The microstructure of annealed galfan coating on steel substrate

Archives of Metallurgy and Materials

Volumn 57, Issue 2, 2012, Pages 517-523

  Zelechower, M ^a   Klis J ^b   Augustyn, E ^a   Grzonka, J ^c   Stroz D ^d   Rzychon T ^a   Woznica H ^a  

^a SILESIAN UNIVERSITY OF TECHNOLOGY   (Poland)

^b Cognor SA ^*  (Poland)

^c INSTITUTE OF METALLURGY AND MATERIALS SCIENCE   (Poland)

^d UNIVERSITY OF SILESIA   (Poland)

Author keywords

Galfan; Heat treatment; Interface; Ternary Fe Al Zn compounds; Zinc coating

Indexed keywords

AL CONTENT; ALLOY COATINGS; ANNEALED SAMPLES; EXPERIMENTAL TECHNIQUES; GALFAN; GALFAN COATING; HOT DIPPING; LAMELLAR EUTECTIC; LOW CARBON; PHASE GRAINS; SEM/EDS; STEEL SUBSTRATE; TERNARY FE-AL-ZN COMPOUNDS; TRANSITION LAYERS; TWO-PHASE STRUCTURES; XRD , TEM;

ALUMINUM; ANNEALING; COATINGS; CORROSION RESISTANCE; HEAT TREATMENT; IRON COMPOUNDS; METAL CLADDING; MICROSTRUCTURE; ZINC; ZINC COATINGS;

INTERFACES (MATERIALS);

EID: 84864206589     PISSN: 17333490     EISSN: None     Source Type: Journal    
DOI: 10.2478/v10172-012-0054-z     Document Type: Article

References (13)

1. A.R. Marder, The metallurgy of zinc-coated steel, Progress of Materials Science 45, 191-271 (2000).
2. M. Guttmann, Y. Lepretre, A. Aubry, M-J. Roche, T. Moreau, P. Drillet, J.M. Mataigne, H. Baudin, Mechanism of the galvanizing reaction. Influence of Ti and P contents in steel and of its surface microstructure after annealing, in: GALVATECH '95, Chicago, Iron and Steel Society, 295 (1995).
3. N.Y. Tang, Modeling of enrichment in galvanized coatings, Met Mater Trans. 26A, 1669 (1995).
4. 5, Acta Cryst. B50, 313-316 (1994).
5. K. Ichiyama, J. Kobayashi, S. Sugimoto, Proceedings of 14th International Hot Dip Galvanization Conference, Munich, Zinc Development Association 9/1 (1985).
6. S.J. Makimattila, On the production possibilities ofadeep drawing quality Zn-5% Al coated steel sheet, Scan J Metall 15, 224 (1986).
7. Z.W. Chen, J.T. Gregory, R.M. Sharp, Intermetallic phases formed during hot dipping of low carbon steel in a Zn-5%Al melt at 450°C, Met Trans. 23A, 2393 (1992).
8. P.G. Caceres, C.A. Hotham, J.A. Spittle, R.D. Jones, Mechanisms of formation and growth of inter-metallic layers during hot dipping of iron in Zn-3Al and Zn-6Al baths, Mater Sci Technol 2, 871 (1986).
9. th International Hot Dip Galvanization Conference, London, Zinc Development Association, 49/I (1982).
10. J. Kliś, A. Tomaszewska, E. Augustyn, J. Grzonka, G. Moskal, H. Woźnica, M. Zelechower, Mikrostrukturaiskład chemiczny powłok typu Galfan po obróbce cieplnej, Inzynieria Materiałowa (Materials Science), 3, 174-181 (in Polish with abstract in English) (2009).
11. M. Urednicek, J.S. Kirkaldy, Mechanism of iron attack inhibition arising from additions of aluminum to liquid Zn(Fe) during galvanizing, Zeitschrift fur Metallkunde 64, 649 (1987).
12. 13 structure and its relationship to the quasihomological homeotypical structures, Zeitschrift fur Kristallogr. 209, 479-487 (1994).
13. J. Wesołowski, W. Głuchowski, L. Ciura, New lead free zinc alloy for unit mode hot - dip galvanising of steel products, Archives of Metallurgy and Materials 51, 2, 283 (2006).