Volumn 20, Issue 7, 2011, Pages 963-978

Influence of resin type on the delamination behavior of carbon fiber reinforced composites under mode-II loading

Author keywords

composite; delamination; fracture; mode II

Indexed keywords

CARBON FIBER REINFORCED COMPOSITE; CARBON REINFORCEMENTS; COMPOSITE; CRITICAL ENERGY RELEASE RATE; DATA ASSESSMENT; END NOTCHED FLEXURES; FATIGUE BEHAVIOR; FATIGUE CRACK INITIATION; FATIGUE CURVES; FATIGUE DELAMINATION; MANUFACTURING PROCESS; MODE II; MODIFIED RESIN; NUMBER OF CYCLES; SHEAR TOUGHNESS;

EID: 80051577938     PISSN: 10567895     EISSN: 15307921     Source Type: Journal    
DOI: 10.1177/1056789510369332     Document Type: Article
Times cited : (25)

References (22)
  • 2
    • 29244433056 scopus 로고    scopus 로고
    • Experimental investigation on the influence of crack front to fiber orientation on fatigue delamination growth rate under mode II
    • DOI 10.1016/j.compscitech.2005.04.033, PII S0266353805001430, Experimental Techniques and Design in Composite Materials
    • Beghini, M., Bertini, L. and Forte, P. (2006). Experimental Investigation on the Influence of Crack Front to Fiber Orientation on Fatigue Delamination Growth Rate Under Mode II, Composites Science and Technology, 66: 240-247. (Pubitemid 41824114)
    • (2006) Composites Science and Technology , vol.66 , Issue.2 , pp. 240-247
    • Beghini, M.1    Bertini, L.2    Forte, P.3
  • 3
    • 33747192264 scopus 로고    scopus 로고
    • Mode II fracture testing of composites: A new look at an old problem
    • DOI 10.1016/j.engfracmech.2006.05.022, PII S0013794406002086
    • Blackman, B.R.K., Brunner, A.J. and Williams, J.G. (2006). Mode II Fracture Testing of Composites: A New Look at an Old Problem, Engineering Fracture Mechanics, 73: 2443-2455. (Pubitemid 44227780)
    • (2006) Engineering Fracture Mechanics , vol.73 , Issue.16 , pp. 2443-2455
    • Blackman, B.R.K.1    Brunner, A.J.2    Williams, J.G.3
  • 4
    • 67650079037 scopus 로고    scopus 로고
    • Fractography and Failure Mechanisms in Static Mode i and II Delamination Testing of Unidirectional Carbon Reinforced Composites
    • Bonhomme, J., Argüelles, A., Viña, J. and Viña, I. (2009). Fractography and Failure Mechanisms in Static Mode I and II Delamination Testing of Unidirectional Carbon Reinforced Composites, Polymer Testing, 28: 612-617.
    • (2009) Polymer Testing , vol.28 , pp. 612-617
    • Bonhomme, J.1    Argüelles, A.2    Viña, J.3    Viña, I.4
  • 6
    • 23844481428 scopus 로고    scopus 로고
    • Assessment of Initiation Criteria Used in Interlaminar Fracture Tests of Composites
    • de Morais, A.B. and de Moura, M.F. (2005). Assessment of Initiation Criteria Used in Interlaminar Fracture Tests of Composites, Engineering Fracture Mechanics, 72: 2615-2627.
    • (2005) Engineering Fracture Mechanics , vol.72 , pp. 2615-2627
    • De Morais, A.B.1    De Moura, M.F.2
  • 7
    • 67650067925 scopus 로고    scopus 로고
    • Fractographic Observations on Delamination Growth and the Subsequent Migration Through the Laminate
    • Greenhalgh, E.S., Rogers, C. and Robinson, P. (2009). Fractographic Observations on Delamination Growth and the Subsequent Migration Through the Laminate, Composites Science and Technology, 14: 2345-2351.
    • (2009) Composites Science and Technology , vol.14 , pp. 2345-2351
