATHODIC PROTECTION; ELECTROLYTES; ETHANOL; HEAT TREATMENT; LOW TEMPERATURE OPERATIONS; SODIUM CHLORIDE; TEMPERATURE; THIN FILMS; TITANIUM DIOXIDE;

NANOTUBES;

EID: 84864838033     PISSN: 19414900     EISSN: 19414919     Source Type: Journal    
DOI: 10.1166/nnl.2012.1347     Document Type: Article

References (34)

1. A. Fujishima and K. Honda, Nature 238, 37 (1972).
2. M. K. Nazeeruddin, A. Kay, I. Rodicio, R. Humphry-Baker, Müller, P. Liska, N. Vlachopoulos, and M. Grüatzel, J. Am. Chem. Soc. 115, 6382 (1993).
3. H. E. Hager and J. A. Belko, Sens. Actua. 8, 161 (1985).
4. T. Takeuchi, Sens. Actua. 14, 109 (1988).
5. K. Kajihara and T. Yao, Phys. Chem. Chem. Phys. 1, 1979 (1999).
6. W. Choi, S. J. Hong, Y. S. Chang, and Y. Cho, Environ. Sci. Technol. 34, 3810 (2000).
7. T. M. Wang, H. Y. Wang, P. Xu, X.-C. Zhao, Y.-L. Liu, and S. Chao, Thin Solid Films 334, 103 (1998).
8. M. Adachi, Y. Murata, and S. Yoshikawa, Chem. Lett. 8, 942 (2000).
9. G. K. Mor, K. Shankar, M. Paulose, O. K. Varghese, and C. A. Grimes, Nano Lett. 5, 191 (2005).
10. S. Uchida, R. Chiba, M. Tomiha, N. Masaki, and M. Shirai, Electrochemistry 70, 418 (2002).
11. G. K. Mor, K. Shankar, M. Paulose, O. K. Varghese, and C. A. Grimes, Nano Lett. 6, 215 (2006).
12. R. Beranek, H. Tsuchiya, T. Sugishima, J. M. Macak, L. Taveira, S. Fujimoto, H. Kisch, and P. Schmuki, Appl. Phys. Lett. 87, 243114 (2005).
13. G. K. Mor, J. Basham, M. Paulose, S. Kin, O. K. Varghese, A. Vaish, S. Yoriya, and C. A. Grimes, Nano Lett. 10, 2387 (2010).
14. R. A. Caruso, J. H. Schattka, and A. Greiner, Adv. Mater. 13, 1577 (2001).
15. D. L. Ma, L. S. Schadler, R. W. Siegel, and J. II. Hong, Appl. Phys. Lett. 83, 1839 (2003).
16. M. Adachi, Y. Murata, M. Harada, and S. Yoshikawa, Chem. Lett. 8, 942 (2000).
17. T. Kasuga, M. Hiramatsu, A. Hoson , T. Sekino, and K. Niihara, Adv. Mater. 11, 1307 (1999).
18. D. Gong, C. A. Grimes, O. K. Varghese, W. Hu, R. H. Singh, Z. Chen, and E. C. Dickey, J. Mater. Res. 16, 3331 (2001).
19. J. M. Macak, H. Tsuchiya, and P. Schmuki, Angew. Chem. Int. Ed. 44, 2100 (2005).
20. J. M. Macak, H. Tsuchiya, and P. Schmuki, Angew. Chem. Int. Ed. 44, 2100 (2005).
21. N. Wang, H. Y. Li, W. L. Lv, J. H. Li, J. S. Wang, Z. T. Zhang, and Y. R. Liu, Biomaterials 32, 6900 (2011).
22. O. K. Varghese, M. Paulose, and C. A. Grimes, Nat. Nanotechnol. 4, 592 (2009).
23. H. Y. Li, J. S. Wang, K. L. Huang, G. S. Sun, and M. L. Zhou, Mater. Lett. 65, 1188 (2011).
24. H. Y. Li, J. S. Wang, X. Chen, M. L. Zhou, G. S. Sun, K. L. Huang, and Q. N. Guo, Chinese J. Inorg. Chem. 26, 217 (2010).
25. H. Yun, C. J. Lin, J. Li, J. R. Wang, and H. B. Chen, Appl. Surf. Sci. 255, 2113 (2008).
26. Y. H. Wang, H. X. Yang, and H. M. Xu, Mater. Lett. 64, 164 (2010).
27. R. Liu, W. D. Yang, and L. S. Qiang, J. Power Sources 199, 418 (2012).
28. M. D. Ye, X. K. Xin, C. J. Lin, and Z. Q. Lin, Nano Lett. 11, 3214 (2011).
29. D. A. Wang, L. F. Liu, F. X. Zhang, K. Tao, E. Pippel, and K. Domen, Nano Lett. 11, 3649 (2011).
30. H. Yun, C. J. Lin, J. Li, J. R. Wang, and H. B. Chen, Appl. Surf. Sci. 255, 2113 (2008).
31. K. Yanagisawa and J. Ovenstone, J. Phys. Chem. B 103, 7781 (1999).
32. H. B.Yin, Y. Wada, T. Kitamura, S. Kambe, S. Murasawa, H. Mori, and S. Yanagida, J. Mater. Chem. 11, 1694 (2001).
33. M. P. Finnegan, H. Z. Zhang, and J. F. Banfield, J. Phys. Chem. C 111, 1962 (2007
34. A. S. Barnard and L. A. Curtiss, Nano Lett. 5, 1261 (2005).