Effect of chromate primer on corrosion fatigue in aluminum alloy 7075

Procedia Engineering

Volumn 10, Issue , 2011, Pages 1220-1225

  Dorman, Sarah E Galyon ^a   Lee, Yongwon ^a  

^a UNITED STATES AIR FORCE ACADEMY   (United States)

Author keywords

Aluminum alloy 7075; Chromate primer; Corrosion fatigue; Corrosion fatigue inhibition

Indexed keywords

ALUMINUM; ALUMINUM ALLOYS; CHROMATE COATINGS; CHROMATES; COATINGS; CORROSION; CORROSION INHIBITORS; CRACKS; DAMAGE TOLERANCE; FATIGUE CRACK PROPAGATION; FATIGUE DAMAGE; FATIGUE OF MATERIALS; FIGHTER AIRCRAFT; LEACHING;

ALUMINUM ALLOY 7075; CORROSION PITS; DAMAGE TOLERANT; FATIGUE CRACKS; PIT-TO-CRACK TRANSITIONS; STANDARDIZED TESTS; TEST SPECIMENS; UNITED STATES AIR FORCE;

CORROSION FATIGUE;

EID: 80052947110     PISSN: 18777058     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1016/j.proeng.2011.04.203     Document Type: Conference Paper

References (8)

1. Warner, JS. The inhibition of environmental fatigue crack propagation in age-hardenable aluminium alloys. PhD Dissertation, University of Virginia, Charlottesville, VA; 2010.
2. Ciccone, MP. The effect of corrosion product formation on fatigue crack closure of AA7075-T6511 and AA7055-T7451. MS Thesis, University of Virginia, Charlottesville, VA; 2005.
3. Burns, JB. The effect of initiation feature and environment on fatigue crack formation and early propagation in Al-Zn-Mg-Cu. PhD Dissertation, University of Virginia, Charlottesville, VA; 2010.
4. www.AFGROW.net version 5.01.05.16 (2010).
5. Gasem Z, Gangloff, RP. Rate-limiting processes in environmental fatigue crack propagation in 7000-series aluminum alloys, In: Jones, RH editors. Chemisty and Electrochemistry of Corrosion and Stress Corrosion Cracking, Warrendale, PA: TMS-AIME; 2001, pp. 501-521
6. Fedrizzi, L, Deflorian, G, Boni, PL, Pasini, E. EIS study of environmentally friendly coil coating performances. Prog. Organic Coat. 1996; 29: 89-96.
7. Petry, L, Dante, JF, "Analysis of isocyanate-free topcoats by electrochemical impedance spectroscopy", Evaluation Report No. 99-71, AFRL/MLSA, September 1999.
8. Jakab, MA, Presuel-Moren, F, Scully, JR. Critical concentrations associated with cobalt, cerium, and molybdenum inhibition of AA 2024-T3 corrosion: delivery from Al-Co-Ce(-Mo) alloys", Corrosion, 2005; 61: 246-263.