    • Greenhalgh, E.S.1    Rogers, C.2    Robinson, P.3
  • 8
    • 0032049414 scopus 로고    scopus 로고
    • Dependence of Intralaminar Fracture Toughness on Direction of Crack Propagation in Unidirectional Composites
    • Hansen, U. and Gillespie, J.W. (1998). Dependence of Intralaminar Fracture Toughness on Direction of Crack Propagation in Unidirectional Composites, Journal of Composites Technology & Research, 20: 89-99. (Pubitemid 128498826)
    • (1998) Journal of Composites Technology and Research , vol.20 , Issue.2 , pp. 89-99
    • Hansen, U.1    Gillespie Jr., J.W.2
  • 9
    • 33745964340 scopus 로고    scopus 로고
    • Modes I and II interlaminar fracture toughness and fatigue delamination of CF/epoxy laminates with self-same epoxy interleaf
    • DOI 10.1016/j.ijfatigue.2006.02.004, PII S0142112306000351
    • Hojo, M., Ando, T., Tanaka, M., Adachi, T., Ochiai, S. and Endo, Y. (2006). Modes I and II Interlaminar Fracture Toughness and Fatigue Delamination of CF/Epoxy Laminates with Self-same Epoxy Interleaf, International Journal of Fatigue, 28: 1154-1165. (Pubitemid 44061956)
    • (2006) International Journal of Fatigue , vol.28 , Issue.SPEC. ISS. 10 , pp. 1154-1165
    • Hojo, M.1    Ando, T.2    Tanaka, M.3    Adachi, T.4    Ochiai, S.5    Endo, Y.6
  • 10
    • 0023591707 scopus 로고
    • Effect of Stress Ratio on Near-threshold Propagation of Delamination Fatigue Cracks in Unidirectional CFRP
    • Hojo, M., Matsuda, S., Tanaka, M., Göran Gustafson, C. and Hayashi, R. (1987). Effect of Stress Ratio on Near-threshold Propagation of Delamination Fatigue Cracks in Unidirectional CFRP, Composites Science and Technology, 29: 273-292.
    • (1987) Composites Science and Technology , vol.29 , pp. 273-292
    • Hojo, M.1    Matsuda, S.2    Tanaka, M.3    Göran Gustafson, C.4    Hayashi, R.5
  • 11
    • 0021409392 scopus 로고
    • Detailed structure of delamination fracture surfaces in graphite/epoxy laminates
    • Johannesson, T., Sjöblom, P. and Selden, R. (1984). The Detailed Structure of Delamination Fracture Surfaces in Graphite/Epoxy Laminates, Journal of Materials Science, 19: 1171-1177. (Pubitemid 14562922)
    • (1984) Journal of Materials Science , vol.19 , Issue.4 , pp. 1171-1177
    • Johannesson, T.1    Sjoblom, P.2    Selden, R.3
  • 12
    • 25844465748 scopus 로고    scopus 로고
    • Effects of loading rate on fracture behavior and mechanism of thermoset epoxy resin
    • DOI 10.1016/j.polymertesting.2005.06.006, PII S014294180500098X
    • Kanchanomai, C., Rattananon, S. and Soni, M. (2005). Effects of Loading Rate on Fracture Behavior and Mechanism of Thermoset Epoxy Resin, Polymer Testing, 24: 886-892. (Pubitemid 41386488)
    • (2005) Polymer Testing , vol.24 , Issue.7 , pp. 886-892
    • Kanchanomai, C.1    Rattananon, S.2    Soni, M.3
  • 13
    • 33847715025 scopus 로고    scopus 로고
    • Characterization of the interlaminar fracture toughness of a laminated carbon/epoxy composite
    • DOI 10.1016/j.compscitech.2006.07.035, PII S0266353806002697
    • Mathews, M.J. and Swanson, S.R. (2007). Characterization of the Interlaminar Fracture Toughness of a Laminated Carbon/Epoxy Composite, Composites Science and Technology, 67: 1489-1498. (Pubitemid 46381371)
    • (2007) Composites Science and Technology , vol.67 , Issue.7-8 , pp. 1489-1498
