Magnetocaloric effect and size-effect related thermal hysteresis reduction in MnAs 1-xP x compounds

Physica Status Solidi (A) Applications and Materials Science

Volumn 208, Issue 8, 2011, Pages 1950-1952

  Sun, Naikun ^a   Xu, Songning ^a   Li, Da ^b   Zhang, Zhidong ^b  

^a SHENYANG LIGONG UNIVERSITY   (China)

^b INTERNATIONAL CENTRE FOR MATERIALS PHYSICS   (China)

Author keywords

magnetocaloric effect; mechanical alloying; thermal hysteresis

Indexed keywords

FIELD CHANGE; GRAIN-SIZE EFFECTS; MAGNETIC REFRIGERANTS; MAGNETIC-ENTROPY; MAXIMUM VALUES; PREPARATION METHOD; PREPARATION TECHNOLOGY; ROOM TEMPERATURE; SIZE EFFECTS; THERMAL HYSTERESIS;

HYSTERESIS; MANGANESE COMPOUNDS; MECHANICAL ALLOYING; METALLURGY;

MAGNETOCALORIC EFFECTS;

EID: 80051679233     PISSN: 18626300     EISSN: 18626319     Source Type: Journal    
DOI: 10.1002/pssa.201026735     Document Type: Article

References (22)

1. E. Warburg, Ann. Phys. Chem. (Leipzig) 13, 141 (1881).
2. C. B. Zimm, A. Jastrab, A. Sternberg, V. K. Pecharsky, K. A. Gschneidner, Jr, M. Osborne, and, I. Anderson, Adv. Cryog. Eng. 43, 1759 (1998).
3. J. Glanz, Science 279, (2045). (1998.
4. V. K. Pecharsky, and, K. A. Gschneidner, Jr., Phys. Rev. Lett. 78, 4494 (1997).
5. O. Tegus, E. Brück, K. H. J. Buschow, and, F. R. de Boer, Nature 415, 150 (2002).
6. F. X. Hu, B. G. Shen, J. R. Sun, Z. H. Cheng, G. H. Rao, and, X. X. Zhang, Appl. Phys. Lett. 78, 3675 (2001).
7. A. Fujita, S. Fujieda, Y. Hasegawa, and, K. Fukamichi, Phys. Rev. B 67, 104416 (2003).
8. H. Wada, and, Y. Tanabe, Appl. Phys. Lett. 79, 3302 (2001).
9. D. L. Rocco, A. de Campos, A. M. G. Carvalho, L. Caron, A. A. Coelho, S. Gama, F. C. G. Gandra, A. O. dos Santos, L. M. da Silva, L. P. Cardoso, P. J. von Ranke, and, N. A. de Oliveira, Appl. Phys. Lett. 90, 242507 (2007).
10. S. Gama, A. A. Coelho, A. de Campos, A. M. G. Carvalho, F. C. G. Gandra, P. J. von Ranke, and, N. A. de Oliveira, Phys. Rev. Lett. 93, 237202 (2004).
11. W. B. Cui, W. Liu, X. H. Liu, S. Guo, Z. Han, X. G. Zhao, and, Z. D. Zhang, Mater. Lett. 63, 595 (2009).
12. E. M. Levin, V. K. Pecharsky, and, K. A. Gschneidner, Jr., Phys. Rev. B 62, R14625 (2000).
13. N. T. Trung, Z. Q. Ou, T.j. Gortenmulder, O. Tegus, K. H. J. Buschow, and, E. Brück, Appl. Phys. Lett. 94, 102513 (2009).
14. W. B. Cui, W. Liu, X. H. Liu, S. Guo, Z. Han, X. G. Zhao, and, Z. D. Zhang, J. Alloys Compd. 479, 189 (2009).
15. N. K. Sun, W. B. Cui, D. Li, D. Y. Geng, F. Yang, and, Z. D. Zhang, Appl. Phys. Lett. 92, 072504 (2008).
16. A. Roger, and, R. Fruchart, Mater. Res. Bull. 3, 253 (1968).
17. H. FjellvÃg, and, A. F. Andresen, J. Magn. Magn. Mater. 46, 29 (1984).
18. G. A. Govor, J. Magn. Magn. Mater. 54-57, 1361 (1984).
19. V. Provenzano, A. J. Shapiro, and, R. D. Shull, Nature 429, 853 (2004).
20. G. J. liu, J. R. Sun, J. Shen, B. Gao, H. W. Zhang, F. X. Hu, and, B. G. Shen, Appl. Phys. Lett. 90, 032507 (2007).
21. N. A. de Oliveira, and, P. J. von Ranke, Phys. Rev. B 77, 214439 (2008).
22. J. S. Amaral, and, V. S. Amaral, Appl. Phys. Lett. 94, 042506 (2009).