Branched mesoporous Mn 3O 4 nanorods: Facile synthesis and catalysis in the degradation of methylene blue

Chemistry - A European Journal

Volumn 18, Issue 17, 2012, Pages 5319-5324

  Bai, Zhongchao ^a   Sun, Bo ^a   Fan, Na ^a   Ju, Zhicheng ^b   Li, Menghua ^a   Xu, Liqiang ^a   Qian, Yitai ^a,b  

^a SHANDONG UNIVERSITY   (China)

^b UNIVERSITY OF SCIENCE AND TECHNOLOGY OF CHINA   (China)

Author keywords

manganese; mesoporous materials; methylene blue; nanostructures; porosity

Indexed keywords

ANNEALING ATMOSPHERES; CATALYTIC DEGRADATION; EXPERIMENTAL PARAMETERS; FACILE SYNTHESIS; HYDROTHERMAL PROCESS; MEAN PORE SIZE; MESOPOROUS; METHYLENE BLUE; PEG-400; POTASSIUM PERMANGANATE; SURFACE AREA;

AROMATIC COMPOUNDS; DEGRADATION; MANGANESE OXIDE; MESOPOROUS MATERIALS; NANORODS; NANOSTRUCTURES; POLYETHYLENE GLYCOLS; POROSITY; POTASSIUM;

MANGANESE;

EID: 84859886404     PISSN: 09476539     EISSN: 15213765     Source Type: Journal    
DOI: 10.1002/chem.201102944     Document Type: Article

References (38)

