Fatigue crack growth in the D16CzATW aluminium alloy in the presence of a calibrated hole under simple bending

International Journal of Fatigue

Volumn 39, Issue , 2012, Pages 54-60

  Mierzyński, Janusz ^a   Hutsaylyuk, Volodymyr ^a  

^a MILITARY UNIVERSITY OF TECHNOLOGY   (Poland)

Author keywords

Aluminium alloy D16CzATW; Calibrated hole; Fatigue life; Fatigue micro mechanism; Short fatigue cracks

Indexed keywords

APPLIED LOADS; CALIBRATED HOLE; CLAD LAYER; COMPARATIVE TESTS; CYLINDRICAL HOLES; FAILURE MECHANISM; FAILURE PROCESS; MATERIAL BEHAVIOR; MICROMECHANISMS; SHORT FATIGUE CRACKS; STATE OF STRESS; STRESS RATIO;

FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS;

RESEARCH;

EID: 84857051684     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2011.04.003     Document Type: Article

References (18)

1. K.J. Miller Short crack problem Fatigue Eng Mater Struct 5 1982 223 232
2. G.N. Fridlyander, G.G. Kanter, and V.M. Beleckiy Perspective use deformation aluminium alloys at constructions plains Avia prom 9 1967 6 10 [In Russian]
3. G.N. Fridlyander Deformation aluminium construction alloys.: Metalurgiya 1979 208 [In Russian]
4. G.N. Fridlyander, and F.I. Kvasov Aluminium alloy type duralumins.: Metalurgiya 1984 240 [In Russian]
5. R.K. Bird, D.L. Dicus, and G.N. Fridlyander Al-Zi alloy 1441 fus fuselage applications Material Science Forum 331-337 2000 907 912
6. V. Kornev, E. Karpov, and A. Demeshkin Damage accumulation in the pre-fracture zone under low-cyclic loading of specimens with the edge crack Procedia Eng 2 1 2010 465 474
7. O.I. Radchenko, A.J. Cabezas Morales, and S.V. Zvyagin The diagram of bifurcation points for process of the fatigue of aluminium D16-alloy Metall Noveishie Tekhnol 20 5 1998 72 79 (Pubitemid 128557465)
8. G.V. Klevtsov, L.R. Botvina, and N.A. Klevtsova Plastic zones formation under different types of loading conditions ISIJ Int 36 2 1996 215 221 (Pubitemid 126519995)
9. A.A. Lebedev, N.G. Chausov, I.O. Boginich, and S.A. Nedoseka Complex evaluation of damage to material in plastic deformation process Probl Prochn 5 1996 23 30
10. G.V. Klevtsov, L.R. Botvina, N.A. Gorbatenko, and R.G. Klevtsov The influence of cycle asymmetry and loading scheme on fractographical and structural features of alloy type D16 fatigue fractures Izvestia Akademii nauk SSSR. Metally 2 1995 145 152
11. J. Schijve, M. Skorupa, A. Skorupa, T. Machniewicz, and P. Gruszczyński Fatigue crack growth in the aluminium alloy D16 under constant and variable amplitude loading Int J Fatigue 26 2004 1 15
12. Broek D, Schijve J. The effect of sheet thickness on the fatigue crack propagation in 2024-T3 Alclad sheet material. Tech. Report M.2129. Amsterdam: Nat Aerospace Lab NLR; 1963.
13. Jacobs FA, Schijve J, Tromp J. The significance of cladding for fatigue of aluminium alloys in aircraft structures. Tech. Report M76065. Amsterdam: Nat Aerospace Lab NLR; 1976.
14. Misawa H, Schijve J. Fatigue crack growth in aluminium alloy sheet material under constant-amplitude and simplified flight-simulation loading. Report LR-381, Delft University of Technology; 1983.
15. Kocańda D, Kocańda S, Torzewski J. Variable amplitude Load interaction in fatigue crack growth for 2024T3 aluminium alloy. Gdoutos EE, editor. In: Proc 16th European Conf. of Fracture ECF-16, Greece; 2006, p. 177-178 (abstract).
16. Kocańda D, Torzewski J. Capability of load-time history reconstruction and fatigue growth rate estimation for 2024T3 aluminium alloy on the basis of fractographic analysis. In: Proc Intern Conf of Mechanical Fatigue of Metals, Ternopil; Ukraine 2006. p. 42-48.
17. MROZIŃSKI S, LIPSKI A.: An experimental analysis of the calibration of rivet holes, In: XXIV Symposium on the Basics of Machine Design; 2009, p. 359-364 [in Polish].
18. MROZIŃSKI S, LIPSKI A.: Numerical simulation of the process of the calibration of a rivet hole, In: XXIV Symposium on the Basics of Machine Design; 2009, p. 310-315 [in Polish].