Upconversion emission from Yb 3+ and Tm 3+ codoped NaYF 4 thin film prepared by thermal evaporation

Journal of Nanoscience and Nanotechnology

Volumn 11, Issue 11, 2011, Pages 9690-9692

  Jia, Zhixu ^a   Zheng, Kezhi ^a   Zhang, Daisheng ^a   Zhao, Dan ^a   Qin, Weiping ^a  

^a JILIN UNIVERSITY   (China)

Author keywords

Fluoride Film; Hexagonal NaYF4; Thermal Evaporation

Indexed keywords

ANNEALED FILMS; ANNEALING PROCESS; BULK MATERIALS; CERAMIC SUBSTRATES; CO-DOPED; HEXAGONAL NAYF4; HIGH TEMPERATURE SOLID-STATE REACTION; HIGH VACUUM; ULTRAVIOLET REGION; UP-CONVERSION EMISSION; UPCONVERSION EMISSION PROPERTIES; UPCONVERSION MECHANISMS; VISIBLE UPCONVERSION;

AMORPHOUS FILMS; EMISSION SPECTROSCOPY; THERMAL EVAPORATION; YTTERBIUM;

THIN FILMS;

EID: 84863121506     PISSN: 15334880     EISSN: None     Source Type: Journal    
DOI: 10.1166/jnn.2011.5256     Document Type: Article

References (18)

1. L. L. Wang, W. P. Qin, T. Wang, G. F. Wang, C. Y. Cao, G. D. Wei, R. Kim, D. S. Zhang, F. H. Ding, and C. F. He, J. Nanosci. Nanotechnol. 10, 1825 (2010).
2. G. F. Wang, W. P. Qin, L. L. Wang, G. D. Wei, P. F. Zhu, and R. Kim, Opt. Exp. 16, 11907 (2008).
3. H. S. Qian and Y. Zhang, Langmuir 24, 12123 (2008).
4. Y. G. Su, L. P. Li, and G. S. Li, Cryst. Growth Des. 8, 2678 (2008).
5. G. S. Yi and G. M. Chow, Chem. Mater. 19, 341 (2007).
6. Y. Wei, F. Q. Lu, X. R. Zhang, and D. P. Chen, Chem. Mater. 18, 5733 (2006).
7. C. Y. Cao, W. P. Qin, J. S. Zhang, J. S. Zhang, Y. Wang, Y. Jin, G. D. Wei, G. F. Wang, and L. L. Wang, J. Nanosci. Nanotechnol. 8, 1384 (2008).
8. G. F. Wang, W. P. Qin, J. S. Zhang, J. S. Zhang, Y. Wang, C. Y. Cao, L. L. Wang, G. D. Wei, P. F. Zhu, and R. Kim, Opt. Mater. 31, 296 (2008).
9. C. Y. Cao, W. P. Qin, J. S. Zhang, Y. Wang, G. F. Wang, G. D. Wei, P. F. Zhu, L. L. Wang, and L. Z. Jin, Opt. Commun. 281, 1716 (2008).
10. J. S. Zhang, W. P. Qin, J. S. Zhang, Y. Wang, C. Y. Cao, Y. Jin, G. D. Wei, G. F. Wang, and L. L. Wang, J. Nanosci. Nanotechnol. 8, 1388 (2008).
11. W. Chen, J. Nanosci. Nanotechnol. 8, 1019 (2008).
12. W. Chen, A. G. Joly, and J. Z. Zhang, Phys. Rev. B 64, 0412021 (2001).
13. G. S. Qin, W. P. Qin, C. F. Wu, S. H. Huang, J. S. Zhang, S. Z. Lu, D. Zhao, and H. Q. Liu, J. Appl. Phys. 93, 4328 (2003).
14. G. S. Qin, W. P. Qin, S. H. Huang, C. F. Wu, D. Zhao, B. J. Chen,S. Lu, and E. Shulin, J. Appl. Phys. 92, 6936 (2002).
15. J. S. Zhang, W. P. Qin, J. S. Zhang, Y. Wang, C. Y. Cao, Y. Jin, G. D. Wei, G. F. Wang, and L. L. Wang, J. Nanosci. Nanotechnol.8, 1258 (2008).
16. W. J. Kim, M. Nyk, and P. N. Prasad, Nanotechnology 20, 185301 (2009).
17. C. K. Lin, M. T. Berry, R. Anderson, S. Smith, and P. S. May, Chem. Mater. 21, 3406 (2009).
18. J. M. Chwalek and G. R. Paz-Pujalt, Appl. Phys. Lett. 66, 410 (1995).