The influence of surface crack on the wear behavior of polyamide 66 under dry sliding condition

Wear

Volumn 271, Issue 9-10, 2011, Pages 2234-2241

  Abdelbary, A ^a   Abouelwafa, M N ^a   Fahham, I M E ^a   Hamdy, A H ^a  

^a Alexandria University The Faculty Of Engineering   (Egypt)

Author keywords

Cyclic load; Polyamide; Surface crack; Wear

Indexed keywords

CRACK ORIENTATIONS; CYCLIC LOADING CONDITIONS; CYCLIC LOADINGS; DRY CONDITION; DRY SLIDING; FATIGUE WEAR; LOADING CONDITION; PERPENDICULAR CRACK; POLYAMIDE 66; RUBBING SURFACES; RUNNING-IN; SLIDING SPEED; STATIC LOADS; SURFACE CRACK; SURFACE CRACKS; SURFACE FATIGUE WEARS; TEST RIGS; TESTING MACHINE; WEAR BEHAVIORS; WEAR RATES; WEAR TEST;

CRACKS; CYCLIC LOADS; LOAD TESTING; LOADING; STEEL TESTING; SURFACE DEFECTS; WEAR OF MATERIALS;

SURFACE TESTING;

EID: 79960688103     PISSN: 00431648     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.wear.2010.11.042     Document Type: Article

References (19)

1. Hutchings I.M. Tribology: friction and wear of engineering materials 1992, Asterix Press.
2. Clark D.T., Feast W.J. Polymer surfaces 1978, John Wiley & Sons, New York.
3. N.P. Suh, Update on the delamination theory of wear, Fundamentals of friction and wear of materials, ASM Materials Science Seminar, Rigeny, D.A., ed., 1980, pp. 43-71.
4. Chen Y.K., Kukureka S.N., Hooke C.J., Rao M. Surface topography and wear mechanisms in polyamide 66 and its composites. J. of Material Science 2000, 35:1269-1281.
5. K. Furber, J.R. Atkenson and D. Dowson, The mechanisms for nylon 66: Paper II, Proc. of the 3rd Leeds-Lyon Symposium on Tribology, 1976.
6. Atkinson J.R., Brown K.J., Dowson D. The wear of high molecular weight polyethlene. Part I: the wear of isotropic polyethylene against dry stainless steel in unidirectional motion. J. Lub. Tech. 1978, 100:208-218.
7. Anderson J.C., Robins E.J. The influence of temperature generation on the wear of some polymers. Proc. of the 3rd Leeds-Lyon Symposium on Tribology 1976.
8. Yap A.U.J., Teoh S.H., Chew C.L. Effect of cyclic loading on occlusal contact area wear of composite restoratives. Dental Materials 2002, 18:149-158.
9. A. Abdelbary, M.N. Abouelwafa, I. El Fahham and A. I. Gomaa, The influence of cyclic loading parameters on the wear of nylon 66, Proc. 8th International Conference on Production Engineering and Control PEDAC (2004) Egypt.
10. Abdelbary A., Abouelwafa M.N., El Fahham I., Gomaa A.I. A New reciprocating tribometer for wear testing under different fluctuating loading conditions. Alexandria Engineering J. 2004, 43:615-619.
11. Barbour P.S.M., Barton D.C., Fisher J. The influence of contact stress on the wear of UHMWPE for total replacement hip prostheses. Wear 1995, 181-183:250-257.
12. Goto K., Kagawa Y., Nojima K., Iba H. Effect of crack fibre interactions on crack growth rate in fibre-reinforced brittle matrix composite under cyclic loading. Material Sc. and Eng. 1996, A212:69-74.
13. Cooper J.R., Dowson D., Fisher J. Macroscopic and Microscopic Wear Mechanisms in UHMWPE. Wear 1993, Vol. 162-164:378-384.
14. Fam H., Keer L.M., Chang W., Cheng H.S. Competition between fatigue crack propagation and wear. J. of Tribology 1993, 115:141-145.
15. Lamethe J.F., Sergot P., Chateauminois A., Briscoe B.J. Contact fatigue behaviour of glassy polymers with improved toughness under fretting wear conditions. Wear 2003, 255:758-765.
16. Rhee S.K., Ludema K.C. Mechanisms of formation of polymeric transfer films. Wear 1978, 46:231-240.
17. Zalisz Z., Vroegop P.H., Bosma R. A running-in model for the reciprocating sliding of nylon 6.6 against stainless steel. Wear 1988, 121:71-93.
18. K. Tanaka and Y. Yamada, Effect of sliding speed on transfer and wear of semicrystaline polymers sliding against smooth steel surface, Proc. the 4th International conference on wear of materials, 1983.
19. Franklin S.E., de Kraker A. Investigation of counterface surface topography effect on the wear and transfer behaviour of a POM-20%PTFE composite. Wear 2003, 225:766-773.