Preparation of Cu-doped γ-Fe2O3 nanowires with high coercivity by chemical vapor deposition

Journal of Materials Research

Volumn 26, Issue 13, 2011, Pages 1634-1638

  Zhou, Shao Min ^a   Lou, Shi Yun ^a   Wang, Yong Qiang ^a   Chen, Xi Liang ^a   Liu, Li Sheng ^a   Yuan, Hong Lei ^a  

^a HENAN UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

ANISOTROPY CONSTANTS; CHEMICAL VAPOR; COERCIVE FIELD; COERCIVE VALUES; FERROMAGNETIC PROPERTIES; HIGH COERCIVITY; MAGHEMITES; MAGNETIZATION DATA; ROOM TEMPERATURE; SINGLE-CRYSTALLINE; TECHNOLOGICAL ADVANCES;

CHEMICAL VAPOR DEPOSITION; COERCIVE FORCE; DOPING (ADDITIVES); FERRITE; FERRITES; IRON ORES; IRON OXIDES;

NANOWIRES;

EID: 80053949127     PISSN: 08842914     EISSN: 20445326     Source Type: Journal    
DOI: 10.1557/jmr.2011.129     Document Type: Article

References (28)

1. 3 thin-films. J. Appl. Phys. 77, 5828 (1995).
2. 3 nanocrystals with a large coercive field. J. Mater. Chem. 15, 1067 (2005).
3. J. Jin, S. Ohkoshi, and K. Hashimoto: Giant coercive field of nanometer-sized iron oxide. Adv. Mater. 16, 48 (2004).
4. N. Lu, X. Song, and J. Zhang: Crystal structure and magnetic properties of ultrafine nanocrystalline SmCo3 compound. Nanotechnology 21, 115708 (2010).
5. H. Kronmuller: Recent developments in high-tech magnetic materials. J. Magn. Magn. Mater. 140-144, 25 (1995).
6. P. Dutta, A. Manivannan, M. Seehra, N. Shah, and G. Huffman: Magnetic properties of nearly defect-free maghemite nanocrystals. Phys. Rev. B 70, 174428 (2004).
7. 3 nanoparticles obtained by a mechanochemically activated solidstate displacement reaction. Scr. Mater. 56, 883 (2007).
8. 3 nanoparticles smaller than 5 nm prepared by laser pyrolysis. J. Mater. Res. 14, 3066 (1999).
9. L. Li, J. Ding, and J. Xue: A facile green approach for synthesizing monodisperse magnetite nanoparticles. J. Mater. Res. 25, 810 (2010).
10. 4) under multicyclic indentation. J. Mater. Res. 24, 749 (2009).
11. 3. J. Solid State Chem. 139, 93 (1998).
12. 3 and low-temperature collapse of the magnetocrystalline anisotropy. Phys. Rev. B 79, 094404 (2009).
13. 3. Adv. Funct. Mater. 17, 1172 (2007).
14. 3 phases (γ→ε→β→α-Phase). J. Am. Chem. Soc. 131, 18299 (2009).
15. 3 structure. J. Am. Chem. Soc. 125, 11470 (2003).
16. 3 nanoparticles: Synthesis and magnetic properties. Nanotechnology 16, 506 (2005).
17. 3. J. Magn. Magn. Mater. 54-57, 1697 (1986).
18. 3 (maghemite). J. Phys. Cond. Mater. 13, 10785 (2001).
19. 3. J. Appl. Phys. 75, 5888 (1994).
20. 3 particles. Mater. Chem. Phys. 51, 169 (1997).
21. 4 films. J. Appl. Phys. 103, 07F701 (2008).
22. 0.3 magnets. J. Appl. Phys. 102, 093905 (2007).
23. W. Li, T. Ohkubo, T. Akiya, H. Kato, and K. Hono: The role of Cu addition in the coercivity enhancement of sintered Nd-Fe-B permanent magnets. J. Mater. Res. 24, 413 (2009).
24. A. Hussein, P. Murugaraj, C. Rix, and D. Mainwaring: The influence of Sb doping in achieving high magnetic coercivities in CoPt nanoparticles for micromagnet applications. J. Mater. Res. 24, 499 (2009).
25. 4. J. Mater. Res. 24, 1741 (2009).
26. 4 nanoparticles for camptothecin loading and release. J. Mater. Res. 24, 2307 (2009).
27. 3 powders. J. Mater. Res. 24, 245 (2009).
28. 3 nanochains by chemical vapor deposition. J. Phys. Cond. Mater. 20, 075217 (2008).