Effect of crack pattern on the residual strength of ceramics after quenching

Journal of the American Ceramic Society

Volumn 94, Issue 9, 2011, Pages 2804-2807

  Shao, Yingfeng ^a   Zhang, Yue ^b   Xu, Xianghong ^a   Zhou, Zhiliang ^a   Li, Wei ^a   Liu, Boyang ^c  

^a INSTITUTE OF MECHANICS   (China)

^b HARBIN INSTITUTE OF TECHNOLOGY   (China)

^c SHANGHAI MARITIME UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

CERAMIC SHEETS; CRACK PATTERNS; CRITICAL THERMAL SHOCK TEMPERATURE; JOINT ACTIONS; LONG CRACKS; PHYSICAL MECHANISM; RESIDUAL STRENGTH; TEMPERATURE RANGE; THEORETICAL APPROACH; WATER-QUENCHING;

CRACKS; QUENCHING; THERMAL SHOCK;

CERAMIC MATERIALS;

EID: 80053025573     PISSN: 00027820     EISSN: 15512916     Source Type: Journal    
DOI: 10.1111/j.1551-2916.2011.04728.x     Document Type: Article

References (12)

1. A. A. Buchheit, G. E. Hilmas, W. G. Fahrenholtz, and, D. M. Deason, " Thermal Shock Resistance of an AlN-BN-SiC Ceramic," J. Am. Ceram. Soc., 92 [ 6 ] 1358-61 (2009).
2. W. E. Pompe, " Thermal Shock Behavior of Ceramic Materials-Modelling and Measurement "; pp. 3-14 in Thermal Shock and Thermal Fatigue Behavior of Advanced Ceramics. Edited by, G. A. Schneider, and, G. Petzow,. Kluwer Academic Publishers, Netherlands, 1993.
3. D. P. H. Hasselman, " Strength Behavior of Polycrystalline Alumina Subjected to Thermal Shock," J. Am. Ceram. Soc., 53 [ 9 ] 490-5 (1970).
4. R. W. Davidge, and, G. Tappin, " Thermal Shock and Fracture in Ceramics," Trans. Br. Ceram. Soc., 66 [ 8 ] 405-22 (1967).
5. D. P. H. Hasselman, " Elastic Energy at Fracture and Surface Energy as Design Criteria for Thermal Shock," J. Am. Ceram. Soc., 46 [ 11 ] 535-40 (1963).
6. D. P. H. Hasselman, " Unified Theory of Thermal Shock Fracture Initiation and Crack Propagation in Brittle Ceramics," J. Am. Ceram. Soc., 52 [ 11 ] 600-4 (1969).
7. H. A. Bahr, H. J. Weiss, H. G. Maschke, and, F. Meissner, " Multiple Crack Propagation in a Strip Caused by Thermal Shock," Theor. Appl. Fract. Mech., 21 [ 1 ] 2716-20 (1986).
8. Y. F. Shao, X. H. Xu, S. H. Meng, G. H. Bai, C. P. Jiang, and, F. Song, " Crack Patterns in Ceramic Plates After Quenching," J. Am. Ceram. Soc., 93 [ 10 ] 3006-8 (2010).
9. H. A. Bahr, G. Fischer, and, H. J. Weiss, " Thermal-Shock Crack Patterns Explained by Single and Multiple Crack Propagation," J. Mater. Sci., 21 [ 1 ] 2716-20 (1986). (Pubitemid 16606518)
10. D. R. Jenkins, " Optimal Spacing and Penetration of Cracks in a Shrinking Slab," Phys. Rev. E, 71 [ 5 ] 056117, 8pp (2005).
11. M. L. Dunn, W. Suwito, and, S. Cunningham, " Fracture Initiation at Sharp Notches: Correlation Using Critical Stress Intensities," Int. J. Solids Struct., 34 [ 29 ] 3873-83 (1997).
12. Z. H. Jin, and, Y. Z. Feng, " Effects of Multiple Cracking on the Residual Strength Behavior of Thermally Shocked Functionally Graded Ceramics," Int. J. Solids Struct., 45 [ 24 ] 5973-86 (2008).