When undercover agents can't stand the heat: Coatings in action and the netherworld of corrosion under insulation

Journal of Protective Coatings and Linings

Volumn 29, Issue 2, 2012, Pages 24-43

  O'Donoghue, Mike ^a   Datta, Vijay ^a   Andrews, Adrian ^a   Adlem, Sean ^a   Giardina, Matthew ^a   De Varennes, Nicole ^b   Lachat, Damien ^b   Johnson, Bill ^c  

^a International Paint Ltd   (United Kingdom)

^b RAE Engineering and Inspection Ltd   (United States)

^c AScT Acuren Group Inc   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ANTI-CORROSION PROPERTY; CORROSION UNDER INSULATIONS; CYCLIC TESTING; CYCLIC TESTS; LABORATORY TEST; PLACING THERMOCOUPLES; POTENTIAL FAULTS; SODIUM CHLORIDE SOLUTION; TASK FORCE;

HEAT RESISTANCE; INSULATION; SODIUM CHLORIDE; THERMOCOUPLES;

COATINGS;

EID: 84859488400     PISSN: 87551985     EISSN: None     Source Type: Trade Journal    
DOI: None     Document Type: Article

References (21)

1. Goldie, B., Kapsanis K., "Corrosion Under Insulation: Basics and Resources or Understanding," JPCL July 2009. p. 34.
2. Bock, P.P., MeLampy, M.F., "Field Maintenance of Coating Systems," JPCL April 2009. p. 44.
3. NACE Standard SP0198-2010, "Control of Corrosion Under Thermal Insulation and Fireproofing Materials - A Systems Approach," (Houston, Texas; NACE 2010).
4. Hart, Gordon, H., "The Toolbox for Prevention of Corrosion Under Insulation," Insulation Outlook, March, 2008.
5. "Uhlig's Corrosion Handbook, 2nd Edition", Review, R.W. Editor, p.566.
6. Fitzgerald, B.J., Lazar, P. III, Kay, R.M., Winnik, D., "Strategies to Prevent Corrosion Under Insulation in Petrochemical Industry Piping," Corrosion 2003, Paper No. 03029.
7. Cunningham, T., Avery, R., "Thermal Spray Aluminum for Corrosion Protection - Some Practical Experience in the Offshore Industry," SSPC Orlando, Florida, 1998.
8. Goulette, B., "TSA Coatings for Risers and Offshore Piping," Presentation at Pipeline Coatings Seminar, NACE Fall Committee Week/2002, Dallas, TX, Sept. 8-13, 2002. The author reviews several researchers' findings on the durability of TSA in corrosive atmospheric environments.
9. Parks, A.R., "Aluminum Sprayed Coatings Onboard US Navy Ships - A Ten-Year Overview," www.inmetl.com/OnNavy 10.
10. Harrup, Eurocorr 2008, "Workshop on Corrosion Under Insulation Case Studies."
11. Mitschke, H., "Informal Technology Exchange" presentation of NACE Corrosion 2007.
12. Kane, R.D., Chauviere, M., "Evaluation of Steel and TSA Coating in a Corrosion Under Insulation (CUI) Environment," NACE Corrosion 2008, Paper No. 08036.
13. Schilling, M.S. - Personal Communication, November 2011.
14. Thomason, W.H., Olsen, S., Haugen, T., Fischer, K., "Deterioration of Thermal Sprayed Aluminum Coatings on Hot Risers Due to Thermal Cycling," Corrosion 2004.
15. Halliday, M., "Preventing Corrosion Under Insulation - New Generation Solutions for an Age Old Problem," Corrosion and Prevention 2006, Paper 014.
16. Knudsen, O., Rogne, T., Rossland, T., "Rapid Degradation of Painted TSA," NACE Paper No. 04023, 2004, p. 6.
17. O'Donoghue, M., Datta, V.J., and Aben, T., "From Trauma to Transcendence: Corrosion Under Insulation," NACE North Western Conference, February 15-18, 2010 Calgary, Alberta.
18. Brown, O., "High Heat Coatings: An Overview of Coating Performance and Product Characteristics," JPCL March 2008. p. 10.
19. Hare, C., "Paint Film Degradation - Mechanisms and Control," SSPC 01-14, Thermal Degradation of Binders, Chap. 45, p. 379, 2001.
20. Betzig, D., "Qualification Testing of High Temperature Coatings," 13th Middle East Conference and Exhibition, Paper No. 10136.
21. Gray, Linda G. S. and Bernard R. Appleman. "EIS: Electrochemical Impedance Spectroscopy. A Tool To Predict Remaining Coating Life?" JPCL February 2003. p. 66.