Size Scaling of Tensile Failure Stress in a Float Soda-Lime-Silicate Glass

International Journal of Applied Glass Science

Volumn 1, Issue 2, 2010, Pages 143-150

  Wereszczak, Andrew A ^a   Kirkland, Timothy P ^a   Ragan, Meredith E ^a   Strong, Kevin T ^a   Lin, Hua Tay ^a   Patel, Parimal ^b  

^a OAK RIDGE NATIONAL LABORATORY   (United States)

^b U S ARMY RESEARCH LABORATORY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

BIAXIAL FLEXURE; EFFECTIVE AREA; FAILURE STRESS; RING CRACKS; SIZE SCALING; SODA LIME SILICATE GLASS; TENSILE FAILURES; WEIBULL MODULUS;

BEAMS AND GIRDERS; LIME; SILICATES; TENSILE STRENGTH; TENSILE TESTING; TIN; WEIBULL DISTRIBUTION;

GLASS;

EID: 79961225048     PISSN: 20411286     EISSN: 20411294     Source Type: Journal    
DOI: 10.1111/j.2041-1294.2010.00014.x     Document Type: Article

References (27)

1. W. A. Weibull, "A Statistical Theory of the Strength of Materials, " Ingeniors Vetenskaps Akademien Handlingar, 151, 5-45 (1939).
2. N. A. Weil and I. M. Daniel, "Analysis of Fracture Probabilities in Nonuniformly Stressed Brittle Materials, " J. Am. Ceram. Soc., 47, 268-274 (1964).
3. ASTM C 1683. Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics, Vol. 15.01. ASTM International, West Conshohocken, PA, 2008.
4. C. J. Phillips, "The Strength and Weakness of Brittle Materials, " Am. Sci., 53, 20-51 (1965).
5. M. H. Krohn, J. R. Hellmann, D. L. Shelleman, D. J. Green, G. E. Sakoske, and J. A. Salem, "Test Methodology for Strength Testing of Soda-Lime-Silica Float Glass Before and After Enameling, " J. Test. Eval., 30 [6] 1-8 (2002).
6. S. I. Sil'vestrovich, V. G. Furman, and V. F. Troshin, "Strength of a Large-Scale Glass Sheet Under a Uniformly Distributed Load, " Glass Ceram., 34 [9] 547-550 (1977).
7. ASTM C 1326. Standard Test Method for Knoop Indentation Hardness of Advanced Ceramics, Vol. 15.01. ASTM International, West Conshohocken, PA, 2008.
8. W. L. Daloz, A. A. Wereszczak, and O. M. Jadaan, "Apparent Yield Strength of Hot-Pressed SiCs, " Ceram. Eng. Sci. Proc., 29 [6] 107-118 (2008).
9. A. A. Wereszczak, T. P. Kirkland, K. T. Strong Jr., and T. J. Holmquist, "ORNL Quasi-Static Mechanical Characterization and Analysis: FY09 Annual Report to TARDEC, " ORNL/TM-2009/234, December 2009.
10. ASTM C 1499. Standard Test Method for Monotonic Equibiaxial Flexure Strength of Advanced Ceramics at Ambient Temperatures, Vol. 15.01. ASTM, West Conshohocken, PA, 2008.
11. K. T. Strong Jr., A. A. Wereszczak, W. L. Daloz, and O. M. Jadaan, "Indenter Elastic Modulus and Hertzian Ring Crack Initiation, " Ceram. Eng. Sci. Proc., 30 [5] 83-90 (2009).
12. K. L. Johnson, Contact Mechanics. Cambridge University Press, Cambridge, U.K., 1985.
13. K. L. Johnson, J. J. O'Connor, and A. C. Woodward, "The Effect of the Indenter Elasticity on the Hertzian Fracture of Brittle Materials, " Proc. R. Soc. Lond., 334, 95-117 (1973).
14. P. D. Warren and D. A. Hills, "The Influence of Elastic Mismatch Between Indenter and Substrate on Hertzian Fracture, " J. Mater. Sci., 29, 2860-2866 (1994).
15. A. A. Wereszczak, W. L. Daloz, and O. M. Jadaan, "Effect of Indenter Elastic Modulus on Hertzian Ring Crack Initiation in Silicon Carbide, " Int. J. Appl. Ceram. Technol., (2010), in press.
16. ASTM C 1239. Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics, Vol. 15.01. ASTM International, West Conshohocken, PA, 2008.
17. R. L. Barnett, P. C. Hermann, J. R. Wingfield, and C. L. Conners "Fracture of Brittle Materials Under Transient Mechanical and Thermal Loading, " Technical Report AFFDL-TR-66-220, March 1967.
18. A. M. Freudenthal, "Statistical Approach to Brittle Fracture, " Fracture, An Advanced Treatise, Vol. 2, Mathematical Fundamentals. Academic Press, New York, 591-612, 1968.
19. O. M. Jadaan, A. A. Wereszczak, and K. E. Johanns, "Weibull Effective Area for Hertzian Ring Crack Initiation Stress, " Int. J. Appl. Ceram. Technol., (2010), in press.
20. S. T. Gulati, R. Akcakaya, and J. R. Varner, "Fracture Behavior of Tin Vs. Air Side of Float Glass, " Fractography of Glasses and Ceramics, Vol. IV, eds., J. R. Varner and G. D. Quinn American Ceramic Society, Westerville, OH, 317-325, 2001.
21. M. K. Krohn, J. R. Hellmann, D. L. Shelleman, C. G. Pantano, and C. E. Sakoske, "Biaxial Flexure Strength and Dynamic Fatigue of Soda-Lime-Silica Float Glass, " J. Am. Ceram. Soc., 85, 1777-1782 (2002).
22. R. Akcakaya, S. Gulati, and J. R. Varner "Fatigue Behavior of Surface Flaws on Air Vs. Tin Side of Soda-Lime-Silica Float Glass: Paper T4.3 in Glass in the New Millennium: Challenges and Break-Through Technologies, "Proceedings of the ICG Annual Meeting 2000 (Amsterdam, The Netherlands, May 15-17, 2000), National Committee Netherlands Glass Industry (NCNG), 2000.
23. R. R. Tummala and B. J. Foster, "Strength and Dynamic Fatigue of Float Glass Surfaces, " J. Am. Ceram. Soc., 58, 156-157 (1975).
24. MIL-O-13830A, "Optical Components for Fire Control Instruments; General Specification Governing the Manufacture, Assembly, and Inspection Of, " September 1963.
25. A. A. Wereszczak, T. P. Kirkland, K. T. Strong Jr., O. M. Jadaan, and G. A. Thompson, "Size-Scaling of Tensile Failure Stress in Boron Carbide, " Adv. Appl. Ceram., (2010), in press.
26. A. A. Wereszczak, T. P. Kirkland, K. T. Strong Jr., J. Campbell, J. C. LaSalvia, and H. T. Miller, "Size-Scaling of Tensile Failure Stress in Hot-Pressed SiC, " Int. J. Appl. Ceram. Technol., (2010), in press.
27. A. Brücker-Foit, E. Diegele, P. Hülsmeier, U. Rettig, and C. Hohmann, "Prediction of the Failure Probability of High Strength Ceramics Subject to Thermal Shock Loading, " Ceram. Eng. Sci. Proc., 23, 141-148 (2002).