1. F. Jiao, A. Harrison, A. H. Hill, P. G. Bruce, Adv. Mater. 2007, 19, 4063.
2. E. S. Toberer, T. D. Schladt, R. Seshadri, J. Am. Chem. Soc. 2006, 128, 1462.
3. Y. G. Li, B. Tan, Y. Y. Wu, Nano Lett. 2008, 8, 265.
4. Y. P. Zhai, Y. Q. Dou, X. X. Liu, S. S. Park, C. S. Ha, D. Y. Zhao, Carbon 2011, 49, 545.
5. B. Z. Tian, X. Y. Liu, B. Tu, C. Z. Yu, J. Fan, L. M. Wang, S. H. Xie, G. D. Stucky, D. Y. Zhao, Nat. Mater. 2003, 2, 159.
6. S. R. Gajjela, K. Ananthanarayanan, C. Yap, M. Gratzelc, P. Balaya, Energy Environ. Sci. 2010, 3, 838.
7. Y. Liu, W. W. Zhao, X. G. Zhang, Electrochim. Acta 2008, 53, 3296.
8. C. L. Xu, Y. Q. Zhao, G. W. Yang, F. S. Lia, H. H. Li, Chem. Commun. 2009, 7575.
9. G. X. Wang, H. Liu, J. Horvat, B. Wang, S. Z. Qiao, J. Park, H. A. Highly, Chem. Eur. J. 2010, 16, 11020.
10. F. Jiao, J. C. Jumas, M. Womes, A. V. Chadwick, A. Harrison, P. G. Bruce, J. Am. Chem. Soc. 2006, 128, 12905.
11. J. Yang, J. J. Peng, R. X. Zou, F. Peng, H. J. Wang, H. Yu, J. Y. Lee, Nanotechnol. 2008, 19, 255603.
12. C. C. Yu, X. P. Dong, L. L. Guo, J. T. Li, F. Qin, L. X. Zhang, J. L. Shi, D. S. Yan, J. Phys. Chem. C. 2008, 112, 13378.
13. J. P. Xie, Q. B. Zhang, W. J. Zhou, J. Y. Lee, D. I. C. T. Wang, Langmuir 2009, 25, 6454.
14. S. Pruneanu, L. Olenic, S. A. F. Al-Said, G. Borodi, A. Houlton, B. R. Horrocks, J. Mater. Sci. 2010, 45, 3151-3159.
15. C. C. Yu, L. X. Zhang, J. L. Shi, J. J. Zhao, J. H. Gao, D. S. Yan, Adv. Funct. Mater. 2008, 18, 1544.
16. L. P. Zhu, G. H. Liao, Y. Yang, H. M. Xiao, J. F. Wang, S. Y. Fu, Nanoscale Res. Lett. 2009, 4, 550.
17. Z. H. Yang, W. X. Zhang, Q. Wang, X. M. Song, Y. T. Qian, Chem. Phys. Lett. 2006, 418, 46.
18. L. C. Zhang, Q. Zhou, Z. H. Liu, X. D. Hou, Y. B. Li, L. Yi, Chem. Mater. 2009, 21, 5066.
19. P. Li, C. Y. Nan, Z. Wei, J. Lu, Q. Peng, Y. D. Li, Chem. Mater. 2010, 22, 4232.
20. H. L. Wang, L. F. Cui, Y. Yang, H. S. Casalongue, J. T. Robinson, Y. Y. Liang, Y. Cui, H. J. Dai, J. Am. Chem. Soc. 2010, 132, 13978.
21. H. Einaga, S. Futamura, J. Catal. 2004, 227, 304.
22. X. Q. Li, L. P. Zhou, J. Gao, H. Miao, H. Zhang, J. Xu, Powder Technol. 2009, 190, 324.
23. W. M. Wang; Y. N. Yang, J. Y. Zhang, Appl. Catal. A 1995, 133, 81.
24. P. K. Sharma, M. S. Whittingham, Mater. Lett. 2001, 48, 319.
25. L. Hernan, J. Morales, J. L. Tirado, Surf. Coat. Technol. 1986, 27, 343.
26. A. Vinu, P. D. Sawant, K. Ariga, M. Hartmann, S. B. Halligudi, Microporous Mesoporous Mater. 2005, 80, 195.
27. Z. H. Wang, L. L. Wang, H. Wang, Cryst. Growth Des. 2008, 8, 4415.
28. D. S. Zhang, H. X. Fu, L. Y. Shi, C. S. Pan, Q. Li, Y. L. Chu, W. J. Yu, Inorg. Chem. 2007, 46, 2446.
29. Z. Q. Li, Y. J. Xiong, Y. Xie, Inorg. Chem. 2003, 42, 8105.
30. Y. Zeng, T. Zhang, L. J. Wang, R. Wang, J. Phys. Chem. C. 2009, 113, 3442-3448.
31. O. P. Ferreira, L. Otubo, R. Romano, O. L. Alves, Cryst. Growth Des. 2006, 6, 601.
32. T. Gao, Norby. F. Krumeich, H. Okamoto, R. Nesper, H. Fjellvåg, J. Phys. Chem. C. 2010, 114, 922.
33. P. Q. Zhang, Y. G. Zhan, B. X. Cai, C. C. Hao, J. Wang, C. X. Liu, Z. J. Meng, Z. L. Yin, Q. Y. Chen, Nano Res. 2010, 3, 235.
34. W. X. Zhang, Z. G. Yang, X. Wang, Y. C. Zhang, X. G. Wen, S. H. Yang, Catal. Commun. 2006, 7, 408.
35. Z. H. Yang, Y. C. Zhang, W. X. Zhang, X. Wang, Y. T. Qian, X. G. Wen, S. H. Yang, J. Solid State Chem. 2006, 179, 679.
36. Q. Fan, M. S. Whittingham, Electrochem. Solid-State Lett. 2007, 10, A 48.
37. Q. Hao, L. Q. Xu, G. D. Li, Z. C. Ju, C. H. Sun, H. Y. Ma, Y. T. Qian, J. Alloys Compd. 2011, 509, 6217.
38. F. Y. Cheng, H. B. Wang, Z. Q. Zhu, Y. Wang, T. R. Zhang, Z. L. Tao, J. Chen, Energy Environ. Sci. 2011, 4, 3668.