    • Mathews, M.J.1    Swanson, S.R.2
  • 14
    • 33745945051 scopus 로고    scopus 로고
    • Mode II fatigue crack growth from delamination in unidirectional tape and satin-woven fabric laminates of high strength GFRP
    • DOI 10.1016/j.ijfatigue.2006.02.006, PII S0142112306000387
    • Matsubara, G., Ono, H. and Tanaka, K. (2006). Mode II Fatigue Crack Growth from Delamination in Unidirectional Tape and Satin-woven Fabric Laminates of High Strength GFRP, International Journal of Fatigue, 28: 1177-1186. (Pubitemid 44061958)
    • (2006) International Journal of Fatigue , vol.28 , Issue.SPEC. ISS. 10 , pp. 1177-1186
    • Matsubara, G.1    Ono, H.2    Tanaka, K.3
  • 16
    • 84958508474 scopus 로고
    • Characterization of Delamination Onset and Growth in A Composite Laminate
    • Reifsnider, K.L. (ed.), Philadelphia, ASTM STP 775
    • O'Brien, T.K. (1982). Characterization of Delamination Onset and Growth in a Composite Laminate. In: Reifsnider, K.L. (ed.), Damage in Composite Materials, Philadelphia, ASTM STP 775, pp. 140-167.
    • (1982) Damage in Composite Materials , pp. 140-167
    • O'Brien, T.K.1
  • 17
    • 0036182346 scopus 로고    scopus 로고
    • Evolution of U.S. military aircraft structures technology
    • Paul, K., Kelly, L., Venkayya, V. and Hess, T. (2002). Evolution of U.S. Military Aircraft Structures Technology, Journal of Aircraft, 39: 18-29. (Pubitemid 34172789)
    • (2002) Journal of Aircraft , vol.39 , Issue.1 , pp. 18-29
    • Paul, D.1    Kelly, L.2    Venkayya, V.3    Hess, T.4
  • 18
    • 1842579165 scopus 로고    scopus 로고
    • Mode-II Fatigue Fracture of Wood-Composite Bonded Interfaces
    • Qiao, P. and Hu, G. (2004). Mode-II Fatigue Fracture of Wood-Composite Bonded Interfaces, Journal of Composite Materials, 38: 453-473.
    • (2004) Journal of Composite Materials , vol.38 , pp. 453-473
    • Qiao, P.1    Hu, G.2
  • 20
    • 84933330679 scopus 로고
    • Mechanical Behavior and Fracture Characteristics of Off-axis Fiber Composites
    • Washington DC
    • Sinclair, J.H. and Chamis, C.C. (1977). Mechanical Behavior and Fracture Characteristics of Off-axis Fiber Composites, NASA Technical Paper 1081, Washington DC.
    • (1977) NASA Technical Paper , vol.1081
    • Sinclair, J.H.1    Chamis, C.C.2
  • 21
    • 33845643197 scopus 로고    scopus 로고
    • Over-leg bending test for mixed-mode I/II interlaminar fracture in composite laminates
    • DOI 10.1177/1056789507060774
    • Szekrényes, A. and Uj, J. (2007). Over-leg Bending Test for Mixed-mode I/II Interlaminar Fracture in Composite Laminates, International Journal of Damage Mechanics, 16: 5-33. (Pubitemid 44942600)
    • (2007) International Journal of Damage Mechanics , vol.16 , Issue.1 , pp. 5-33
    • Szekrenyes, A.1    Uj, J.2
  • 22
    • 50249164378 scopus 로고    scopus 로고
    • Mode II Fracture Mechanics Properties of Wood Measured by the Asymmetric Four-point Bending Test Using a Single-edge-notched Specimen
    • Yoshihara, H. (2008). Mode II Fracture Mechanics Properties of Wood Measured by the Asymmetric Four-point Bending Test Using a Single-edge-notched Specimen, Engineering Fracture Mechanics, 75: 4727-4739.
    • (2008) Engineering Fracture Mechanics , vol.75 , pp. 4727-4739
    • Yoshihara, H.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.